Abstract

A hydrocracking catalyst, containing a USY zeolite modified by treatment with an organic acid to remove aluminum, an alumina binder, two or more metals selected from metals of Groups VIB and VIII, and cerium in the range of 0.1 to 5.0 wt %. A method of making the hydrocracking catalyst, whereby a USY zeolite is treated with an organic acid to remove aluminum from the zeolite structure and subsequently impregnating with a rare earth metal of the Lanthanide series to form a modified USY zeolite. The modified USY zeolite is mixed with alumina comprising a peptizing agent and impregnated with two or more metals selected from metals of Groups VIB and VIII.

First claim

The invention claimed is:

1. A hydrocracking catalyst, comprising: a USY zeolite modified by treatment with an organic acid to remove aluminum; an alumina binder; two or more metals selected from metals of Groups VIB and VIII; and cerium in the range of 0.1 to 5.0 wt. %; wherein the USY zeolite has an acidity ranging from 0.86-0.99 mmol/g.

2. The catalyst of claim 1 , wherein the metal of Group VIB is W.

3. The catalyst of claim 1 , wherein the metal of Group VIII is Ni.

4. The hydrocracking catalyst of claim 1 , wherein at least one of the metals of Group VIB and the metals of Group VIII is in sulfided form.

5. The hydrocracking catalyst of claim 1 , wherein a Si/Al molar ratio of the USY zeolite is in the range of 6-10.

6. The hydrocracking catalyst of claim 1 , wherein the amount of the USY zeolite is from 25 to 50 wt % based on the total weight of the catalyst.

7. The hydrocracking catalyst of claim 1 , wherein the amount of the alumina binder is from 25 to 50 wt % based on the total weight of the catalyst.

8. The hydrocracking catalyst of claim 1 , comprising WO 3 in an amount of from 20 to 30 wt % based on a total weight of the catalyst.

9. The hydrocracking catalyst of claim 1 , comprising NiO in an amount of 1 to 10 wt % based on a total weight of the catalyst.

10. A process of hydrocracking, comprising hydrocracking of a hydrotreated vacuum gas oil with the hydrocracking catalyst of claim 1 .

11. The hydrocracking catalyst of claim 1 , wherein the USY zeolite has an aluminum content ranging from 8.01-9.80 wt % relative to the total weight of the USY zeolite.

12. The hydrocracking catalyst of claim 1 , wherein the USY zeolite has an acidity of 0.86 mmol/g.

13. The hydrocracking catalyst of claim 1 , wherein the USY zeolite has an acidity of 0.99 mmol/g.

Assignees

• Univ King Fahd Pet & Minerals

Inventors

• Ahmed Shakeel
• Ali Mohammad Ashraf

Classifications

• B01J2229/37

  Acid treatment · CPC title

• C10G47/20

  the catalyst containing other metals or compounds thereof · CPC title

• B01J2523/3712

  Cerium · CPC title

• B01J2229/16

  to increase the Si/Al ratio; Dealumination · CPC title

• B01J29/166 Primary

  Y-type faujasite · CPC title