Method to achieve tribocharge uniformity of a developer mix across different temperature and humidity conditions by modifying the surface of the magnetic carrier particle

Patent metadata

Field	Value
Publication number	US-9523932-B2
Application number	US-201414580830-A
Country	US
Kind code	B2
Filing date	Dec 23, 2014
Priority date	Dec 23, 2014
Publication date	Dec 20, 2016
Grant date	Dec 20, 2016

Abstract

A method for providing a developer mix having tribocharge uniformity across varying temperature and humidity conditions is provided. A developer mix used in a dual component development (DCD) system typically is a mixture of toner particles and magnetic carrier particles. Tribocharge uniformity is achieved in the developer mix by performing the step of treating the surface of the magnetic carrier particles with surface additives before the magnetic carrier particles are mixed with the toner particles. Surface additives include but are not limited to silica, titania and alumina.

First claim

What is claimed is:

1. A method for forming a developer mix to be used in an electrophotographic imaging device comprising:
providing toner particles formed an emulsion aggregation process;
providing magnetic carrier particles having a polymer coating on its outer surface;
surface treating the outer surface of the polymer coated magnetic carrier particles with one or more extra particular additives selected from the group consisting of silica, titania and alumina or combinations thereof: and
mixing the toner particles and the surface treated polymer coated magnetic carrier particles.

2. The method of claim 1 further comprising the steps of screening the surface treated polymer coated magnetic carrier particles to remove extra particular additives having large agglomerates prior to the mixing of the surface treated polymer coated magnetic carrier particles and the toner particles.

3. The method of claim 1 , wherein the polymer coating is acrylic.

4. The method of claim 1 wherein the polymer coated magnetic carrier particles have a ferrite core.

5. The method of claim 1 wherein the polymer coated magnetic carrier particles have an average particle size between 30 μm to about 50 μm and a saturation magnetization of 50 and 120 emu/g (A·m 2 /kg).

6. The method of claim 1 , wherein the extra particulate additives are surface treated with a hydrophobizing agent selected from a group consisting of hexamethyldisilazane, polydimethylsiloxane, dimethyldiethoxysiloxane, octyltriethoxysilane and combinations thereof.

7. The method of claim 1 , wherein the extra particulate additives have an average primary particle size in the range of about 8 nm to about 100 nm.

8. The method of claim 1 , wherein the extra particulate additives are present in the range of about 0.05% to about 1.0% by weight of the polymer coated magnetic carrier particles.

9. The method of claim 1 , wherein the extra particulate additives are present in the range of about 0.06% to about 0.15% by weight of the polymer coated magnetic carrier particles.

10. The method of claim 1 wherein the extra particulate additives are titania.

11. The method of claim 1 wherein the extra particulate additives are silica.

12. A method for forming a developer mix to be used in an electrophotographic imaging device comprising:
providing toner particles formed using an emulsion aggregation process;
providing magnetic carrier particles having a polymer coating on their outer surface;
surface treating the outer surface of the polymer coated magnetic carrier particle with one or more extra particular additives selected from the group consisting of silica, titania and alumina:
screening the surface treated polymer coated magnetic carrier particles to remove large agglomerates of the extra particular additives: and
mixing the toner particles with the screened surface treated polymer coated magnetic carrier particles.

Assignees

• Lexmark Int Inc

Inventors

• Srinivasan Kasturi Rangan
• Bejat Ligia Aura
• Blassingame Michael Anthony
• Jones Rick Owen
• Lin Brandon Michael
• Minor James Craig

Classifications

• G03G9/1075

  Structural characteristics of the carrier particles, e.g. shape or crystallographic structure · CPC title

• G03G9/0817

  Separation; Classifying · CPC title

• G03G9/0808 Primary

  by dry mixing the toner components in solid or softened state · CPC title

• G03G9/0815

  Post-treatment · CPC title

• G03G9/1139 Primary

  Inorganic components of coatings · CPC title