Method for producing masterbatches

Patent metadata

Field	Value
Publication number	US-9527966-B2
Application number	US-201214367115-A
Country	US
Kind code	B2
Filing date	Dec 7, 2012
Priority date	Dec 20, 2011
Publication date	Dec 27, 2016
Grant date	Dec 27, 2016

Abstract

The method of producing a masterbatch according to the present invention is a method of producing a masterbatch in which a metal salt compound is incorporated into a polyester resin, the method being characterized by comprising: a first step of obtaining a kneaded product by feeding the polyester resin and the metal salt compound to an extruder and melt-kneading the polyester resin and the metal salt compound; and a second step of, while continuing kneading after the first step, further feeding the polyester resin to the extruder and kneading the resulting mixture, wherein, in the first step, the polyester resin and the metal salt compound are fed at such a mass ratio that the amount of the metal salt compound is not more than twice the amount of the polyester resin; the total amount of the polyester resin fed in the first and second steps and the metal salt compound fed in the first step is, in terms of mass ratio, in the range of 2 to 20 times the total amount of the polyester resin and the metal salt compound that are fed in the first step.

First claim

The invention claimed is:

1. A method of producing a masterbatch in which a metal salt compound is incorporated into a polyester resin, said method comprising:
a first step of obtaining a kneaded product by feeding said polyester resin and said metal salt compound to an extruder and melt-kneading said polyester resin and said metal salt compound; and
a second step of, while continuing kneading after said first step, further feeding said polyester resin to said extruder and kneading the resulting mixture, wherein,
in said first step, said polyester resin and said metal salt compound are fed at such a mass ratio that the amount of said metal salt compound is not more than twice the amount of said polyester resin;
the total amount of said polyester resin fed in said first and second steps and said metal salt compound fed in said first step is, in terms of mass ratio, in the range of 2 to 20 times the total amount of said polyester resin and said metal salt compound that are fed in said first step;
the processing temperature in said first step is in the range of 20° C. to 80° C. higher than the melting point of said polyester resin; and
the processing temperature in said second step is in the range of 0° C. to 50° C. higher than the melting point of said polyester resin.

2. The method of producing a masterbatch according to claim 1 , wherein said metal salt compound is at least one selected from the group consisting of metal benzoates, aliphatic metal carboxylates, metal salts of sulfonamide compounds and metal salts of sulfonimide compounds.

3. The method of producing a masterbatch according to claim 1 , wherein said polyester resin is at least one selected from the group consisting of polyethylene terephthalate, polytrimethylene terephthalate, polybutylene terephthalate, polyethylene naphthalate and polybutylene naphthalate.

4. The method of producing a masterbatch according to claim 1 , wherein, in said second step, said polyester is fed to said kneaded product obtained in said first step by a side feeder.

5. A method of producing a masterbatch in which a metal salt compound is incorporated into a polyester resin, said method comprising:
a first step of obtaining a kneaded product by feeding said polyester resin and said metal salt compound to an extruder and melt-kneading said polyester resin and said metal salt compound; and
a second step of, while continuing kneading after said first step, further feeding said polyester resin to said extruder and kneading the resulting mixture,
wherein:
said metal salt compound is at least one selected from the group consisting of metal benzoates, aliphatic metal carboxylates, metal salts of sulfonamide compounds and metal salts of sulfonimide compounds;
in said first step, said polyester resin and said metal salt compound are fed at such a mass ratio that the amount of said metal salt compound is not more than twice the amount of said polyester resin;
the total amount of said polyester resin fed in said first and second steps and said metal salt compound fed in said first step is, in terms of mass ratio, in the range of 2 to 20 times the total amount of said polyester resin and said metal salt compound that are fed in said first step;
the processing temperature in said first step is in the range of 20° C. to 80° C. higher than the melting point of said polyester resin; and
the processing temperature in said second step is in the range of 0° C. to 50° C. higher than the melting point of said polyester resin.

Assignees

• Adeka Corp

Inventors

• Urushihara Tsuyoshi
• Tsuneizumi Yota

Classifications

• B29C48/405

  Intermeshing co-rotating screws · CPC title

• C08J2367/02

  Polyesters derived from dicarboxylic acids and dihydroxy compounds; (C08J2367/06 takes precedence) · CPC title

• B29K2503/04

  Inorganic materials · CPC title

• B29K2509/00

  Use of inorganic materials not provided for in groups {B29K2503/00 - B29K2507/00,} as filler · CPC title

• C08J3/201

  Pre-melted polymers · CPC title