Core-shell particles with catalytic activity

Patent metadata

Field	Value
Publication number	US-9539563-B2
Application number	US-201214118748-A
Country	US
Kind code	B2
Filing date	May 30, 2012
Priority date	May 30, 2011
Publication date	Jan 10, 2017
Grant date	Jan 10, 2017

Abstract

The present invention pertains to novel core-shell particles comprising a core of iron oxide and a shell of cobalt oxide, characterized in that they are spherical with a number average diameter, as measured by TEM, of between 1 and 20 nm. This invention is also directed to their uses in the manufacture of a catalyst, and to the method for preparing these particles, by precipitating cobalt oxide onto magnetite or hematite particles which are themselves precipitated from Fe(III) and optionally Fe(II) salts.

First claim

The invention claimed is:

1. A method for the preparation of spherical core-shell particles, comprising the successive steps of:
(a) preparing an aqueous solution comprising a ferric salt, at a temperature of less than 50° C.;
(b) adding at least one base to said aqueous solution, so as to obtain a suspension of iron oxide particles having a pH value of from 10 to 14;
(c) washing the suspension;
(d) adding a strong acid to the washed suspension to peptize the washed suspension;
(e) reacting at least one base with said peptized suspension, until the pH reaches a value from 10 to 14, at a temperature of from 50 to 95° C.;
(f) adding a cobalt salt to the heated suspension in order to obtain spherical particles having a core of iron oxide and a shell comprising cobalt oxide.

2. The method according to claim 1 , characterized in that the aqueous solution comprising the ferric salt further includes a ferrous salt in a molar ratio of Fe(III) to Fe(II) of 2:1, whereby the iron oxide particles are magnetite particles.

3. The method according to claim 1 , characterized in that the ferric salt is ferric nitrate, ferric chloride or ferric hydroxide.

4. The method according to claim 2 , characterized in that the ferrous salt is ferrous nitrate, ferrous chloride or ferrous hydroxide.

5. The method according to claim 1 characterized in that the cobalt salt is cobalt nitrate, cobalt chloride or cobalt sulphate.

6. The method according to claim 1 , characterized in that the strong acid is nitric acid or hydrochloric acid.

7. The method according to claim 3 , characterized in that the ferric salt is ferric chloride.

8. The method according to claim 4 , characterized in that the ferrous salt is ferrous chloride.

9. The method according to claim 5 , characterized in that the cobalt salt is cobalt nitrate.

Assignees

• Calderone Vincenzo Roberto
• Shiju Nirappurackal Raveendran
• Rothenberg Gad
• Curulla-Ferre Daniel
• Total Raffinage Chimie

Inventors

• Calderone Vincenzo Roberto
• Shiju Nirappurackal Raveendran
• Rothenberg Gad
• Curulla-Ferre Daniel

Classifications

• B01J2235/00

  Indexing scheme associated with group B01J35/00, related to the analysis techniques used to determine the catalysts form or properties · CPC title

• B01J35/53

  with a core-shell structure · CPC title

• B01J35/45

  Nanoparticles · CPC title

• B01J37/0225

  of metal substrates · CPC title

• B01J35/08

  Operations & Transport · mapped topic