Electrocatalyst for fuel cells and method for producing said electrocatalyst

Patent metadata

Field	Value
Publication number	US-9548498-B2
Application number	US-201214359201-A
Country	US
Kind code	B2
Filing date	Dec 18, 2012
Priority date	Dec 22, 2011
Publication date	Jan 17, 2017
Grant date	Jan 17, 2017

Abstract

The invention relates to a carbon-free electrocatalyst for fuel cells, containing an electrically conductive substrate and a catalytically active species, wherein the conductive substrate is an inorganic, multi-component substrate material of the composition 0X1-0X2, in which 0X1 means an electrically non-conductive inorganic oxide having a specific surface area (BET) in the range of 50 to 400 mVg and 0X2 means a conductive oxide. The non-conductive inorganic oxide 0X1 is coated with the conductive oxide 0X2. The multi-component substrate preferably has a core/shell structure. The multi-component substrate material 0X1-0X2 has an electrical conductivity in the range>0.01 S/cm and is coated with catalytically active particles containing noble metal. The electrocatalysts produced therewith are used in electrochemical devices such as PEM fuel cells and exhibit high corrosion stability.

First claim

What is claimed is:

1. An electrocatalyst for fuel cells comprising
an electrically conductive support and a catalytically active species, wherein the conductive support is an inorganic multicomponent support material of composition OX1-OX2 wherein
OX1 is an oxide which is not electrically conductive and has a specific surface area (BET) in the range from 50 to 400 m 2 /g and
OX2 is a conductive oxide

and wherein the catalytically active species comprises a noble metal selected from the group consisting of ruthenium, osmium, rhodium, iridium, palladium, platinum, silver and gold, or mixtures or alloys thereof.

2. The electrocatalyst as claimed in claim 1 , wherein the multicomponent support material OX1-OX2 has an electrical conductivity in the range of >0.01 S/cm.

3. The electrocatalyst as claimed in claim 2 , wherein the multicomponent support material OX1-OX2 has an electrical conductivity in the range of >0.1 S/cm.

4. The electrocatalyst as claimed in claim 1 , wherein the conductive oxide OX2 is located at or on the surface of the inorganic oxide OX1.

5. The electrocatalyst as claimed in claim 1 , wherein the multicomponent support material OX1-OX2 has a core/shell structure.

6. The electrocatalyst as claimed in claim 1 , wherein the inorganic oxide OX1 is selected from the group consisting of titanium oxide (TiO 2 ), aluminum oxide (Al 2 O 3 ), silicon dioxide (SiO 2 ), zirconium dioxide (ZrO 2 ), yttrium oxide (Y 2 O 3 ), cerium oxide (Ce 2 O 3 ), cerium dioxide (CeO 2 ), lanthanum oxide (La 2 O 3 ), tin oxide (SnO 2 ) and mixtures and combinations thereof.

7. The electrocatalyst as claimed in claim 1 , wherein the conductive oxide OX2 is selected from the group consisting of ruthenium(IV) dioxide (RuO 2 ), iridium(IV) oxide (IrO 2 ), tungsten oxide (WO x ), molybdenum oxide (MoO x ), niobium oxide (NbO x ), tantalum oxide (TaO x ), tin oxide (SnO x ), reduced titanium oxide (TiO x ) and mixtures and combinations thereof.

8. The electrocatalyst as claimed in claim 7 , wherein the conductive oxide OX2 comprises dopants of the elements vanadium, niobium, tantalum or antimony, dopants of the halide ions F − or Cl − or mixtures or combinations thereof.

9. The electrocatalyst as claimed in claim 1 , wherein the conductive oxide OX2 is present in proportions of from 10 to 99 wt % (based on the total weight of the support material).

10. The electrocatalyst as claimed in claim 9 , wherein the conductive oxide OX2 is present in proportions of from 20 to 95 wt % (based on the total weight of the support material).

11. The electrocatalyst as claimed in claim 1 , wherein the catalytically active species comprises platinum or a platinum alloy of a base metal selected from the group consisting of vanadium, chromium, manganese, iron, cobalt, nickel, copper and zinc.

12. The electrocatalyst as claimed in claim 1 , wherein the catalytically active species is present on the support material OX1-OX2 in the form of fine particles having a mean particle diameter of between 1 and 100 nm.

13. The electrocatalyst as claimed in claim 1 , wherein the catalytically active species is present on the support material OX1-OX2 in proportions of from 5 to 60 wt % (based on the total weight of the catalyst).

14. The electrocatalyst as claimed in claim 13 , wherein the catalytically active species is present on the support material OX1-OX2 in proportions of from 5 to 40 wt % (based on the total weight of the catalyst).

15. The electrocatalysts as claimed in claim 1 , having the composition Pt/IrO x —TiO 2 , PtCo/IrO x —TiO 2 , Pt/IrO x —Al 2 O 3 , Pt/SbSnO x —TiO 2 , PtNi/SbSnO x —Al 2 O 3 , Pt/TaSnO x —TiO 2 , Pt/NbSnO x —TiO 2 or PtNbTiO x —TiO 2 .

16. A process for preparing an electrocatalyst comprising an electrically conductive support and a catalytically active species, wherein the conductive support is an inorganic multicomponent support material of composition OX1-OX2 wherein
OX1 is an oxide which is not electrically conductive and has a specific surface area (BET) in the range from 50 to 400 m 2 /g and
OX2 is a conductive oxide,

and wherein the catalytically active species comprises a noble metal selected from the group consisting of ruthenium, osmium, rhodium, iridium, palladium, platinum, silver and gold, or mixtures or alloys thereof,
the process comprising the steps of
(a) coating the oxide OX1 with the conductive oxide OX2 by precipitation or impregnation with suitable OX2 precursor compounds to form conductive support OX1-OX2, and
(b) depositing the catalytically active species onto the conductive support OX1-OX2 by precipitation or impregnation with suitable metal precursor compounds.

17. The process as claimed in claim 16 , wherein the OX2 precursor compounds are selected from the group consisting of hexachloroiridic(IV) acid, iridium(III) chloride, iridium(III) nitrate, Ru(III) nitrosyl-nitrate, Ru(III) acetate, Ru(III) acetylacetonate, SnCl 4 *5H 2 O, Sn acetate, tin(II) nitrate, SbCl 3 , antimony(III) nitrate, antimony(III) acetate, ammonium molybdate ([NH 4 ] 2 MoO 4 ), sodium molybdate, ammonium tungstate ([NH 4 ] 2 WO 4 ), sodium tungstate, ammonium vanadate ([NH 4 ]VO 3 ), ammonium niobate(V) oxalate, ammonium tantalate(V) oxalate and sodium vanadate.

18. The process as claimed in claim 16 , wherein the metal precursor compounds comprise halogen-free and/or halogen-poor compounds of a noble metal.

19. The process as claimed in claim 16 further comprising drying and/or calcining of the conductive support OX1-OX2 after step (a).

20. The process as claimed in claim 16 further comprising a reduction, drying or calcining step, or a combination of such steps, after step (b).

21. A PEM fuel cell, direct methanol fuel cell (DMFC), regenerative fuel cell or electrolyzer comprising the electrocatalyst as claimed in claim 1 .

Assignees

• Umicore Ag & Co Kg

Inventors

• Klose-Schubert Barbara
• Herein Daniel
• Lopez Marco
• Becker Carsten

Classifications

• H01M8/20

  Indirect fuel cells, e.g. fuel cells with redox couple being irreversible (H01M8/18 takes precedence) · CPC title

• H01M4/8657 Primary

  layered · CPC title

• H01M4/9075

  Catalytic material supported on carriers, e.g. powder carriers (H01M4/8807, H01M4/881, H01M4/8814, H01M4/925 take precedence) · CPC title

• H01M4/9016

  Oxides, hydroxides or oxygenated metallic salts · CPC title

• H01M4/921

  Alloys or mixtures with metallic elements · CPC title