Cold-rolled steel sheet with controlled microstructure, grain diameters, and texture

Patent metadata

Field	Value
Publication number	US-9580767-B2
Application number	US-201314379829-A
Country	US
Kind code	B2
Filing date	Feb 13, 2013
Priority date	Feb 22, 2012
Publication date	Feb 28, 2017
Grant date	Feb 28, 2017

Abstract

A high-strength cold-rolled steel sheet includes a composition having controlled amounts of carbon, silicon, manganese, phosphorous, sulfur, titanium, niobium, sol. Aluminum, chromium, molybdenum, vanadium, boron, calcium, REM, and iron. A microstructure thereof has a main phase of ferrite of at least 40 area %, and a second phase of a low-temperature transformation phase consisting either or both of martensite and bainite, which comprises at least 10 area % in total and retained austenite (γ) at least comprising 3 area % . An average grain diameter of ferrite has a tilt angle of at least 15° is at most 5.0 mm, an average grain diameter of the low-temperature transformation-produced phase is at most 2.0 mm, an average grain diameter of lump-like retained γ having an aspect ratio of less than 5 is at most 1.5 mm, and an area fraction of the lump-like retained γ relative to the retained γ is at least 50%.

First claim

The invention claimed is:

1. A cold-rolled steel sheet characterized by having:
a chemical composition comprising, in mass %, C: 0.06 to 0.3%, Si: 0.4 to 2.5%, Mn: 0.6 to 3.5%, P: at most 0.1%, S: at most 0.05%, Ti: 0 to 0.08%, Nb: 0 to 0.04%, a total content of Ti and Nb: 0 to 0.10%, sol.Al: 0 to 2.0%, Cr: 0 to 1%, Mo: 0 to 0.3%, V: 0 to 0.3%, B: 0 to 0.005%, Ca: 0 to 0.003%, REM: 0 to 0.003% and the remainder of Fe and impurities,
a microstructure having a main phase of ferrite comprising at least 40 area %, and a second phase of a low-temperature transformation phase consisting either or both of martensite and bainite which comprising at least 10 area % in total and retained austenite at least which comprising 3 area %, and satisfying Equations (1) to (4):
d F ≦5.0  (1);

d M+B ≦2.0  (2);

d As ≦1.5  (3); and

r As ≧50  (4),

where d F is an average grain diameter (μm) of ferrite defined by high angle grain boundaries having a tilt angle of at least 15°;
d M+B is an average grain diameter (μm) of the low-temperature transformation phase;
d As is an average grain diameter (μm) of retained austenite having an aspect ratio of less than 5; and
r AS is an area fraction (%) of retained austenite having an aspect ratio of less than 5 relative to all the retained austenite, wherein,
the cold-roiled steel sheet has a texture whose ratio of an average X-ray intensity of {100}<011> to {211}<011> orientations relative to an average X-ray intensity of a random structure having no texture is less than 6 at a death of ½ of a sheet thickness, and
the cold-rolled steel sheet has a tensile strength of at least 782 MPa.

2. The cold-rolled steel sheet as set forth in claim 1 , wherein the chemical composition contains one or two selected from, in mass %, Ti: 0.005 to 0.08% and Nb: 0.003 to 0.04%.

3. The cold-rolled steel sheet as set forth in claim 1 , wherein the chemical composition contains, in mass %, sol.Al: 0.1 to 2.0%.

4. The cold-rolled steel sheet as set forth in claim 1 , wherein the chemical composition contains one or more selected from, in mass %, Cr: 0.03 to 1%, Mo: 0.01 to 0.3% and V: 0.01 to 0.3%.

5. The cold-rolled steel sheet as set forth in claim 1 , wherein the chemical composition contains, in mass %, B: 0.0003 to 0.005%.

6. The cold-rolled steel sheet as set forth in claim 1 , wherein the chemical composition contains one or two selected from, in mass %, Ca: 0.0005 to 0.003% and REM: 0.0005 to 0.003%.

7. The cold-rolled steel sheet as set forth in claim 1 , comprising a plating layer on a sheet surface.

Assignees

• Nippon Steel & Sumitomo Metal Corp

Inventors

• Hata Kengo
• Tomida Toshiro
• Imai Norio
• Haga Jun
• Nishio Takuya

Classifications

• Y10T428/12972

  Containing 0.01-1.7% carbon [i.e., steel] · CPC title

• C21D8/0284

  Application of a separating or insulating coating · CPC title

• C22C38/00

  Ferrous alloys, e.g. steel alloys (cast-iron alloys C22C37/00) · CPC title

• C22C38/26

  with niobium or tantalum · CPC title

• C22C38/18

  containing chromium · CPC title