Treated coated article and process of treating a coated article

Patent metadata

Field	Value
Publication number	US-9518325-B2
Application number	US-201313847253-A
Country	US
Kind code	B2
Filing date	Mar 19, 2013
Priority date	Mar 19, 2013
Publication date	Dec 13, 2016
Grant date	Dec 13, 2016

Abstract

A process of treating a coated article and a treated article are disclosed. The process includes providing an article having a MCrAlY coating, applying an aluminide treatment onto the MCrAlY coating to form a treated MCrAlY coating, and outwardly forming β-phase material from the MCrAlY coating into the treatment. The applying is selected from the group consisting of soaking, spraying, brushing, dipping, pouring, pack cementation, vapor deposition, and combinations thereof. The treated article includes a substrate and a treated MCrAlY coating positioned on at least a portion of the substrate. The treated MCrAlY coating includes a β-phase aluminide in a spray-applied, brush-applied, pour-applied, dip-applied, pack cement-applied, vapor deposit-applied, or soaking-applied treatment.

First claim

What is claimed is:

1. A process of treating a coated article, the process comprising:
commencing a service period of a gas turbine, the service period being the period throughout which operation of the gas turbine is suspended, the gas turbine including the coated article having a MCrAlY coating;
during the service period, applying an aluminide treatment including at least one of NiAl and Ni 2 Al 3 onto the MCrAlY coating to form a treated MCrAlY coating, the aluminide treatment diffusing into the MCrAlY coating by a depth of at least 1 mil, the depth of the MCrAlY into which the aluminide treatment has diffused possessing a strain range of about 4%; and
outwardly forming (β-phase material from the MCrAlY coating into the treatment;
wherein the applying is selected from the group consisting of soaking, spraying, brushing, dipping, pouring, and combinations thereof, and the process is performed without stripping any MCrAlY from the coated article or re-coating the coated article with MCrAlY during the service period.

2. The process of claim 1 , comprising heating the aluminide treatment to a predetermined temperature range of between about 1600° F. and 2200° F.

3. The process of claim 1 , comprising heating the aluminide treatment to a predetermined temperature range of between about 1900° F. and 2150° F.

4. The process of claim 1 , comprising heating the aluminide treatment to a predetermined temperature range of between about 1950° F. and 2050° F.

5. The process of claim 1 , wherein the MCrAlY coating includes a depletion of (β-phase aluminide prior to the applying of the aluminide treatment.

6. The process of claim 1 , wherein the aluminide treatment diffuses into the MCrAlY coating by a depth of about 2 mils.

7. The process of claim 1 , comprising providing the aluminide treatment with aluminum at a concentration, by weight, of between about 15% and about 30%.

8. The process of claim 1 , comprising providing the aluminide treatment with aluminum at a concentration, by weight, of about 20%.

9. The process of claim 1 , wherein the aluminide treatment includes NiAl.

10. The process of claim 1 , wherein the aluminide treatment includes Ni 2 Al 3 .

11. The process of claim 1 , wherein the aluminide treatment is a slurry.

12. The process of claim 1 , comprising providing an inert atmosphere for the process.

13. A process of treating a coated article, the process comprising:
commencing a service period of a gas turbine, the service period being the period throughout which operation of the gas turbine is suspended, the gas turbine including the coated article having a MCrAlY coating;
during the service period, spraying an aluminide treatment including at least one of NiAl and Ni 2 Al 3 onto the MCrAlY coating to form a treated MCrAlY coating, the aluminide treatment diffusing into the MCrAlY coating by a depth of at least 1 mil, the depth of the MCrAlY into which the aluminide treatment has diffused possessing a strain range of about 4%; and
outwardly forming (β-phase material from the MCrAlY coating into the aluminide treatment,
wherein the process is performed without stripping any MCrAlY from the coated article or re-coating the coated article with MCrAlY during the service period.

14. The process of claim 13 , wherein the (β-phase material includes (β-phase aluminide.

15. The process of claim 13 , wherein the MCrAlY coating includes a depletion of (β-phase aluminide prior to the spraying of the aluminide treatment.

Assignees

• Gen Electric

Inventors

• Bucci David Vincent
• Cavanaugh Dennis William

Classifications

• C23C28/021

  including at least one metal alloy layer · CPC title

• C23C28/028

  Including graded layers in composition or in physical properties, e.g. density, porosity, grain size · CPC title

• C23C10/26

  more than one element being diffused · CPC title

• Y10T428/12535

  with additional, spatially distinct nonmetal component · CPC title

• C23C28/022 Primary

  with at least one MCrAlX layer · CPC title