High-strength electric-resistance-welded steel pipe of excellent long-term softening resistance in intermediate temperature ranges

Patent metadata

Field	Value
Publication number	US-9551047-B2
Application number	US-201314410912-A
Country	US
Kind code	B2
Filing date	Jun 17, 2013
Priority date	Jun 28, 2012
Publication date	Jan 24, 2017
Grant date	Jan 24, 2017

Abstract

A high strength electric resistance welded steel pipe has a yield strength of 450 MPa or more and excellent resistance to softening for a long period in an intermediate temperature range and a method of manufacturing the steel pipe are provided. The steel pipe has a chemical composition containing, by mass%, C: 0.026% or more and 0.084% or less, Si: 0.10% or more and 0.30% or less, Mn: 0.70% or more and 1.90% or less, Al: 0.01% or more and 0.10% or less, Nb: 0.001% or more and 0.070% or less, V: 0.001% or more and 0.065% or less, Ti: 0.001% or more and 0.033% or less, Ca: 0.0001% or more and 0.0035% or less, in which the condition that Pcm is 0.20 or less is satisfied.

First claim

The invention claimed is:

1. A high strength electric resistance welded pipe having a longitudinally extending seam of an electric resistance weld zone, a base metal of the pipe having a chemical composition containing, by mass %,
C: 0.025% or more and 0.084% or less, Si: 0.10% or more and 0.30% or less,
Mn: 0.70% or more and 1.90% or less, P: 0.018% or less,
S: 0.0029% or less, Al: 0.01% or more and 0.10% or less,
Nb: 0.001% or more and 0.070% or less, V: 0.001% or more and 0.065% or less,
Ti: 0.001% or more and 0.033% or less, Ca: 0.0001% or more and 0.0035% or less,
N: 0.0050% or less, O: 0.0030% or less
and the balance being Fe and inevitable impurities, in which a condition that Pcm defined by equation (1) below is 0.20 or less is satisfied, having a microstructure in the base metal portion including, in terms of volume percentage, 90% or more of a quasi-polygonal ferrite phase as a main phase and the balance being hard phases other than the quasi-polygonal ferrite phase in which the quasi-polygonal ferrite phase has an average grain diameter of 10 μm or less, having a microstructure in an electric resistance weld zone including, in terms of volume percentage, 90% or more of a quasi-polygonal ferrite phase as a main phase and the balance being hard phases other than the quasi-polygonal ferrite phase, in which the quasi-polygonal ferrite phase has an average grain diameter of 10 μm or less, and having a yield strength YS of 450 MPa or more:
Pcm=C+Si/30+Mn/20+Cu/20+Ni/60+Cr/20+Mo/15+V/10+5B  (1),

where C, Si, Mn, Cu, Ni, Cr, Mo, V and B represent the contents (mass %) of chemical elements respectively represented by the corresponding atomic symbols.

2. The high strength electric resistance welded pipe according to claim 1 , wherein total content of Si, Mn, Al, Ca and Cr contained in inclusions having an equivalent circle diameter of 5 μm or more present in the electric resistance weld zone is 49 mass ppm or less.

3. The pipe according to claim 1 , wherein the chemical composition further contains, by mass %, one or more selected from among Cu: 0.001% or more and 0.350% or less, Ni: 0.001% or more and 0.350% or less, Mo: 0.001% or more and 0.350% or less and Cr: 0.001% or more and 0.350% or less.

4. The high strength electric resistance welded pipe according to claim 3 , wherein total content of Si, Mn, Al, Ca and Cr contained in inclusions having an equivalent circle diameter of 5 μm or more present in the electric resistance weld zone is 49 mass ppm or less.

Assignees

• Jfe Steel Corp

Inventors

• Toyoda Shunsuke
• Goto Sota
• Okabe Takatoshi
• Inoue Tomohiro

Classifications

• C21D8/10 Primary

  during manufacturing of tubular bodies · CPC title

• C22C38/00

  Ferrous alloys, e.g. steel alloys (cast-iron alloys C22C37/00) · CPC title

• Y10T428/12979

  Containing more than 10% nonferrous elements [e.g., high alloy, stainless] · CPC title

• Y10T428/12972

  Containing 0.01-1.7% carbon [i.e., steel] · CPC title

• C22C38/38

  with more than 1.5% by weight of manganese · CPC title