Calcium hexaluminate-containing mold and facecoat compositions and methods for casting titanium and titanium aluminide alloys

Patent metadata

Field	Value
Publication number	US-9592548-B2
Application number	US-201313752880-A
Country	US
Kind code	B2
Filing date	Jan 29, 2013
Priority date	Jan 29, 2013
Publication date	Mar 14, 2017
Grant date	Mar 14, 2017

Abstract

The disclosure relates generally to mold compositions and methods of molding and the articles so molded. More specifically, the disclosure relates to mold compositions, intrinsic facecoat compositions, and methods for casting titanium-containing articles, and the titanium-containing articles so molded, where the mold comprises calcium hexaluminate.

First claim

The invention claimed is:

1. A mold for casting a titanium-containing article, comprising:
a bulk comprising calcium hexaluminate and a calcium aluminate cement, said calcium aluminate cement comprising calcium monoaluminate, calcium dialuminate, and mayenite;
a cavity for casting the titanium-containing article therein; and
an intrinsic facecoat of thickness about 10 microns to about 500 microns disposed between the bulk and the cavity, wherein said intrinsic facecoat comprises calcium hexaluminate and a calcium aluminate cement, said calcium aluminate cement comprising calcium monoaluminate, calcium dialuminate, and mavenite.

2. The mold as recited in claim 1 , wherein said calcium hexaluminate comprises particles that are less than about 50 microns in outside dimension.

3. The mold as recited in claim 1 , wherein said calcium hexaluminate comprises from about 15 percent by weight to about 50 percent by weight of the mold.

4. The mold as recited in claim 1 , wherein the intrinsic facecoat is a continuous intrinsic facecoat or a non-continuous intrinsic facecoat.

5. The mold as recited in claim 1 , wherein the bulk and the intrinsic facecoat have different compositions, and wherein the intrinsic facecoat comprises calcium aluminate cement with a particle size of less than about 50 microns.

6. The mold as recited in claim 1 , wherein the bulk and the intrinsic facecoat have different compositions, and wherein the bulk comprises alumina particles larger than about 50 microns.

7. The mold as recited in claim 1 , wherein the bulk comprises alumina particles larger than about 50 microns and the intrinsic facecoat comprises calcium aluminate cement particles less than about 50 microns in size.

8. The mold as recited in claim 1 , wherein the intrinsic facecoat has, by weight fraction, at least 20 percent more calcium monoaluminate than does the bulk.

9. The mold as recited in claim 1 , wherein the intrinsic facecoat has, by weight fraction, at least 20 percent less alumina than does the bulk.

10. The mold as recited in claim 1 , wherein the intrinsic facecoat has, by weight fraction, at least 20 percent more calcium monoaluminate, at least 20 percent less alumina, and at least 50 percent less mayenite than does the bulk of the mold.

11. The mold as recited in claim 1 , wherein said calcium monoaluminate in the bulk comprises a weight fraction of about 0.05 to 0.95, and said calcium monoaluminate in the intrinsic facecoat comprises a weight fraction of about 0.30 to 0.95.

12. The mold as recited in claim 1 , wherein said calcium dialuminate in the bulk comprises a weight fraction of about 0.05 to about 0.80, and said calcium dialuminate in the intrinsic facecoat comprises a weight fraction of about 0.05 to 0.30.

13. The mold as recited in claim 1 , wherein said mayenite in the bulk comprises a weight fraction of about 0.01 to about 0.30, and said mayenite in the intrinsic facecoat comprises a weight fraction of about 0.01 to 0.05.

14. The mold as recited in claim 1 , wherein said calcium monoaluminate in the bulk comprises a weight fraction of about 0.05 to about 0.95, and said calcium monoaluminate in the intrinsic facecoat comprises a weight fraction of about 0.3 to about 0.95;
wherein said calcium dialuminate in the bulk comprises a weight fraction of about 0.05 to about 0.80, and said calcium dialuminate in the intrinsic facecoat comprises a weight fraction of about 0.05 to about 0.30; and
wherein said mayenite in the bulk comprises a weight fraction of about 0.01 to about 0.30, and said mayenite in the intrinsic facecoat comprises a weight fraction of about 0.01 to about 0.05.

15. The mold as recited in claim 1 further comprising:
aluminum oxide particles in the bulk that are less than about 500 microns in outside dimension.

16. The mold as recited in claim 1 , wherein the calcium aluminate cement comprises more than 30 percent by weight of the composition used to make the mold.

17. The mold as recited in claim 1 , further comprising:
magnesium oxide particles, calcium oxide particles, zirconium oxide particles, titanium oxide particles, or compositions thereof.

18. The mold as recited in claim 1 , further comprising:
hollow particles of aluminum oxide in the bulk.

19. The mold as recited in claim 17 , further comprising:
more than about 10 percent by weight and less than about 50 percent by weight of calcium oxide particles.

20. The mold as recited in claim 1 , further comprising silica.

21. The mold as recited in claim 1 , further comprising silicates in an amount of less than about 5 weight percent.

Assignees

• Gen Electric

Inventors

• Bewlay Bernard Patrick
• Weimer Michael James
• Bancheri Stephen Francis
• Mckiever Joan
• Ellis Brian Michael

Classifications

• Y10T428/26

  Web or sheet containing structurally defined element or component, the element or component having a specified physical dimension · CPC title

• Y10T428/256

  Heavy metal or aluminum or compound thereof · CPC title

• Y10T428/1317

  Multilayer [continuous layer] · CPC title

• Y10T428/131

  Glass, ceramic, or sintered, fused, fired, or calcined metal oxide or metal carbide containing [e.g., porcelain, brick, cement, etc.] · CPC title

• B22D21/005

  with high melting point, e.g. Be 1280 degrees C, Ti 1725 degrees C · CPC title