Flame-retardant resin composition

Patent metadata

Field	Value
Publication number	US-9502156-B2
Application number	US-201013392241-A
Country	US
Kind code	B2
Filing date	Nov 24, 2010
Priority date	Nov 24, 2009
Publication date	Nov 22, 2016
Grant date	Nov 22, 2016

Abstract

The present invention relates to a flame-retardant resin composition including (A) a base resin containing (A1) a propylene polymer where 90% by mass or more of constituent monomers are propylene and (A2) at least one of specific thermoplastic elastomers, (B) a metal hydrate, (C) a phenol-based antioxidant, and (D) a metal soap, wherein the blending ratio (A1):(A2) of (A1) the propylene polymer to (A2) the specific thermoplastic elastomer in (A) the base resin is 9:1 to 7:3 in terms of mass ratio; (B) the metal hydrate, (C) the phenol-based antioxidant, and (D) the metal soap each is blended in a specific amount, and (D) the metal soap contains a specific metal salt of one or more specific fatty acids in a specific amount.

First claim

The invention claimed is:

1. A flame-retardant resin composition comprising:
a base resin containing a polypropylene homopolymer having a melt flow rate (MFR) at 230° C. of 0.5 g/10 minute and an olefin-based thermoplastic elastomer having a melt flow rate (MFR) at 230° C. of 9 g/10 minute,
a metal hydrate comprising magnesium hydroxide,
a phenol-based antioxidant, and
a metal soap,
wherein the blending ratio of the propylene homopolymer to the thermoplastic elastomer in the base resin is 7:3 in terms of a mass ratio,
into 100 parts by mass of the base resin are blended 75 to 100 parts by mass of the metal hydrate, 2 parts by mass of the phenol-based antioxidant, and 0.5 to 2 parts by mass of the metal soap, and
0.1 to 0.5 parts by mass of the metal soap based on 100 parts by mass of the base resin is magnesium behenate.

2. The flame-retardant resin composition according to claim wherein the metal hydrate is treated with a surface treating agent.

3. The flame-retardant resin composition according to claim 2 , wherein the surface treating agent comprises a long-chain fatty acid having 12 to 25 carbon atoms or an ester, an alkali metal salt or an alkaline earth metal salt thereof.

4. The flame-retardant resin composition according to claim 2 , wherein the surface treating agent comprises a chain alcohol having 6 to 30 carbon atoms.

5. The flame-retardant resin composition according to claim 1 , wherein the metal hydrate has an average particle diameter of 0.5 to 3 μm.

6. The flame-retardant resin composition according to claim 1 , wherein the metal soap comprises a combination of two different compounds.

7. The flame-retardant resin composition according to claim 6 , wherein the metal soap comprises magnesium behenate and calcium stearate.

8. The flame-retardant resin composition according to claim 1 , wherein the metal hydrate further comprises aluminum hydroxide.

9. The flame-retardant resin composition according to claim 1 , wherein the phenol-based antioxidant comprises tetrakis[methylene-3-(3,5-di-t-butyl-4-hydroxyphenyl)propionate]methane.

10. The flame-retardant resin composition according to claim 1 , wherein the magnesium behenate has a metal content of 2.9 to 3.7% by mass.

11. A non-halogen insulated electric wire for automobiles comprising:
a twisted wire composed of a plurality of conducting wires and
an insulating cover layer provided on an outer peripheral surface of the twisted wire and containing the flame-retardant resin composition according to claim 1 .

12. A wire harness for automobiles comprising:
an electric wire bundle containing a plurality of insulated electric wires and
an insulating protective material containing the flame-retardant resin composition according to claim 1 , which protects an outer periphery of the electric wire bundle.

13. A flame-retardant resin composition comprising:
a base resin containing a polypropylene homopolymer having a melt flow rate (MFR) at 230° C. of 0.5 g/10 minute, and an olefin-based thermoplastic elastomer having a melt flow rate (MFR) at 230° C. of 9 g/10 minute,
magnesium hydroxide,
a phenol-based antioxidant, and
magnesium behenate,
wherein the blending ratio of the propylene polymer to the thermoplastic elastomer in the base resin is 9:1 to 7:3 in terms of a mass ratio,
into 100 parts by mass of the base resin are blended 75 to 100 parts by mass of the metal hydrate, 0.5 to 2 parts by mass of the phenol-based antioxidant, and 0.1 to 0.5 parts by mass of magnesium behenate.

14. The flame-retardant resin composition according to claim 13 , wherein into 100 parts by mass of the base resin are blended 2 parts by mass of the phenol-based antioxidant,
and the blending ratio of the propylene polymer to the thermoplastic elastomer in the base resin is 7:3 in terms of a mass ratio.

Assignees

• Kambe Makoto
• Yazaki Corp

Inventors

• Kambe Makoto

Classifications

• C08L2666/04

  Macromolecular compounds according to groups C08L7/00 - C08L49/00, or C08L55/00 - C08L57/00; Derivatives thereof · CPC title

• H01B3/441

  from alkenes · CPC title

• C08L23/10 Primary

  Homopolymers or copolymers of propene · CPC title

• H01B3/28

  natural or synthetic rubbers · CPC title

• H01B7/295 Primary

  using material resistant to flame · CPC title