Surface-treated rare earth-based magnetic particles, resin composition for bonded magnets comprising the earth-based magnetic particles and bonded magnet comprising the earth-based magnetic particles

Patent metadata

Field	Value
Publication number	US-9566646-B2
Application number	US-201013147274-A
Country	US
Kind code	B2
Filing date	Feb 3, 2010
Priority date	Feb 3, 2009
Publication date	Feb 14, 2017
Grant date	Feb 14, 2017

Abstract

The present invention relates to surface-treated rare earth-based magnetic particles comprising rare-earth-based magnetic particles, a first coating layer comprising a phosphoric acid compound which is formed on a surface of the respective magnetic particles and a second coating layer in the form of a composite coating film comprising a silicon compound and a phosphoric acid compound which is formed on a surface of the first coating layer, wherein an amount of Fe eluted from the rare earth-based magnetic particles is not more than 10 mg/L; a resin composition for bonded magnets comprising the above surface-treated rare earth-based magnetic particles and a resin; and a bonded magnet comprising the above surface-treated rare earth-based magnetic particles.

First claim

The invention claimed is:

1. Surface-treated rare earth-based magnetic particles comprising
rare-earth-based magnetic particles,
a first coating layer comprising a phosphoric acid compound which is formed on a surface of the respective rare-earth-based magnetic particles, and
a second coating layer in the form of a composite coating film comprising a silicon compound and a phosphoric acid compound, which is formed on a surface of the first coating layer,
an amount of Fe eluted from the rare earth-based magnetic particles being not more than 5 mg/L.

2. Surface-treated rare earth-based magnetic particles according to claim 1 , wherein the composite coating film comprising the silicon compound and the phosphoric acid compound which forms the second coating layer comprises a compound produced from the phosphoric acid compound selected from the group consisting of orthophosphoric acid, disodium hydrogen phosphate, pyrophosphoric acid, metaphosphoric acid, manganese phosphate, zinc phosphate and aluminum phosphate, an alkoxy oligomer whose molecular end is capped with an alkoxysilyl group, and a silane coupling agent.

3. Surface-treated rare earth-based magnetic particles according to claim 1 , wherein a content of the phosphoric acid compounds in the surface-treated rare earth-based magnetic particles is 0.01 to 2.0% by weight.

4. Surface-treated rare earth-based magnetic particles according to claim 1 wherein a content of Si in the surface-treated rare earth-based magnetic particles is 0.01 to 2.0% by weight.

5. Surface-treated rare earth-based magnetic particles according to claim 1 , wherein a content of carbon in the surface-treated rare earth-based magnetic particles is 0.01 to 2.0% by weight.

6. Surface-treated rare earth-based magnetic particles according to claim 1 , wherein the rare earth-based magnetic particles are Nd—Fe—B-based magnetic particles.

7. Surface-treated rare earth-based magnetic particles according to claim 1 , wherein the rare earth-based magnetic particles are Sm—Fe—N-based magnetic particles.

8. A resin composition for bonded magnets comprising the surface-treated rare earth-based magnetic particles as defined in claim 1 , and a resin.

9. A bonded magnet comprising the surface-treated rare earth-based magnetic particles as defined in claim 1 .

10. Surface-treated rare earth-based magnetic particles according to claim 1 , wherein the amount of Fe eluted from the rare earth-based magnetic particles is not more than 2.5 mg/L.

11. Surface-treated rare earth-based magnetic particles according to claim 1 , wherein the phosphoric acid compound forming the first coating layer is selected from the group consisting of orthophosphoric acid, disodium hydrogen phosphate, pyrophosphoric acid, metaphosphoric acid, manganese phosphate, zinc phosphate and aluminum phosphate.

Assignees

• Shigeoka Kuniyoshi
• Katayama Nobuhiro
• Toda Kogyo Corp

Inventors

• Shigeoka Kuniyoshi
• Katayama Nobuhiro

Classifications

• B22F1/16

  Metallic particles coated with a non-metal (coated with lubricating or binding agents or with organic material B22F1/10) · CPC title

• C22C2202/02

  Magnetic · CPC title

• B22F1/02 Primary

  Operations & Transport · mapped topic

• B22F3/14 Primary

  simultaneously · CPC title

• C22C33/0278

  with at least one alloying element having a minimum content above 5% · CPC title