Cold-rolled steel sheet

Patent metadata

Field	Value
Publication number	US-9523139-B2
Application number	US-201214130552-A
Country	US
Kind code	B2
Filing date	Jun 27, 2012
Priority date	Jul 6, 2011
Publication date	Dec 20, 2016
Grant date	Dec 20, 2016

Abstract

A high-strength cold-rolled steel sheet excellent in ductility, work hardenability, and stretch flangeability, and having tensile strength of 780 MPa or more includes: a chemical composition containing, in mass percent, C: more than 0.020% to less than 0.30%, Si: more than 0.10% to 3.00% or less, Mn: more than 1.00% to 3.50% or less; and metallurgical structure whose main phase is a low-temperature transformation product, and whose secondary phase contains retained austenite. The retained austenite has a volume fraction relative to overall structure of more than 4.0% to less than 25.0% and an average grain size of less than 0.80 μm, and of the retained austenite, the number density of retained austenite grains whose grain size is 1.2 μm or more is 3.0×10 −2 grains/μm 2 or less.

First claim

The invention claimed is:

1. A cold-rolled steel sheet having a chemical composition consisting of, in mass percent, C: more than 0.020% to less than 0.30%; Si: more than 0.10% to at most 3.00%; Mn: more than 1.00% to at most 3.50%; P: at most 0.10%; S: at most 0.010%; sol.Al: at least 0% and at most 2.00%; N: at most 0.010%; Ti: at least 0% and less than 0.050%; Nb: at least 0% and less than 0.050%; V: at least 0% and at most 0.50%; Cr: at least 0% and at most 1.0%; Mo: at least 0% and at most 0.50%; B: at least 0% and at most 0.010%; Ca: at least 0% and at most 0.010%; Mg: at least 0% and at most 0.010%; REM: at least 0% and at most 0.050%; Bi: at least 0% and at most 0.050%; and the remainder being Fe and impurities, and
having metallurgical structure whose main phase is a low-temperature transformation product, and whose secondary phase contains retained austenite, the retained austenite having a volume fraction of more than 4.0% to less than 25.0% relative to overall structure, and an average grain size of less than 0.80 μm, and
wherein of the retained austenite, a number density of retained austenite grains whose grain size is 1.2 μm or more is 3.0×10 −2 grains/μm 2 or less.

2. The cold-rolled steel sheet as set forth in claim 1 , wherein the average grain size of the grains having a bcc structure and the grains having a bct structure surrounded by a grain boundary having a misorientation angle of 15 or larger is 7.0 μm or smaller in the metallurgical structure.

3. The old-rolled steel sheet as set forth in claim 1 , wherein
in the metallurgical structure, the secondary phase contains the retained austenite and polygonal ferrite, and
the polygonal ferrite has a volume fraction relative to overall structure of more than 2.0% to less than 27.0%, and an average grain size of less than 5.0 μm.

4. The cold-rolled steel sheet as set forth in claim 1 , wherein the chemical composition contains, in mass percent, one kind or two or more kinds selected from a group consisting of Ti: at least 0.005% and less than 0.050%, Nb: at least 0.005% and less than 0.050%, and V: at least 0.010% and at most 0.50%.

5. The cold-rolled steel sheet as set forth in claim 1 , wherein the chemical composition contains, in mass percent, one kind or two or more kinds selected from a group consisting of Cr: at least 0.20% and at most 1.0%, Mo: at least 0.05% and at most 0.50%, and B: at least 0.0010% and at most 0.010%.

6. The old-rolled steel sheet as set forth in claim 1 , wherein the chemical composition contains, in mass percent, one kind or two or more kinds selected from a group consisting of Ca: at least 0.0005% and at most 0.010%, Mg: at least 0.0005% and at most 0.010%, REM: at least 0.0005% and at most 0.050%, and Bi: at least 0.0010% and at most 0.50%.

Assignees

• Haga Jun
• Nishio Takuya
• Wakita Masayuki
• Tanaka Yasuaki
• Imai Norio
• Tomida Toshiro
• Nippon Steel & Sumitomo Metal Corp

Inventors

• Haga Jun
• Nishio Takuya
• Wakita Masayuki
• Tanaka Yasuaki
• Imai Norio
• Tomida Toshiro

Classifications

• C21D1/673

  for die quenching · CPC title

• C22C38/001 Primary

  containing N · CPC title

• C21D2211/002

  Bainite · CPC title

• C22C38/26

  with niobium or tantalum · CPC title

• C21D2211/001

  Austenite · CPC title