Milling process

Patent metadata

Field	Value
Publication number	US-9518178-B2
Application number	US-201214239004-A
Country	US
Kind code	B2
Filing date	Aug 9, 2012
Priority date	Aug 17, 2011
Publication date	Dec 13, 2016
Grant date	Dec 13, 2016

Abstract

The invention pertains to a process for cryogenic milling mixtures of (per)fluoroelastomers and semicrystalline thermoplastic VDF polymers, and to free-flowing micronized pellets obtainable therefrom, said micronized pellets advantageously yielding, after extrusion and compounding, excellent mechanical properties, even improved over those of base fluoroelastomer matrix.

First claim

The invention claimed is:

1. A process for manufacturing micronized pellets of a (per)fluoroelastomer composition, said process comprising milling a composition consisting essentially of at least one (per)fluoroelastomer (A) and at least one thermoplastic semicrystalline vinylidene fluoride polymer (F) at a temperature below glass transition temperature of said (per)fluoroelastomer, wherein the micronized pellets, after 24 hours of storage at room temperature, have a pourability of less than 60 s when measured according to ASTM D1895 standard, using the funnel of Test method B and the cylinder of Test Method A, when measured at room temperature.

2. The process of claim 1 , wherein fluoroelastomer (A) is selected from the group consisting of:
(1) VDF-based copolymers, in which VDF is copolymerized with at least one comonomer selected from the group consisting of:
(a) C 2 -C 8 perfluoroolefins;
(b) hydrogen-containing C 2 -C 8 olefins;
(c) C 2 -C 8 chloro and/or bromo and/or iodo-fluoroolefins;
(d) (per)fluoroalkylvinylethers (PAVE) of formula CF 2 ═CFOR f , wherein R f is a C 1 -C 6 (per)fluoroalkyl group;
(e) (per)fluoro-oxy-alkylvinylethers of formula CF 2 ═CFOX, wherein X is a C 1 -C 12 ((per)fluoro)-oxyalkyl comprising catenary oxygen atoms;
(f) (per)fluorodioxoles having formula:

wherein R f3 , R f4 , R f5 , R f6 , equal or different from each other, are independently selected from fluorine atoms and C 1 -C 6 (per)fluoroalkyl groups, optionally comprising one or more than one oxygen atom;
(g) (per)fluoro-methoxy-vinylethers (MOVE) having formula:
CFX 2 ═CX 2 OCF 2 OR″ f

wherein R″ f is selected from C 1 -C 6 (per)fluoroalkyls, linear or branched; C 5 -C 6 cyclic (per)fluoroalkyls; and C 2 -C 6 (per)fluorooxyalkyls, linear or branched, comprising from 1 to 3 catenary oxygen atoms, and X 2 is selected from F and H; and
(h) C 2 -C 8 non-fluorinated olefins (Ol); and

(2) TFE-based copolymers, in which TFE is copolymerized with at least one comonomer chosen from (c), (d), (e), (g), (h) as above detailed and (i) perfluorovinyl ethers containing cyanide groups.

3. The process of claim 2 , wherein fluoroelastomer (A) is selected from the group consisting of VDF-based copolymers, as defined in claim 2 .

4. The process of claim 1 , wherein fluoroelastomer (A) comprises recurring units derived from a bis-olefin (OF) having general formula:

wherein R 1 , R 2 , R 3 , R 4 , R 5 and R 6 , equal or different from each other, are H or C 1 -C 5 alkyl; Z is a linear or branched C 1 -C 18 alkylene or cycloalkylene radical, optionally containing oxygen atoms, or a (per)fluoropolyoxyalkylene radical.

5. The process of claim 4 , wherein said bis-olefin (OF) is selected from the group consisting of olefins complying with formulae (OF-1), (OF-2) and (OF-3):

wherein j is an integer between 2 and 10, and R1, R2, R3, R4, equal or different from each other, are H, F or C 1-5 alkyl or (per)fluoroalkyl;

wherein each of A, equal or different from each other and at each occurrence, is independently selected from F, Cl, and H; each of B, equal or different from each other and at each occurrence, is independently selected from F, Cl, H and OR B , wherein R B is a branched or straight chain alkyl radical which can be partially, substantially or completely fluorinated or chlorinated; E is a divalent group having 2 to 10 carbon atoms, optionally fluorinated, which may be inserted with ether linkages; and

wherein E, A and B have the same meaning as above defined; and R5, R6, R7, equal or different from each other, are H, F or C 1-5 alkyl or (per)fluoroalkyl.

6. The process according to claim 1 , wherein fluoroelastomer (A) comprises iodine and/or bromine cure sites in such amount that the content of iodine and/or bromine in fluoroelastomer (A) is at least 0.05% wt, and not exceeding 2% wt, with respect to the total weight of fluoroelastomer (A).

7. The process according to claim 6 , wherein said cure sites comprise pendant groups bound to the backbone of the fluoroelastomer (A) polymer chain or terminal groups of said polymer chain.

8. The process according to claim 1 , wherein polymer (F) has a heat of fusion, measured according to ASTM standard D 3418, of at least 5 J/g.

9. The process according to claim 1 , wherein polymer (F) is chosen from VDF homopolymers and copolymers of VDF with one or more comonomers containing at least one unsaturation of ethylenic type, wherein the amount of VDF in said copolymers is greater than 85 mol %, based on the total amount of recurring units.

10. The process according to claim 9 , wherein polymer (F) is selected from the group consisting of VDF homopolymers and VDF copolymers consisting essentially of repeating units derived from VDF and between 0.1 mol % and 15 mol % of repeating units derived from a comonomer chosen from hexafluoropropylene (HFP), chlorotrifluoroethylene (CTFE) and trifluoroethylene (TrFE), and mixtures thereof.

11. The process according to claim 1 , wherein the amount of polymer (F) in the composition is between 5% and 80% by weight relative to the total weight of fluoroelastomer (A) and polymer (F).

12. Micronized pellets of a composition comprising at least one (per)fluoroelastomer (A) and at least one thermoplastic semicrystalline vinylidene fluoride polymer (F), as prepared by the process according to claim 1 , having a pourability of less than 60 s when measured according to ASTM D1895 standard, using the funnel of Test method B and the cylinder of Test Method A, when measured at room temperature.

13. A peroxide curable composition comprising the micronized pellets of claim 12 and at least one peroxide.

14. An ionically curable composition comprising micronized pellets of claim 12 and at least one curing agent and at least one accelerator.

15. The process of claim 2 , wherein fluoroelastomer (A) is selected from the group consisting of:
(1) VDF-based copolymers, in which VDF is copolymerized with at least one comonomer selected from the group consisting of:
(a) C 2 -C 8 perfluoroolefins selected from tetrafluoroethylene (TFE), hexafluoropropylene (HFP) and hexafluoroisobutylene;
(b) hydrogen-containing C 2 -C 8 olefins selected from vinyl fluoride (VF), trifluoroethylene (TrFE), and perfluoroalkyl ethylenes of formula CH 2 ═CH—R f , wherein R f is a C 1 -C 6 perfluoroalkyl group;
(c) chlorotrifluoroethylene (CTFE);
(d) (per)fluoroalkylvinylethers (PAVE) of formula CF 2 ═CFOR f , wherein R f is selected from CF 3 , C 2 F 5 and C 3 F 7 ;
(e) (per)fluoro-oxy-alkylvinylethers of formula CF 2 ═CFOX, wherein X is perfluoro-2-propoxypropyl;
(per)fluorodioxoles having formula:

wherein R f3 , R f4 , R f5 , R f6 , equal or different from each other, are independently selected from fluorine, —CF 3 , —C 2 F 5 , —C 3 F 7 , —OCF 3 and —OCF 2 CF 2 OCF 3 ;
(g) (per)fluoro-methoxy-vinylethers (MOVE) having formula:

Assignees

• Chernysheva Liubov
• Comino Giovanni
• Brinati Giulio
• Solvay Specialty Polymers It

Inventors

• Chernysheva Liubov
• Comino Giovanni
• Brinati Giulio

Classifications

• C08F214/22 Primary

  Vinylidene fluoride · CPC title

• C08F214/225

  with non-fluorinated comonomers · CPC title

• C08F214/222

  with fluorinated vinyl ethers · CPC title

• C08L27/16

  Homopolymers or copolymers or vinylidene fluoride · CPC title

• C08L27/20 Primary

  Homopolymers or copolymers of hexafluoropropene · CPC title