Silicon oxide particles, making method, lithium ion secondary battery, and electrochemical capacitor

Patent metadata

Field	Value
Publication number	US-9553309-B2
Application number	US-201615009238-A
Country	US
Kind code	B2
Filing date	Jan 28, 2016
Priority date	May 16, 2012
Publication date	Jan 24, 2017
Grant date	Jan 24, 2017

Abstract

Silicon oxide particles each comprising an inner portion having an iron content of 10-1,000 ppm and an outer portion having an iron content of up to 30 ppm are suitable as negative electrode active material in nonaqueous electrolyte secondary batteries. Using a negative electrode comprising the silicon oxide particles as active material, a lithium ion secondary battery or electrochemical capacitor having a high capacity and improved cycle performance can be constructed.

First claim

The invention claimed is:

1. A lithium ion secondary battery comprising a positive electrode, a negative electrode, and a lithium ion-conducting nonaqueous electrolyte, said negative electrode comprising a silicon oxide particles as negative electrode active material having an average particle size of 0.1 to 30 μm and a BET specific surface area of 0.5 to 30 m 2 /g, wherein a first iron content of inner portion of the silicon oxide particles is 15 to 1,000 ppm, and a second iron content of outer portion of the silicon oxide particles is 4 to 10 ppm, and
wherein the inner portion is different from the outer portion.

2. The lithium ion secondary battery of claim 1 , the second iron content of outer portion of the silicon oxide particles is determined by a method where a powder sample is mixed with 50% by weight of aqua regia and heated at 170° C. for dissolution, followed by cooling, static holding, and filtration, and obtained filtrate is analyzed by ICP-AES to determine the second iron content of outer portion of the silicon oxide particles, and
the first iron content of inner portion of the silicon oxide particles is determined by a method, where a total iron content of particles is measured by adding 50% by weight of hydrofluoric acid to a powder sample, once reaction begins, 50% by weight of nitric acid is further added to obtain a liquid, the liquid is heated at 200° C. until complete melting, the liquid is analyzed by ICP-AES to determine the total iron content of particles, and then the first iron content of inner portion of the silicon oxide particles is determined by subtracting the second iron amount of outer portion from the total amount ((the total iron content)−(the second iron content of outer portion of the silicon oxide particles)).

3. The lithium ion secondary battery of claim 1 , wherein the first iron content of inner portion of the silicon oxide particles is 20 to 800 ppm.

4. The lithium ion secondary battery of claim 1 , wherein the first iron content of inner portion of the silicon oxide particles is 15 to 850 ppm, and the second iron content of outer portion of the silicon oxide particles is 4 to 5 ppm.

Assignees

• Shinetsu Chemical Co

Inventors

• Fukuoka Hirofumi
• Ueno Susumu
• Watanabe Koichiro

Classifications

• H01G11/30

  characterised by their material · CPC title

• H01M4/483 Primary

  for non-aqueous cells (H01M4/485 takes precedence) · CPC title

• H01M4/366

  as layered products · CPC title

• H01M2004/021

  Physical characteristics, e.g. porosity, surface area · CPC title

• H01M4/1395

  of electrodes based on metals, Si or alloys · CPC title