Clear coating composition and method for coating automobile body

Patent metadata

Field	Value
Publication number	US-9533328-B2
Application number	US-201214130455-A
Country	US
Kind code	B2
Filing date	Jul 12, 2012
Priority date	Jul 12, 2011
Publication date	Jan 3, 2017
Grant date	Jan 3, 2017

Abstract

To provide a coating composition, which is capable of providing a coating film on a resin part and on a steel plate part at the same time at lower temperatures than conventional coating compositions, and which is capable of providing a coating film that has excellent bending resistance. A clear coating composition, which contains a base material that contains an acrylic polyol, a crosslinking agent that is composed of an active methylene type blocked isocyanate and a melamine resin, and a curing catalyst. The mass ratio of the base material to the melamine resin is 1.5-9.0, and the mass percentage of the active methylene type blocked isocyanate in the composition is set within a specific range when the total of the mass percentage of the base material and the mass percentage of the melamine resin in the composition is taken as 100% by mass.

First claim

The invention claimed is:

1. A method for coating an automobile body, comprising:
a base-coating coating step of simultaneously coating a base coating on both parts among a resin part and a steel sheet part of an automobile body to form a base coating film thereon;
a clear-coating coating step of simultaneously coating a clear coating on both parts among the resin part and the steel sheet part on which the base coating film was formed to form a clear coating film thereon; and
a curing step of baking the dear coating film to cure,
wherein the clear-coating coating step coats a clear coating composition that comprises:
a base resin containing acrylic polyol;
a crosslinking agent consisting of an active methylene blocked isocyanate and melamine resin; and
a curing catalyst that contains dibutyltin dilaurate as a blocked isocyanate curing catalyst, and p-toluene sulfonic acid as a melamine curing catalyst,
wherein a mass ratio of the base resin to the melamine resin is 1.5 to 9.0,
when defining a total of mass percentage of the base resin and mass percentage of the melamine resin in the composition as 100% by mass, the minimum value for mass percentage of the active methylene blocked isocyanate in the composition is calculated according to formula (1) below, and the maximum value thereof is calculated according to formula (2) below, and
wherein the base-coating coating step coats a base coating that contains the active methylene blocked isocyanate and the melamine resin, which are the same as those blended in the clear coating composition,

[Math. 1]
Minimum value=−4.13×(mass ratio of base resin to melamine resin)+38.52  (1)

Maximum value=1.74×(mass ratio of base resin to melamine resin)+43.21  (2).

2. A method for coating an automobile body according to claim 1 ,
wherein the clear coating composition is a two-part coating composition consisting of a first liquid and a second liquid,
the melamine resin being contained in the first liquid, and the melamine curing catalyst being contained in the second liquid.

3. A method for coating an automobile body according to claim 1 , further comprising:
an electrocoating step of electrocoating a steel sheet component forming the steel sheet part, prior to the base-coating coating step; and
an assembly step of assembling the steel sheet component thus electrocoated and a resin component forming the resin part so as to make a set of an automobile body,
wherein the clear coating is coated wet-on-wet in the clear-coating coating step, and
wherein the base coating film and the clear coating film are simultaneously baked to cure in the curing step.

4. A method for coating an automobile body according to claim 2 , further comprising:
an electrocoating step of electrocoating a steel sheet component forming the steel sheet part, prior to the base-coating coating step; and
an assembly step of assembling the steel sheet component thus electrocoated and a resin component forming the resin part so as to make a set of an automobile body,
wherein the clear coating is coated wet-on-wet in the clear-coating coating step, and
wherein the base coating film and the clear coating film are simultaneously baked to cure in the curing step.

Assignees

• Kondo Masuo
• Kojima Keisuke
• Honda Motor Co Ltd

Inventors

• Kondo Masuo
• Kojima Keisuke

Classifications

• C08G2150/90

  Compositions for anticorrosive coatings · CPC title

• C09D4/00

  Coating compositions, e.g. paints, varnishes or lacquers, based on organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond {; Coating compositions, based on monomers of macromolecular compounds of groups C09D183/00 - C09D183/16} · CPC title

• C09D175/04

  Polyurethanes · CPC title

• B05D7/532

  the two layers being cured or baked together, i.e. wet on wet · CPC title

• C08G18/8093

  Compounds containing active methylene groups · CPC title