Finely divided, cationic or amphoteric, aqueous polymer dispersions, process for their preparation, their use, cationic or amphoteric protective colloids and their preparation

Patent metadata

Field	Value
Publication number	US-9481785-B2
Application number	US-201113988527-A
Country	US
Kind code	B2
Filing date	Nov 22, 2011
Priority date	Nov 25, 2010
Publication date	Nov 1, 2016
Grant date	Nov 1, 2016

Abstract

A finely divided, cationic or amphoteric, aqueous polymer dispersion which is obtainable by emulsion polymerization of ethylenically unsaturated monomers in the presence of a cationic or amphoteric protective colloid, wherein first the cationic or amphoteric protective colloid is prepared by polymerizing a monomer blend in the presence of at least one first polymerization initiator in an organic solvent, and is carried out in a pressurized reactor at a pressure of at least 1720 kPa and at a temperature of at least 150° C., which monomer blend comprises at least one ethylenically unsaturated monomer carrying an amine group, to provide a resin, then combining the resin, with an acid and water, to form the cationic or amphoteric protective colloid, thereafter carrying out an emulsion polymerization by introducing a monomer mixture into an aqueous medium containing said cationic or amphoteric protective colloid and at least one second polymerization initiator, wherein said monomer mixture comprises at least one ethylenically unsaturated water insoluble monomer. The composition is useful as a sizing agent for paper.

First claim

The invention claimed is:

1. A sizing agent comprising a finely divided, cationic or amphoteric, aqueous polymer dispersion obtained by emulsion polymerizing an ethylenically unsaturated monomer in the presence of a cationic or amphoteric protective colloid,
wherein first the cationic or amphoteric protective colloid is prepared by polymerizing a monomer blend in the presence of at least one first polymerization initiator in an organic solvent in a pressurized reactor at a pressure of at least 1720 kPa and at a temperature of between 170° C. and 220° C., and wherein the monomer blend comprises an ethylenically unsaturated monomer comprising an amine group, to obtain a resin, then
combining the resin with an acid and water to obtain the cationic or amphoteric protective colloid,
thereafter performing an emulsion polymerization by introducing a monomer mixture into an aqueous medium comprising the cationic or amphoteric protective colloid and a second polymerization initiator, wherein the monomer mixture comprises an ethylenically unsaturated water insoluble monomer.

2. The sizing agent of claim 1 , wherein the resin is obtained by polymerizing
(a) from 0.1 to 99.9% by weight of at least one ethylenically unsaturated aromatic monomer;
(b) from 0.1 to 99.9% by weight of at least one ethylenically unsaturated monomer comprising an amine group;
(c) from 0 to 5% by weight of at least one ethylenically unsaturated monomer comprising an acid group; and
(d) from 0 to 20% by weight of at least one non-ionic, ethylenically unsaturated monomer different from (a),
the sum of (a)+(b)+(c)+(d) being 100% by weight.

3. The sizing agent of claim 1 , wherein the resin is obtained by polymerizing
(a) from 40 to 90% by weight of at least one optionally substituted styrene;
(b) from 10 to 60% by weight of at least one ethylenically unsaturated monomer comprising an amine group;
(c) from 0 to 5% by weight of at least one ethylenically unsaturated monomer comprising an acid group; and
(d) from 0 to 20% by weight of at least one non-ionic, ethylenically unsaturated monomer different from (a),
the sum of (a)+(b)+(c)+(d) being 100% by weight.

4. The sizing agent of claim 1 , wherein the resin is obtained by polymerizing
(a) from 40 to 90% by weight of styrene;
(b) from 10 to 60% by weight of at least one compound selected from the group consisting of N,N-dimethylaminopropylmethacrylamide, N,N-dimethylaminoethyl methacrylate and N,N-dimethylaminoethyl acrylate;
(c) from 0 to 5% by weight of acrylic acid, methacrylic acid, or both; and
(d) from 0 to 5% by weight of stearyl acrylate.

5. The sizing agent of claim 1 , wherein in the emulsion polymerizing the monomer mixture comprises
(i) from 0 to 99.9% by weight of at least one ethylenically unsaturated aromatic monomer;
(ii) from 0.1 to 100% by weight of at least one ester of an ethylenically unsaturated carboxylic acid;
(iii) from 0 to 30% by weight of at least one vinyl ester of a linear or branched C 1 - to C 18 -carboxylic acid and
(iv) from 0 to 30% by weight of at least one non-ionic or anionic ethylenically unsaturated monomer differing from (i), (ii) and (iii),
the sum of (i)+(ii)+(iii)+(iv) being 100% by weight.

6. The sizing agent of claim 1 , wherein in the emulsion polymerizing the monomer mixture comprises
(i) from 0 to 50% by weight of at least one optionally substituted styrene;
(ii) from 50 to 100% by weight of at least one C 1 - to C 18 -(meth) acrylate;
(iii) from 0 to 30% by weight of at least one vinyl ester of a linear or branched C 1 - to C 18 -carboxylic acids and
(iv) from 0 to 30% by weight of at least one non-ionic or anionic ethylenically unsaturated monomer differing from (i), (ii) and (iii),
the sum of (i)+(ii)+(iii)+(iv) being 100% by weight.

7. The sizing agent of claim 1 , wherein in the emulsion polymerizing the monomer mixture comprises:
(i) from 0 to 50% by weight of styrene;
(ii) from 50 to 100% by weight of n-butyl acrylate, tert-butyl acrylate or a mixture of n-butyl acrylate and tert-butyl acrylate in a weight ratio in a range of 3:1 to 1:3,
(iv) from 0 to 30% by weight of 2-ethylhexyl acrylate, acrylic acid, or both,
the sum of (i)+(ii)+(iv) being 100% by weight.

8. The sizing agent of claim 1 , wherein the emulsion polymerizing is performed in the presence of from 0.1 to 5% by weight of at least one polymerization regulator.

9. The sizing agent of claim 1 , wherein the polymerization of the monomer blend to form the resin and the emulsion polymerization to form the finely divided, cationic or amphoteric, aqueous polymer dispersion are performed separately in different reaction vessels.

10. A process of preparing a sizing agent comprising a finely divided, cationic or amphoteric, aqueous polymer dispersion, the process comprising:
polymerizing a monomer blend in the presence of at least one first polymerization initiator in an organic solvent in a pressurized reactor at a pressure of at least 1720 kPa and at a temperature between 170° C. and 220° C., wherein the monomer blend comprises an ethylenically unsaturated monomer comprising an amine group, to obtain a resin; then
combining the resin with an acid and water to obtain a cationic or amphoteric protective colloid; thereafter,
performing an emulsion polymerization by introducing a monomer mixture into an aqueous medium comprising the cationic or amphoteric protective colloid and a second polymerization initiator, wherein the monomer mixture comprises an ethylenically unsaturated water insoluble monomer.

11. The sizing agent of claim 1 , wherein the finely divided aqueous polymer dispersion is cationic.

12. The sizing agent of claim 1 , wherein the finely divided aqueous polymer dispersion is amphoteric.

13. The sizing agent of claim 1 , wherein in the emulsion polymerizing the monomer mixture comprises (i) from 0 to 29% by weight of the optionally substituted styrene.

14. The sizing agent of claim 1 , wherein in the emulsion polymerizing the monomer mixture comprises (i) from 0 to 29% by weight of styrene.

15. The sizing agent of claim 1 , wherein, in the emulsion polymerizing, the monomer mixture comprises (ii) from 71 to 100% by weight of n-butyl acrylate, tert-butyl acrylate or a mixture of n-butyl acrylate and tert-butyl acrylate in a weight ratio in a range of 3:1 to 1:3.

16. The sizing agent of claim 1 , wherein the emulsion polymerizing is performed in the presence of from 0.1 to 5% by weight of at least one polymerization regulator.

17. The sizing agent of claim 1 , wherein the emulsion polymerizing is performed in the presence of from 0.1 to 5% by weight of at least one polymerization regulator.

Assignees

• Song Anja
• Kern Holger
• Williams-Harry Michele N
• Arnold Petra
• Milazzo Simone
• Basf Se

Inventors

• Song Anja
• Kern Holger
• Williams-Harry Michele N
• Arnold Petra
• Milazzo Simone

Classifications

• D21H17/34

  obtained by reactions only involving carbon-to-carbon unsaturated bonds · CPC title

• C08L33/14

  of esters containing halogen, nitrogen, sulfur, or oxygen atoms in addition to the carboxy oxygen · CPC title

• C08L33/08 Primary

  Homopolymers or copolymers of acrylic acid esters · CPC title

• C08F257/02

  on to polymers of styrene or alkyl-substituted styrenes · CPC title

• C09D4/06

  {Organic non-macromolecular compounds having at least one polymerisable carbon-to-carbon unsaturated bond} in combination with a macromolecular compound other than an unsaturated polymer of groups C09D159/00 - C09D187/00 · CPC title