Super absorbent polymer and a preparation method thereof

Patent metadata

Field	Value
Publication number	US-9517446-B2
Application number	US-201314394685-A
Country	US
Kind code	B2
Filing date	Apr 23, 2013
Priority date	Apr 25, 2012
Publication date	Dec 13, 2016
Grant date	Dec 13, 2016

Abstract

The present invention relates to a super absorbent polymer (SAP) and a preparation method thereof. More specifically, the present invention provides a SAP satisfying the overall properties required to a SAP and especially the superior initial absorbency and absorbing rate under load at the same time, and a preparation method thereof, by treating the surface of the SAP with a surface treatment solution including water and a diol-based or glycol-based surface crosslinking agent.

First claim

The invention claimed is:

1. A super absorbent polymer (SAP), comprising
a base polymer powder comprising a crosslinked polymer of at least partially neutralized water-soluble ethylenic unsaturated monomer of acrylic acid; and
a surface crosslinking layer formed on the base polymer powder,
wherein the surface crosslinking layer is obtained by crosslinking the surface of the base polymer powder with a C 2 -C 8 diol-based or glycol-based compound, and the surface crosslinking is performed by spraying a surface treatment aqueous solution comprising the C 2 -C 8 diol-based or glycol-based compound on the base polymer powder with the spray angle of 10 to 30° and carrying out the surface crosslinking reaction at 120 to 250° C. for 10 to 120 minutes,
wherein the SAP has the SPAN value of 1.2 or less, represented by the following Mathematical Formula 1, and
satisfies the absorbing rate under load (ARUL) represented by the following Mathematical Formula 2:
SPAN=[ D (90%)− D (10%)]/ D (50%)≦1.2  [Mathematical Formula 1]

in Mathematical Formula 1,
D(90%) is the diameter of the particle when the accumulated weight from the smallest particle becomes 90%, when the SAP particles are arranged in order of particle diameter measured according to EDANA method WSP 220.2,
D(10%) is the diameter of the particle when the accumulated weight from the smallest particle becomes 10%, when the SAP particles are arranged in order of particle diameter measured according to EDANA method WSP 220.2, and
D(50%) is the diameter of the particle when the accumulated weight from the smallest particle becomes 50%, when the SAP particles are arranged in order of particle diameter measured according to EDANA method WSP 220.2,
1.0>ARUL=AUP(10 min)/AUP(60 min)>0.70  [Mathematical Formula 2]

in Mathematical Formula 2,
AUP (10min) is the absorbency under pressure after 10 mins represented by the following Mathematical Formula 3, and AUP (60 min) is the absorbency under pressure after 60 mins represented by the following Mathematical Formula 3,
AUP( g/g ) =[Wb ( g ) −Wa ( g )]/weight of absorbent polymer( g )  [Mathematical Formula 3]

in Mathematical Formula 3,
Wa (g) is the sum of the weight of the absorbent polymer and the weight of the device capable of providing load to the absorbent polymer, and
Wb (g) is the sum of the weight of the absorbent polymer in which moisture is absorbed under load (0.7 psi) for a given time of 10 mins or 60 mins and the weight of the device capable of providing load to the absorbent polymer.

2. The super absorbent polymer according to claim 1 , the base polymer powder comprises:
the powder having the diameter of 300 to 600 μm in an amount of 50 weight % or more.

3. The super absorbent polymer according to claim 2 , the base polymer powder comprises:
the powder having the diameter of 600 to 850 μm in an amount of 7 weight % or more; and
the powder having the diameter of 150 to 300 μm in an amount of 7 weight % or more.

4. A sanitary fitting including the super absorbent polymer of claim 1 .

5. A diaper including the super absorbent polymer of claim 1 .

6. A product including the super absorbent polymer of claim 1 , wherein the product is a water combination soil for horticulture, a water-stop material for civil engineering and construction, a nursery sheet, a freshness preservation in a food distribution field or a poultice material.

Assignees

• Lg Chemical Ltd

Inventors

• Won Tae-Young
• Han Chang-Sun
• Kim Gi-Cheul
• Lee Yong-Hun
• Lee Sang-Gi
• Kim Kyu-Pal
• Park Sung-Soo
• Leem Gyu

Classifications

• C08J2333/02

  Homopolymers or copolymers of acids; Metal or ammonium salts thereof · CPC title

• C08J3/245

  Differential crosslinking of one polymer with one crosslinking type, e.g. surface crosslinking · CPC title

• C08J3/12

  Powdering or granulating · CPC title

• A61L15/60

  Liquid-swellable gel-forming materials, e.g. super-absorbents · CPC title

• C08J3/24

  Crosslinking, e.g. vulcanising, of macromolecules (mechanical aspects B29C35/00; crosslinking agents C08K) · CPC title