Process for the production of carbon black from at least one FCC slurry cut, comprising a specific hydrotreatment

Patent metadata

Field	Value
Publication number	US-9512319-B2
Application number	US-201414554271-A
Country	US
Kind code	B2
Filing date	Nov 26, 2014
Priority date	Nov 27, 2013
Publication date	Dec 6, 2016
Grant date	Dec 6, 2016

Abstract

The present invention describes a process for the production of carbon black starting from a 360+ cut known as a slurry cut obtained from a FCC or RFCC unit, to which a vacuum residue type cut may be added, said process using a specific hydrotreatment unit.

First claim

The invention claimed is:

1. A process for the production of carbon black with a sulphur content of less than 0.3% starting from at least one feed which is a slurry cut obtained from a catalytic cracking unit (FCC or RFCC), the process involving the following steps:
a step (FILT) for filtering fine solid particles contained in the slurry cut, resulting in a clarified slurry cut, containing less than 300 ppm fine particles;
a step (RDS) for hydrotreatment of the clarified slurry cut, operating under the following conditions:
a) a pressure in the range 50 to 200 bars;
b) a temperature in the range 300° C. to 420° C.;
c) a HSV in the range 0.1 to 2.5 h −1 ;
the catalyst used being a succession of at least two distinct hydrotreatment catalysts, and said hydrotreatment step producing an effluent with a BMCI value of more than 110;
a step (DIST) for distillation of the effluent from the hydrotreatment step, resulting in a “light” portion used as a cut in a fuel pool, and a distillation residue with a sulphur content of less than 0.3%, and having a BMCI of more than 80, and with a density of more than 0.97 g·m −3 , said distillation residue being introduced into a carbon black unit (CBU),
a step (CBU) for producing carbon black in the unit, which results in a final product with a specifications in accordance with at least one of the ASTM standards N110, N220, N300, N330, N550, N683, N770, N880, N990.

2. The process for the production of carbon black according to claim 1 , in which the two catalysts used in the hydrotreatment unit (RDS) are, in succession (i.e. in the direction of flow of the feed to be treated):
a catalyst primarily ensuring hydrodemetallization (denoted HDM);
a catalyst primarily ensuring hydrodesulphurization (denoted HDS), the volumetric ratio of the HDM catalyst to the HDS catalyst being in the range 0.05 to 1.

3. The process for the production of carbon black according to claim 1 , in which a feed selected from the following is added to the clarified slurry cut upstream of the hydrotreatment unit (RDS):
a vacuum residue obtained from a vacuum distillation column,
an atmospheric residue obtained from an atmospheric distillation column,
a vacuum distillate obtained from the vacuum distillation column;
the feed thus produced after mixing having a BMCI of more than 130 before hydrotreatment.

4. The process for the production of carbon black according to claim 1 additionally comprising, a hydrotreated vacuum residue (RSV) feed added to the clarified slurry cut upstream of the hydrotreatment unit (RDS), the RSV feed is hydrotreated in an ebullated bed unit (HYC) under the following operating conditions:
a pressure in the range 50 to 250 bars;
a temperature in the range 300° C. to 550° C.;
an HSV in the range 0.1 to 10 h −1 ;
the catalysts being selected from catalysts comprising an alumina support and at least one metal from group VIII selected from nickel and cobalt, said element from group VIII being used in association with at least one metal from group VIB selected from molybdenum and tungsten.

5. The process for the production of carbon black according to claim 1 , in which a 360° C.+ fraction obtained from coal liquefaction is added to the clarified slurry cut upstream of the hydrotreatment unit (RDS).

6. The process for the production of carbon black according to claim 1 , in which a feed known as steam cracking tar is added to the clarified slurry cut upstream of the hydrotreatment unit (RDS).

Assignees

• Ifp Energies Now

Inventors

• Chatron-Michaud Pascal
• Majcher Jerome
• Morel Frederic

Classifications

• C09C1/48 Primary

  Carbon black · CPC title

• C01P2006/10

  Solid density · CPC title

• C09C1/54 Primary

  Acetylene black; thermal black {; Preparation thereof (separation or recovery C09C1/487)} · CPC title

• C01B31/02

  Chemistry & Metallurgy · mapped topic

• C10G65/12

  including cracking steps and other hydrotreatment steps · CPC title