Method for manufacturing a photovoltaic module with annealing for forming a photovoltaic layer and electrically conducting region

Patent metadata

Field	Value
Publication number	US-9583660-B2
Application number	US-201314371224-A
Country	US
Kind code	B2
Filing date	Jan 9, 2013
Priority date	Jan 11, 2012
Publication date	Feb 28, 2017
Grant date	Feb 28, 2017

Abstract

The invention relates to a method for manufacturing a photovoltaic module comprising plurality of solar cells in a thin-layer structure, in which the following are formed consecutively in the structure: an electrode on the rear surface ( 41 ), a photovoltaic layer ( 43 ) obtained by depositing components including metal precursors and at least one element taken from Se and S and by annealing such as to convert said components into a semiconductor material, and another semiconductor layer ( 44 ) in order to create a pn junction with the photovoltaic layer ( 43 ); characterized in that the metal precursors form, on the electrode on the rear surface ( 41 ), a continuous layer, while said at least one element forms a layer having at least one break making it possible, at the end of the annealing step, to leave an area ( 430 ) of the layer of metal precursors in the metal state at said break.

First claim

The invention claimed is:

1. A process for producing a photovoltaic module comprising a plurality of solar cells in a thin film structure, in which the following are successively produced in the structure: a rear-face electrode ( 41 ), a photovoltaic film ( 43 ) obtained by deposition of constituents comprising metal precursors and at least one element taken from Se and S and, by annealing, to convert these constituents into a semiconducting material, and another semiconducting film ( 44 ), in order to create a pn junction with the photovoltaic film ( 43 ), characterized in that the metal precursors form, on the rear-face electrode ( 41 ), a continuous film ( 420 ), whereas said at least one element forms a film ( 421 ) exhibiting at least one discontinuity ( 422 ), making it possible, on conclusion of the annealing, to leave a region ( 430 ) of the film ( 420 ) of metal precursors in the metal state at said discontinuity, said process further comprising:
depositing said at least one element of S and Se to form the film ( 421 ) on the layer of metal precursors ( 420 ), the film ( 421 ) of the at least one element of S and Se is deposited so as to form the at least one discontinuity forming an opening ( 422 ) so that the film of precursors ( 420 ) is devoid of said at least one element of S and Se in a left free region ( 423 ) facing the opening ( 422 ),
under the annealing, the metal precursors contained in the film of precursors ( 420 ) react with said at least one element of S and Se contained in the film ( 421 ) to form said photovoltaic film ( 43 ) and the metallic precursors of said film of precursors ( 420 ) at said left free region ( 423 ) remain in metallic form by being not in contact with the at least one element of S and Se and thereby form an electrically conducting region ( 430 ) through the photovoltaic film ( 43 ).

2. The process as claimed in claim 1 , characterized in that the film ( 421 ) of said at least one element is deposited in localized fashion.

3. The process as claimed in claim 1 , characterized in that the metal precursors are of the Cu, Ga and In or Cu, Zn and Sn type.

4. The process as claimed in claim 1 , characterized in that the annealing is carried out at a temperature of between 400 and 600° C. and preferably of the order of 550° C.

5. The process as claimed in claim 1 , characterized in that the other semiconducting film ( 44 ) exhibits a discontinuity ( 440 ) at said region ( 430 ).

Assignees

• Commissariat Energie Atomique

Inventors

• Karst Nicolas
• Amtablian Sevak
• Perraud Simon

Classifications

• Y02E10/541

  CuInSe2 material PV cells · CPC title

• H01L31/0324

  Electricity · mapped topic

• H01L31/0463

  Electricity · mapped topic

• H01L31/0322

  Electricity · mapped topic

• H01L31/0516 Primary

  Electricity · mapped topic