Negative electrode for alkaline secondary battery, outer case for alkaline secondary battery and alkaline secondary battery

Patent metadata

Field	Value
Publication number	US-9525166-B2
Application number	US-201214234461-A
Country	US
Kind code	B2
Filing date	Jul 27, 2012
Priority date	Jul 28, 2011
Publication date	Dec 20, 2016
Grant date	Dec 20, 2016

Abstract

A negative electrode for an alkaline secondary battery includes a current collecting substrate having a substrate containing iron. The current collecting substrate does not have a conductive protecting layer, or has a conductive protecting layer having a thickness of 3 μm or less or having defects, on the substrate. The negative electrode contains magnesium or a magnesium compound and a hydrogen storing alloy.

First claim

The invention claimed is:

1. A negative electrode for an alkaline secondary battery comprising a current collecting substrate having a substrate containing iron,
wherein the current collecting substrate has a conductive protecting layer having defects by which the substrate containing iron is partially exposed, on the substrate,
wherein the negative electrode contains magnesium or a magnesium compound and a hydrogen storage alloy, and
wherein the content of magnesium or the magnesium compound is 1.0 to 3.0% by mass with respect to the total amount of the hydrogen storage alloy and magnesium or the magnesium compound in the negative electrode.

2. The negative electrode for an alkaline secondary battery according to claim 1 , wherein the protecting layer comprises nickel.

3. The negative electrode for an alkaline secondary battery according to claim 1 , wherein a hydrogen storage alloy layer is formed on the current collecting substrate, the hydrogen storage alloy layer containing magnesium or a magnesium compound and a hydrogen storage alloy.

4. The negative electrode for an alkaline secondary battery according to claim 1 , wherein a magnesium compound layer and a hydrogen storage alloy layer are formed on the current collecting substrate.

5. The negative electrode for an alkaline secondary battery according to claim 4 , wherein the magnesium compound layer is formed directly on the current collecting substrate having the substrate containing iron and the conductive protecting layer.

6. The negative electrode for an alkaline secondary battery according to claim 1 , wherein a magnesium layer is formed on the current collecting substrate when the negative electrode is observed by using an electron probe microanalyzer.

7. The negative electrode for an alkaline secondary battery according to claim 1 , wherein the magnesium compound is magnesium oxide.

8. An alkaline secondary battery comprising the negative electrode for an alkaline secondary battery according to claim 1 .

9. A negative electrode for an alkaline secondary battery comprising a current collecting substrate having a substrate containing iron,
wherein the current collecting substrate does not have a conductive protecting layer on the substrate containing iron,
wherein the negative electrode contains magnesium or a magnesium compound and a hydrogen storage alloy, and
wherein the content of magnesium or the magnesium compound is 1.0 to 3.0% by mass with respect to the total amount of the hydrogen storage alloy and magnesium or the magnesium compound in the negative electrode.

10. The negative electrode for an alkaline secondary battery according to claim 9 , wherein a hydrogen storage alloy layer is formed on the current collecting substrate, the hydrogen storage alloy layer containing magnesium or a magnesium compound and a hydrogen storage alloy.

11. The negative electrode for an alkaline secondary battery according to claim 9 , wherein a magnesium compound layer and a hydrogen storage alloy layer are formed on the current collecting substrate.

12. The negative electrode for an alkaline secondary battery according to claim 11 , wherein the magnesium compound layer is formed directly on the current collecting substrate.

13. The negative electrode for an alkaline secondary battery according to claim 9 , wherein a magnesium layer is formed on the current collecting substrate when the negative electrode is observed by using an electron probe microanalyzer.

14. The negative electrode for an alkaline secondary battery according to claim 9 , wherein the magnesium compound is magnesium oxide.

15. An alkaline secondary battery comprising the negative electrode for an alkaline secondary battery according to claim 9 .

16. A negative electrode for an alkaline secondary battery comprising a current collecting substrate having a substrate containing iron,
wherein the current collecting substrate has a conductive protecting layer having defects by which the substrate containing iron is partially exposed, on the substrate,
wherein the negative electrode comprises:
a magnesium compound layer comprising magnesium or a magnesium compound; and
a hydrogen storage alloy layer comprising a hydrogen storage alloy, and

wherein the conductive protecting layer is in direct contact with the substrate, the magnesium compound layer is in direct contact with the conductive protecting layer and an exposed part of the substrate, and the hydrogen storage alloy layer is in direct contact with the magnesium compound layer.

17. A negative electrode for an alkaline secondary battery comprising a current collecting substrate having a substrate containing iron,
wherein the current collecting substrate does not have a conductive protecting layer on the substrate containing iron,
wherein the negative electrode comprises:
a magnesium compound layer comprising magnesium or a magnesium compound, the magnesium compound layer being in direct contact with the substrate; and
a hydrogen storage alloy layer comprising a hydrogen storage alloy, the hydrogen storage alloy layer being in direct contact with the magnesium compound layer.

Assignees

• Kakeya Tadashi
• Kanemoto Manabu
• Kodama Mitsuhiro
• Gs Yuasa Int Ltd

Inventors

• Kakeya Tadashi
• Kanemoto Manabu
• Kodama Mitsuhiro

Classifications

• H01M10/24

  Alkaline accumulators · CPC title

• H01M4/383

  Hydrogen absorbing alloys · CPC title

• H01M4/134 Primary

  Electrodes based on metals, Si or alloys · CPC title

• H01M4/36

  Selection of substances as active materials, active masses, active liquids · CPC title

• H01M4/661

  Metal or alloys, e.g. alloy coatings (H01M4/669 take precedence) · CPC title