Abstract

Production method for a multilayer lining for thermal and sound insulation with the steps of blending reinforcement fibers and polyamide matrix material, in the form of fibers, flakes or powder, and forming a web of said blend; layering said blended web and at least an additional layer chosen from an open cell foam layer, a heat reflective layer, or another of said blended web inside a mold; treating the stacked multilayer material with pressurized saturated steam, such that the polyamide matrix material in the blended web is melting at a temperature under steam pressure that is lower than the melting temperature of the polyamide matrix according to DSC, thereby binding the reinforcement fibers together thus consolidating the blended web forming a porous reinforcement layer, and all layers of the multilayer are laminated together.

First claim

The invention claimed is:

1. A production method for a multilayer lining for thermal and sound insulation, comprising the steps of:
blending reinforcement fibers with a polyamide matrix material, in the form of fibers, flakes or powder, to form a blended web;
layering the blended web inside a mould with at least one additional layer forming a stacked multilayer material, where each of the additional layers is an open cell foam layer, a heat reflective layer, or a further blended web;
treating with pressurized saturated steam the stacked multilayer material in the mould, the pressurized saturated steam having a temperature sufficient to melt the polyamide matrix material in each blended web, the melted polyamide matrix material consolidating the reinforcement fibers in each blended web into a porous reinforcement layer, while simultaneously laminating the layers of the stacked multilayer material into a multilayer lining.

2. The method of claim 1 , wherein the blended web contains reinforcement fibers in the range of between 40 to 80% by weight, with the balance being the polyamide matrix material.

3. The method of claim 1 , wherein the saturated steam has a pressure in the range of 9 to 20 atmospheres absolute.

4. The method of claim 1 , wherein, in the layering step, at least one scrim layer is included in the stacked multilayer material.

5. The method of claim 1 , wherein, when present, the heat reflective layer only partially covers a layer adjacent thereto.

6. The method of claim 1 , wherein the reinforcement fibers are selected from a group comprising mineral based fibers, man made fibers having a melting temperature higher than the melting temperature of the polyamide under steam pressure, and natural fibers.

7. The method of claim 1 , wherein the reinforcement fibers are a blend of mineral based fibers, and one selected from a group comprising man made fibers having a melting temperature higher than the melting temperature of the polyamide under steam pressure, and natural fibers.

8. The method of claim 1 , whereby the reinforcement fibers forming the reinforcement layer is a mixture of 20-40% by weight of polyamide reinforcing fibers, 20-50% by weight of glass fibers, and 20-50% by weight of polyester and/or natural fibers.

9. The method of claim 1 , wherein the polyamide matrix is polyamide-6 or polyamide-6,6 or co-polyamide or a mixture of different types of polyamide.

10. The method of claim 1 , wherein the open cell foam layer, when present, is a skinless foam.

11. The method of claim 10 , wherein the open cell foam layer is polyurethane (PUR) foam or polyester (PET) foam or a fiber filled foam.

12. The method of claim 1 , wherein, in the treating step, the mould conforms the multilayer lining into a three dimensional shape.

13. The method of claim 1 , wherein the treating step comprises the substeps of:
closing and clamping the mould with the stacked multilayer material layered therein:
applying the pressurized saturated steam into the closed and clamped mould, melting the polyamide matrix material;
releasing the steam pressure from the closed and clamped mould, resolidifying the polyamide matrix material; and
unclamping and opening the mould to release the multilayer liner as a stiff part.

14. The method of claim 1 , wherein the pressurized saturated steam has a saturation temperature that is between the temperature at which the polyamide matrix material melts in the presence of pressurized saturated steam and the temperature at which the polyamide matrix material melts according to Differential Scanning calorimetry.

Assignees

• Burgin Thomas
• Daniere Pierre
• Godano Philippe
• Konigbauer Stefan
• Krause Wenzel
• Autoneum Man Ag

Inventors

• Burgin Thomas
• Daniere Pierre
• Godano Philippe
• Konigbauer Stefan
• Krause Wenzel

Classifications

• B32B2260/021

  Fibrous or filamentary layer · CPC title

• B32B5/28

  impregnated with or embedded in a plastic substance {(not used)} · CPC title

• B32B2260/023

  Two or more layers · CPC title

• B29C70/026 Primary

  and with one or more layers of pure plastics material, e.g. foam layers (applying a non-preformed coating, e.g. a gel-coat B29C37/0025; with foam blocks B29C70/86) · CPC title

• B32B3/26

  characterised by a particular shape of the outline of the cross-section of a continuous layer; characterised by a layer with cavities or internal voids {(foam layer B32B5/18; layer of synthetic resin characterised by fillers that create voids or cavities B32B27/205); characterised by an apertured layer} · CPC title