Process for the preparation of a catalyst based on tungsten for use in hydrotreatment or in hydrocracking

Patent metadata

Field	Value
Publication number	US-9579642-B2
Application number	US-201414265655-A
Country	US
Kind code	B2
Filing date	Apr 30, 2014
Priority date	Apr 30, 2013
Publication date	Feb 28, 2017
Grant date	Feb 28, 2017

Abstract

The invention concerns a process for the preparation of a catalyst based on tungsten intended for hydrotreatment or hydrocracking processes.
The invention concerns a process for the preparation of a catalyst for carrying out hydrogenation reactions in hydrotreatment and hydrocracking processes. Said catalyst is prepared from at least one mononuclear precursor compound based on tungsten (W), in its monomeric or dimeric form, having at least one W═O or W—OR bond or at least one W═S or W—SR bond where [R═C x H y where x≧1 and (x−1)≦y≦(2x+1) or R═Si(OR′) 3 or R═Si(R′) 3 where R′═C x′ H y′ where x′≧1 and (x′−1)≦y′≦(2x′+1)], optionally at least one Mo precursor and optionally at least one promoter element from group VIII. Said precursors are deposited onto an oxide support which is suitable for the process in which it is used, said catalyst advantageously being sulphurized before being deployed in said process.

First claim

The invention claimed is:

1. A process for the preparation of a catalyst comprising at least one support, optionally at least one metal from group VIII of the periodic classification of the elements and at least tungsten, said process comprising:
introducing tungsten onto at least one support, in an organic solvent A, in the form of at least one mononuclear precursor compound based on W, in its monomeric or dimeric form, having at least one W═O or W—OR bond or at least one W═S or W—SR bond,
where
R═C x H y ,
x≧1, and
(x−1)≦y≦(2x+1),
or
R═Si(OR′) 3 or R═Si(R′) 3 ,
R′═C x′ H y′ ,
x′≧1, and
(x′−1)≦y′≦(2x′+1),
and comprising at least one final step for gas phase sulphurization, in situ and/or ex situ.

2. The process as claimed in claim 1 , in which the metal from group VIII is cobalt, iron or nickel.

3. The process as claimed in claim 2 , in which the metal from group VIII is nickel.

4. The process as claimed in claim 1 , in which the tungsten precursor is a mononuclear precursor based on tungsten W, in its monomeric or dimeric form, with formula W(═O) n (═S) n′ (OR) a (SR′) b (L1) c (L 2 ) d (L3) e (L4) f (L5) g ,
where
R═C x H y ,
x≧1, and
(x−1)≦y≦(2x+1),
or
R═Si(OR″) 3 or R═Si(R″) 3 ,
R″═C x″ H y″ ,
x″≧1, and
(x″−1)≦y″≦(2x″+1),
R′═C x′ H y′ ,
x′≧1, and
(x′−1)≦y′≦(2x′+1),
or
R′═Si(OR′″) 3 or R′═Si(R′″) 3 ,
R′″═C x′″ H y′″ ,
x′″≧1, and
(x′″−1)≦y′″≦(2x′″+1),
0≦n+n′≦2,
0≦n≦2, and
0≦n′≦2,
if n=n′=0,
then
a≠0 or b≠0,
and
a+b+c+d+e+f+g=6 and 0≦a≦6, 0≦b≦6, 0≦c≦6, 0≦d≦6, 0≦e≦6, 0≦f≦6, 0≦g≦6;
or
a+b+c+d+e+f+g=5 and 0≦a≦5, 0≦b≦5, 0≦c≦5, 0≦d≦5, 0≦e≦5, 0≦f≦5, 0≦g≦5;
or
a+b+c+d+e+f+g=4 and 0≦a≦4, 0≦b≦4, 0≦c≦4, 0≦d≦4, 0≦e≦4, 0≦f≦4, 0≦g≦4;
if (n=1 and n′=0) or (n′=1 and n=0),
then
a+b+c+d+e+f+g=4 and 0≦a≦4, 0≦b≦4, 0≦c≦4, 0≦d≦4, 0≦e≦4, 0≦f≦4, 0≦g≦4;
or
a+b+c+d+e+f+g=3 and 0≦a≦3, 0≦b≦3, 0≦c≦3, 0≦d≦3, 0≦e≦3, 0≦f≦3, 0≦g≦3;
if n+n′=2 and 0≦n≦2 and 0≦n′≦2,
then
a+b+c+d+e+f+g=2 and 0≦a≦2, 0≦b≦2, 0≦c≦2, 0≦d≦2, 0≦e≦2, 0≦f≦2, 0≦g≦2;
and
(L1), (L2), (L3), (L4) and (L5) are selected from the group consisting of ligands of the type THF, dimethyl ether, dimethylsulphide, P(CH 3 ) 3 , allyl, aryl, halogen, amine, acetate, acetylacetonate, halide, hydroxide and —SH.

5. The process as claimed in claim 4 , in which the precursor is W(OEt) 5 , W(OEt) 6 , W(═O)(OEt) 4 , W(═S)(OEt) 4 , W(═S)(SEt) 4 , W(═O) 2 (OEt) 2 , W(OC 6 H 5 ) 6 , W(SEt) 5 , W(SEt) 6 , W(OEt) 3 (SEt) 2 , W(OEt) 4 (SEt), or W(═O)(OEt) 3 (acac) with Et=CH 2 CH 3 (ethyl group) and acac=(CH 3 COCHCOCH 3 ) − (acetylacetonate), in their monomeric or dimeric form.

6. The process as claimed in claim 1 , in which molybdenum is also introduced into the catalyst, in the form of a precursor in an aqueous, alcoholic or organic solvent.

7. The process as claimed in claim 6 , in which the molybdenum precursor is a mononuclear precursor, in its monomeric or dimeric form, comprising at least one Mo═O or Mo—OR bond or at least one Mo═S or Mo—SR bond where
R═C x H y ,
x≧1, and
(x−1)≦y≦(2x+1),
or
R═Si(OR′) 3 or R═Si(R′) 3 ,
R′═C x′ H y′ ,
x′≧1, and
(x′−1)≦y′≦(2x′+1).

8. The process as claimed in claim 7 , in which the molybdenum precursor is a compound with the following formula Mo(═O) n (═S) n′ (OR) a (SR′) b (L1) c (L2) d (L3) e (L4) f (L5) g ,
where
R═C x H y ,
x≧1, and
(x−1)≦y≦(2x+1),
or
R═Si(OR″) 3 or R═Si(R″) 3 ,
R″═C x″ H y′ ,
x″≧1, and
(x″−1)≦y″≦(2x″+1),
R′═C x′ H y′ ,
x′≧1, and
(x′−1)≦y′≦(2x′+1),
or
R′═Si(OR′″) 3 or R′═Si(R′″) 3 ,
R′″═C x′″ H y′″ ,
x′″≧1, and
(x′″−1)≦y′″≦(2x′″+1),
0≦n+n′≦2,
0≦n≦2, and
0≦n′≦2,
if n=n′=0,
then
a≠0 or b≠0
and
a+b+c+d+e+f+g=6 and 0≦a≦6, 0≦b≦6, 0≦c≦6, 0≦d≦6, 0≦e≦6, 0≦f≦6, 0≦g≦6;
or
a+b+c+d+e+f+g=5 and 0≦a≦5, 0≦b≦5, 0≦c≦5, 0≦d≦5, 0≦e≦5, 0≦f≦5, 0≦g≦5;
or a+b+c+d+e+f+g=4 and 0≦a≦4, 0≦b≦4, 0≦c≦4, 0≦d≦4, 0≦e≦4, 0≦f≦4, 0≦g≦4;
if (n=1 and n′=0) or (n′=1 and n=0),
then
a+b+c+d+e+f+g=4 and 0≦a≦4, 0≦b≦4, 0≦c≦4, 0≦d≦4, 0≦e≦4, 0≦f≦4, 0≦g≦4;
or
(a+b+c+d+e+f+g=3 and 0≦a≦3, 0≦b≦3, 0≦c≦3, 0≦d≦3, 0≦e≦3, 0≦f≦3, 0≦g≦3;
if n+n′=2 and 0≦n≦2 and 0≦n′≦2,
then
a+b+c+d+e+f+g=2 and 0≦a≦2, 0≦b≦2, 0≦c≦2, 0≦d≦2, 0≦e≦2, 0≦f≦2, 0≦g≦2;
and
(L1), (L2), (L3), (L4) and (L5) are selected from the group consisting of ligands of the type THF, dimethyl ether, dimethylsulphide, P(CH 3 ) 3 , allyl, aryl, halogen, amine, acetate, acetylacetonate, halide, hydroxide and —SH.

9. The process as claimed in claim 8 , in which the molybdenum precursor is Mo(OEt) 5 .

10. The process for the preparation of a catalyst as claimed in claim 1 , in which the tungsten, optionally the molybdenum, optionally the metal or metals from group VIII, are introduced simultaneously or in succession.

11. The process for the preparation of a catalyst as claimed in claim 1 , comprising at least one final step for gas phase sulphurization, in situ.

12. The process for the preparation of a catalyst as claimed in claim 1 , comprising at least the following steps:
a) impregnation by bringing a solution S comprising the organic solvent A with at least said mononuclear precursor based on tungsten, in its monomeric or dimeric form, having at least one W═O or W—OR bond or at least one W═S or W—SR bond,
where
R═C x H y ,
x≧1, and
(x−1)≦y≦(2x+1),
or
R═Si(OR′) 3 or R═Si(R′) 3 ,
R′═C x′ H y′ ,
x′≧1, and
(x′−1)≦y′≦(2x′+1),
into contact with a porous mineral support, which has been calcined under vacuum or in a stream of inert gas;
b) maturing in an anhydrous atmosphere;
c) drying the impregnated support in an anhydrous atmosphere or under vacuum or in a stream of inert gas; and
d) ex situ sulphurization in a H 2 S/H 2 or H 2 S/N 2 mixture containing at least 5% by volume of H 2 S in the mixture at a temperature equal to or higher than ambient temperature.

13. The process for the preparation of a catalyst as claimed in claim 12 , in which the optional molybdenum precursor is introduced into the impregnation step a) in the same solution S as the tungsten precursor.

14. The process for the preparation of a catalyst as claimed in claim 12 , in which the optional molybdenum precursor is introduced in a post-impregnation step a2) after drying at c).

15. The process for the preparation of a catalyst as claimed in claim 12 , in which the optional metal from group VIII is introduced into step a) in the same solution S as the tungsten precursor or after the drying c) in a post-impregnation step a2) with the aid of a solution containing an organic solvent B, or after the sulphurization step d) in a post-impregnation step a3) with the aid of an aqueous or organic solution.

16. The process for the preparation of a catalyst as claimed in claim 1 , comprising at least one final step for gas phase sulphurization, ex situ.

17. A catalyst which has been prepared as claimed in claim 1 .

18. The catalyst as claimed in claim 17 , comprising a cumulative quantity of (tungsten+molybdenum) in the range of 4% to 30% by weight and a metal or metals from group VIII content in the range of 0.1% to 8% by weight with respect to the total catalyst weight.

19. The process for the hydrogenation of a hydrocarbon feed, comprising subjecting said feed to hydrogenation conditions in the presence of a catalyst according to claim 17 .

20. The process as claimed in claim 19 , comprising hydrotreatment or hydrocracking.

Assignees

• Ifp Energies Now

Inventors

• Alphazan Thibault
• Bonduelle Audrey
• Legens Christele
• Raybaud Pascal
• Coperet Christophe

Classifications

• B01J31/0211

  with a metal-oxygen link · CPC title

• B01J31/2226

  Anionic ligands, i.e. the overall ligand carries at least one formal negative charge · CPC title

• B01J2531/847

  Nickel · CPC title

• C10G45/08

  in combination with chromium, molybdenum, or tungsten metals, or compounds thereof · CPC title

• C10G45/00

  Refining of hydrocarbon oils using hydrogen or hydrogen-generating compounds · CPC title