Acrylic adhesive tape and method of producing the same

Patent metadata

Field	Value
Publication number	US-9487679-B2
Application number	US-201113877348-A
Country	US
Kind code	B2
Filing date	Sep 27, 2011
Priority date	Oct 13, 2010
Publication date	Nov 8, 2016
Grant date	Nov 8, 2016

Abstract

An acrylic adhesive tape exhibiting good adhesion to a curved surface and good peel characteristics under a constant load even in the absence of a cross-linking agent includes an acrylic adhesive layer photo-polymerized by irradiation with ultraviolet rays. The acrylic adhesive layer contains: an acrylic polymer A formed by irradiating a solvent-free photo-polymerizable monomer composition containing an acrylic monomer and a photopolymerization initiator with ultraviolet rays so that the acrylic polymer A is formed by photopolymerization of the acrylic monomer and has a weight average molecular weight of 700,000 to 3,000,000 when a cross-linking agent is absent; an acrylic polymer B having a weight average molecular weight of 350,000 to 650,000; and an adhesion-imparting polymer having a weight average molecular weight of 2,000 to 10,000. The acrylic adhesive layer has a molecular weight distribution of 2.4 to 4.4.

First claim

The invention claimed is:

1. A method of producing an acrylic adhesive tape including a release film substrate and an acrylic adhesive layer formed thereon, the method comprising the following steps (a) to (d):
step (a) of irradiating a solvent-free photo-polymerizable monomer composition containing an acrylic monomer and a photopolymerization initiator with ultraviolet rays to produce an acrylic polymer A from the acrylic monomer by photopolymerization, the acrylic polymer A having a weight average molecular weight of 700,000 to 3,000,000 when a cross-linking agent is absent, to thereby prepare a polymer syrup containing the acrylic polymer A and an unreacted portion of the acrylic monomer;
after preparing the polymer syrup in step (a), step (b) of mixing an adhesion-imparting polymer having a weight average molecular weight of 2,000 to 10,000 with the polymer syrup to prepare an adhesive coating solution,
after preparing the adhesive coating solution in step (b), step (c) of applying the adhesive coating solution to the release film substrate to form an adhesive coating film; and
after forming the adhesive coating film in step (c), step (d) of irradiating the adhesive coating film with ultraviolet rays to produce an acrylic polymer B from the unreacted portion of the acrylic monomer in the adhesive coating film by photopolymerization, the acrylic polymer B having a weight average molecular weight of 350,000 to 650,000 when a cross-linking agent is absent, to thereby form an acrylic adhesive layer having a molecular weight distribution of 2.4 to 4.4.

2. The production method according to claim 1 , wherein the polymer syrup in the step (a) has a viscosity of 200 to 5,000 cps at 25° C.

3. The production method according to claim 1 , wherein the acrylic polymer A in the step (a) has a weight average molecular weight of 750,000 to 1,000,000.

4. The production method according to claim 1 , wherein 5 to 25% of the solvent-free photo-polymerizable monomer composition is polymerized in the step (a).

5. The production method according to claim 1 , wherein the solvent-free photo-polymerizable monomer composition includes, as the acrylic monomers, a (meth)acrylate which may be substituted with a hydroxy group, and (meth)acrylic acid.

6. The production method according to claim 1 , wherein the solvent-free photo-polymerizable monomer composition includes, as the acrylic monomers, 2-ethylhexyl acrylate, butyl acrylate, acrylic acid, and 2-hydroxyethyl acrylate.

7. The production method according to claim 1 , wherein the solvent-free photo-polymerizable monomer composition includes, as the acrylic monomers, 25 to 35 parts by mass of 2-ethylhexyl acrylate, 75 to 65 parts by mass of butyl acrylate, and 3 to 5 parts by mass of acrylic acid and 0.2 to 0.5 parts by mass of 2-hydroxyethyl acrylate based on 100 parts by mass of the total of 2-ethylhexyl acrylate and butyl acrylate.

8. The production method according to claim 1 , wherein the solvent-free photo-polymerizable monomer composition includes 0.005 to 0.1 parts by mass of the photopolymerization initiator based on 100 parts by mass of the acrylic monomers.

9. The production method according to claim 1 , wherein ultraviolet irradiation in the step (a) is performed under conditions such that the irradiation is performed 5 to 20 times at idling intervals of 20 to 40 seconds in an inert gas atmosphere, at a polymerization initiation temperature of 25 to 130° C., with light having a wavelength of 250 to 400 nm and an output power of 15 to 100 mW/cm 2 for 10 to 60 seconds.

10. The production method according to claim 1 , wherein the adhesion-imparting polymer used in the step (b) is an acrylic adhesion-imparting polymer.

11. The production method according to claim 10 , wherein the acrylic adhesion-imparting polymer is one produced by photopolymerization of a cycloalkyl (meth)acrylate, (meth)acrylic acid, a thiol, and a photopolymerization initiator.

12. The production method according to claim 10 , wherein the acrylic adhesion-imparting polymer is one produced by photopolymerization of cyclohexyl methacrylate, methacrylic acid, n-dodecyl mercaptan, and a photopolymerization initiator.

13. The production method according to claim 10 , wherein the acrylic adhesion-imparting polymer is one produced by photopolymerization of 95 to 97 parts by mass of cyclohexyl methacrylate, 3 to 5 parts by mass of methacrylic acid, 3 to 6 parts by mass of n-dodecyl mercaptan, and 0.25 to 0.5 parts by mass of the photopolymerization initiator.

14. The production method according to claim 1 , wherein the adhesion-imparting polymer used in the step (b) has a weight average molecular weight of 3,000 to 8,000.

15. The production method according to claim 1 , wherein the photopolymerization in preparing the adhesion-imparting polymer used in the step (b) is performed under conditions such that irradiation is performed 5 to 20 times at idling intervals of 20 to 40 seconds in an inert gas atmosphere, at a temperature of 25 to 130° C., with light having a wavelength of 250 to 400 nm and an output power of 15 to 100 mW/cm 2 for 10 to 60 seconds.

16. The production method according to claim 1 , wherein the acrylic polymer B in the step (d) has a weight average molecular weight of 450,000 to 650,000.

17. The production method according to claim 1 , wherein ultraviolet irradiation in the step (d) is performed under conditions such that the irradiation is performed in an inert gas atmosphere, at a temperature of 40 to 90° C., with light having a wavelength of 250 to 400 nm and an output power of 15 to 100 mW/cm 2 for 10 to 60 seconds.

18. The production method according to claim 1 , wherein a cross-linking agent is further added to the adhesive coating solution in the step (c).

Assignees

• Ogata Takanori
• Koike Azumi
• Dexerials Corp

Inventors

• Ogata Takanori
• Koike Azumi

Classifications

• C08K5/0025

  Crosslinking or vulcanising agents; including accelerators · CPC title

• C09J2433/00

  Presence of (meth)acrylic polymer · CPC title

• C08L33/04

  Homopolymers or copolymers of esters {(C08L43/04 takes precedence)} · CPC title

• C08J5/18

  Manufacture of films or sheets · CPC title

• C08L2312/06

  by radiation · CPC title