Solar cell sealing material, method for manufacturing solar cell sealing material, and solar cell module

Patent metadata

Field	Value
Publication number	US-9595630-B2
Application number	US-201214239143-A
Country	US
Kind code	B2
Filing date	Aug 16, 2012
Priority date	Aug 18, 2011
Publication date	Mar 14, 2017
Grant date	Mar 14, 2017

Abstract

An encapsulating material for solar cell containing an ethylene/α-olefin copolymer satisfying the following a1) and a2), and a specific peroxyketal having a 1-hour half-life temperature in a range of 100 to 135 degrees centigrade; the peroxyketal being contained in an amount of 0.1 to less than 0.8 weight parts relative to 100 weight parts of the ethylene/α-olefin copolymer.
a1) the shore A hardness is from 60 to 85 as measured in accordance with ASTM D2240. a2) MFR is from 2 to 50 g/10 minutes as measured under the conditions of a temperature of 190 degrees centigrade and a load of 2.16 kg in accordance with ASTM D1238.

First claim

The invention claimed is:

1. An encapsulating material for solar cell containing an ethylene/α-olefin copolymer satisfying the following a1) and a2)-1, and a peroxyketal represented by the following general formula (1) and having a 1-hour half-life temperature in a range of 100 to 135 degrees centigrade; the peroxyketal being contained in an amount of 0.1 to less than 0.8 weight parts relative to 100 weight parts of the ethylene/α-olefin copolymer,
wherein the α-olefin in the ethylene/α-olefin copolymer includes at least one or more kinds selected from propylene, 1-butene, 1-pentene, 1-hexene, 3-methyl-1-butene, 3,3-dimethyl-1-butene, 4-methyl-1-pentene, and 1-octene, and
wherein the encapsulating material comprises organic peroxide consisting of the peroxyketal of Chemical Formal 1, with
a1) the shore A hardness is from 60 to 85 as measured in accordance with ASTM D2240;
a2)-1 MFR is from 10 to 50 g/10 minutes as measured under the conditions of a temperature of 190 degrees centigrade and a load of 2.16 kg in accordance with ASTM D1238

wherein in the above general formula (1), R 1 s are each independently a straight-chain or branched alkyl group having 3 to 8 carbon atoms, and R 2 and R 3 are each independently a straight-chain or branched alkyl group having 1 to 8 carbon atoms, or R 2 and R 3 may be bonded together to form an aliphatic ring having 5 to 9 carbon atoms or an alkyl-substituted aliphatic ring.

2. The encapsulating material for solar cell according to claim 1 , wherein the ethylene/α-olefin copolymer satisfies the following a3) and a4):
a3) the content ratio of structural units derived from ethylene is from 80 to 90 mol % and the content ratio of structural units derived from α-olefin having 3 to 20 carbon atoms is from 10 to 20 mol %;
a4) the density is from 0.865 to 0.884 g/cm 3 as measured in accordance with ASTM D1505.

3. The encapsulating material for solar cell according to claim 1 , wherein the ethylene/α-olefin copolymer is an ethylene/α-olefin/non-conjugated polyene copolymer and satisfies the following a5):
a5) the content ratio of structural units derived from ethylene is from 80 to 90 mol %, the content ratio of structural units derived from α-olefin having 3 to 20 carbon atoms is from 9.99 to 19.99 mol %, and the content ratio of structural units derived from non-conjugated polyene is from 0.01 to 5.0 mol %.

4. The solar cell sealing material according to claim 1 , wherein the peroxyketal is at least one or more kinds selected from the following general formulae (2) to (4):

In the above general formula (2), R 4 s each independently represent a straight-chain or branched alkyl group having 3 to 8 carbon atoms;

wherein in the above general formula (3), R 5 s each independently represent a straight-chain or branched alkyl group having 3 to 8 carbon atoms;

wherein in the above general formula (4), R 6 s each independently represent a straight-chain or branched alkyl group having 3 to 8 carbon atoms.

5. The encapsulating material for solar cell according to claim 1 , wherein the encapsulating material for solar cell comprises a silane coupling agent in an amount of 0.1 to 5 weight parts, based on 100 weight parts of the ethylene/α-olefin copolymer.

6. The encapsulating material for solar cell according to claim 5 , wherein the encapsulating material for solar cell further comprises at least one kind selected from the group consisting of an ultraviolet absorber, a heat-resistant stabilizer and a hindered amine type light stabilizer in an amount of 0.005 to 5 weight parts, based on 100 weight parts of the ethylene/α-olefin copolymer.

7. The encapsulating material for solar cell according to claim 6 , wherein the encapsulating material for solar cell further comprises a crosslinking aid in an amount of 0.05 to 5 weight parts, based on 100 weight parts of the ethylene/α-olefin copolymer.

8. The encapsulating material for solar cell according to claim 1 , wherein the material is in a sheet form.

9. A method for manufacturing the encapsulating material for solar cell as described in claim 8 , in which the resin composition containing the ethylene/α-olefin copolymer and the peroxyketal represented by the above general formula (1) is molded into a film form by melt-extrusion molding.

10. An encapsulating material for solar cell containing an ethylene/α-olefin copolymer satisfying the following a1) and a2)-2, and a peroxyketal represented by the following general formula (1) and having a 1-hour half-life temperature in a range of 100 to 135 degrees centigrade; the peroxyketal being contained in an amount of 0.1 to less than 0.8 weight parts relative to 100 weight parts of the ethylene/α-olefin copolymer,
wherein the α-olefin in the ethylene/α-olefin copolymer includes at least one or more kinds selected from propylene, 1-butene, 1-pentene, 1-hexene, 3-methyl-1-butene, 3, 3-dimethyl-1-butene, 4-methyl-1-pentene, and 1-octene, and
wherein the encapsulating material comprises organic peroxide consisting of the peroxyketal of Chemical Formula 1, with
a1) the shore A hardness is from 60 to 85 as measured in accordance with ASTM D2240;
a2)-2 MFR is equal to or more than 2 g/10 minutes and less than 10 g/10 minutes as measured under the conditions of a temperature of 190 degrees centigrade and a load of 2.16 kg in accordance with ASTM D1238

wherein in the above general formula (1), R 1 s are each independently a straight-chain or branched alkyl group having 3 to 8 carbon atoms, and R 2 and R 3 are each independently a straight-chain or branched alkyl group having 1 to 8 carbon atoms, or R 2 and R 3 may be bonded together to form an aliphatic ring having 5 to 9 carbon atoms or an alkyl-substituted aliphatic ring.

11. The encapsulating material for solar cell according to claim 10 , wherein the ethylene/α-olefin copolymer satisfies the following a3), a4) and a5):
a3) the content ratio of structural units derived from ethylene is from 80 to 90 mol % and the content ratio of structural units derived from α-olefin having 3 to 20 carbon atoms is from 10 to 20 mol %;
a4) the density is from 0.865 to 0.884 g/cm 3 as measured in accordance with ASTM D1505;
a5) the content ratio of structural units derived from ethylene is from 80 to 90 mol %, the content ratio of structural units derived from α-olefin having 3 to 20 carbon atoms is from 9.99 to 19.99 mol %, and the content ratio of structural units derived from non-conjugated polyene is from 0.01 to 5.0 mol %.

12. The solar cell sealing material according to claim 10 , wherein the peroxyketal is at least one or more kinds selected from the following general formulae (2) to (4):

wherein in the above general formula (2), R 4 s each independently represent a straight-chain or branched alkyl group having 3 to 8 carbon atoms;

In the above general formula (3), R 5 s each independently represent a straight-chain or branched alkyl group having 3 to 8 carbon

Assignees

• Ikenaga Shigenobu
• Takeuchi Fumito
• Watanabe Keiji
• Ito Tomoaki
• Mitsui Chemicals Tohcello Inc

Inventors

• Ikenaga Shigenobu
• Takeuchi Fumito
• Watanabe Keiji
• Ito Tomoaki

Classifications

• H10F19/804 Primary

  Materials of encapsulations · CPC title

• C08L2203/16

  used for films · CPC title

• C09D123/0815

  Copolymers of ethene with aliphatic 1-olefins · CPC title

• C08K5/14 Primary

  Peroxides · CPC title

• C08L2312/00

  Crosslinking · CPC title