Mixed manganese ferrite coated catalyst, method of preparing the same, and method of preparing 1,3-butadiene using the same

Patent metadata

Field	Value
Publication number	US-9550174-B2
Application number	US-201113810557-A
Country	US
Kind code	B2
Filing date	May 26, 2011
Priority date	Jul 20, 2010
Publication date	Jan 24, 2017
Grant date	Jan 24, 2017

Abstract

This invention relates to a method of preparing a mixed manganese ferrite coated catalyst, and a method of preparing 1,3-butadiene using the same, and more particularly, to a method of preparing a catalyst by coating a support with mixed manganese ferrite obtained by co-precipitation at 10˜40° C. using a binder and to a method of preparing 1,3-butadiene using oxidative dehydrogenation of a crude C4 mixture containing n-butene and n-butane in the presence of the prepared catalyst. This mixed manganese ferrite coated catalyst has a simple synthetic process, and facilitates control of the generation of heat upon oxidative dehydrogenation and is very highly active in the dehydrogenation of n-butene.

First claim

The invention claimed is:

1. A method of preparing a mixed manganese ferrite coated catalyst for use in preparing 1,3-butadiene, comprising:
a) co-precipitating a precursor aqueous solution comprising a manganese precursor and an iron precursor while being mixed in a basic solution, thus forming a co-precipitated solution;
b) washing and filtering the co-precipitated solution, thus obtaining a solid sample of mixed manganese ferrite which is then dried at 70˜200° C.;
c) mixing the dried solid sample of mixed manganese ferrite, a binder of alumina, distilled water and an acid at a weight ratio of 1:1˜1,5: 8˜10:0.4˜0.6 at room temperature, thus obtaining a mixture, wherein said alumina is boehmite and the acid is selected from the group consisting of nitric acid, sulfuric acid, hydrochloric acid and phosphoric acid; and
d) adding a support to the mixture obtained in c) and then performing blending and drying, wherein said drying is performed at 50˜80° C., and the support is silicon carbide.

2. The method of claim 1 , wherein amounts of the manganese precursor and the iron precursor are adjusted so that an atom ratio of iron/manganese is 2.0˜2.5.

3. The method of claim 1 , wherein the precursor aqueous solution is co-precipitated while being mixed in a 1.5˜4,0 M basic solution at 10˜40° C.

4. The method of claim 1 , further comprising heat treating the solid catalyst dried in d) at 350˜800° C.

5. The method of claim 1 , wherein the support is a spherical or cylindrical support having a size of 1˜10 mm.

6. The method of claim 1 , wherein the support is used in an amount 5˜15times the weight of the dried solid sample.

7. The method of claim 1 , wherein the alumina has a specific surface area of 70˜250m 2 /g.

Assignees

• Kwon Yong Tak
• Kim Tae Jin
• Chung Young Min
• Kim Ok Youn
• Oh Seung Hoon
• Sk Innovation Co Ltd

Inventors

• Kwon Yong Tak
• Kim Tae Jin
• Chung Young Min
• Kim Ok Youn
• Oh Seung Hoon

Classifications

• B01J37/0215

  Coating · CPC title

• C07C2521/08

  Silica · CPC title

• B01J37/088

  Decomposition of a metal salt · CPC title

• C07C2523/889

  Manganese, technetium or rhenium · CPC title

• B01J23/8892 Primary

  Manganese · CPC title