Rhodium-iron catalysts

Patent metadata

Field	Value
Publication number	US-9475004-B2
Application number	US-201514732307-A
Country	US
Kind code	B2
Filing date	Jun 5, 2015
Priority date	Jun 6, 2014
Publication date	Oct 25, 2016
Grant date	Oct 25, 2016

Abstract

The present disclosure describes rhodium iron catalysts of use in catalyst systems. Disclosed here are TWCs configured to include a substrate and one or more of a washcoat layer, an impregnation layer, and/or an overcoat layer. Disclosed herein are one or more of a washcoat layer and/or an overcoat layer formed using a slurry that includes one or more of an oxygen storage material, a refractory support oxide, iron, and rhodium. Disclosed herein are methods of preparing catalysts wherein a washcoat layer is deposited onto the substrate, one or more impregnation layers may be deposited onto the washcoat layer, one or more overcoat layers may be deposited onto the impregnation washcoat layer, and one or more additional impregnation layers may be deposited onto the one or more washcoat layers.

First claim

What is claimed is:

1. A catalyst system, comprising:
a substrate;
a washcoat deposited on the substrate;
at least one impregnation layer; and
an overcoat;
wherein the washcoat comprises at least one of the group consisting of about 10 wt % to about 75 wt % cerium oxide, about 25 wt % to about 90 wt % zirconium-hafnium oxide, about 0 wt % to about 15 wt % lanthanum oxide, about 0 wt % to about 15 wt % neodymium oxide, about 0 wt % to about 15 wt % yttrium oxide, and about 0 wt % to about 15 wt % praseodymium oxide;
wherein the at least one impregnation layer comprises one or more of the group consisting of rhodium, iron nitrate, cerium, and combinations thereof; and
wherein the overcoat comprises at least one of the group consisting of an oxygen storage material, a refractory support oxide, iron, rhodium, and combinations thereof.

2. The catalyst system of claim 1 , wherein the washcoat further comprises at least one of the group consisting of a refractory support oxide, iron, rhodium, and combinations thereof.

3. The catalyst system of claim 1 , wherein the at least one impregnation layer is loaded with about 2.9 g/ft 3 to about 9.8 g/ft 3 of rhodium.

4. The catalyst system of claim 3 , wherein the at least one impregnation layer is loaded in the washcoat and wherein the washcoat further comprises a second impregnation layer of about 1 wt % to about 4 wt % iron.

5. The catalyst system of claim 3 , wherein the at least one impregnation layer is loaded with about 60 g/ft 3 to about 630 g/ft 3 of iron.

6. The catalyst system of claim 5 , wherein the at least one impregnation layer is loaded with about 150 g/ft 3 to about 630 g/ft 3 of iron.

7. The catalyst system of claim 3 , wherein the washcoat comprises at least one of the group consisting of a fluorite phase Cerium Zirconium-Hafnium Lanthanum (CZL) OSM, a Cerium Zirconium-Hafnium Neodymium (CZN) OSM, a Cerium Zirconium-Hafnium Yttrium (CZY) OSM, a Cerium Zirconium-Hafnium Lanthanum Praseodymium (CZLP) OSM, a Cerium Zirconium (CZ) OSM, and a Cerium Zirconium-Hafnium Neodymium Yttrium (CZNY) OSM.

8. The catalyst system of claim 7 , wherein said CZL OSM includes 30 wt % Cerium Oxide, 60 wt % Zirconium-Hafnium Oxide, and 10 wt % Lanthanum Oxide; said CZN OSM includes 30 wt % Cerium Oxide, 60 wt % Zirconium-Hafnium Oxide, and 10 wt % Neodymium Oxide; said CZY OSM includes 30 wt % Cerium Oxide, 60 wt % Zirconium-Hafnium Oxide, and 10 wt % Yttrium Oxide; said CZLP OSM includes 30 wt % Cerium Oxide, 60 wt % Zirconium-Hafnium Oxide, 5 wt % Lanthanum Oxide, and 5 wt % Praseodymium Oxide; said CZ OSM includes 75 wt % Cerium Oxide and 30% Zirconium-Hafnium Oxide; and said CZNY OSM includes 31 wt % Cerium, 58.3 wt % Zirconium-Hafnium, 5.5 wt % Neodymium, and 5.2 wt % Yttrium Oxide.

9. The catalyst system of claim 3 , wherein the washcoat comprises at least one of the group consisting of a CZL, a CZN, a CZY, a CZLP, and a CZNY.

10. The catalyst system of claim 9 , wherein said CZL OSM includes 30 wt % Cerium Oxide, 60 wt % Zirconium-Hafnium Oxide, and 10 wt % Lanthanum Oxide; said CZN OSM includes 30 wt % Cerium Oxide, wt % Zirconium-Hafnium Oxide, and 10 wt % Neodymium Oxide; said CZY OSM includes 30 wt % Cerium Oxide, 60 wt % Zirconium-Hafnium Oxide, and 10 wt % Yttrium Oxide; said CZLP OSM includes 30 wt % Cerium Oxide, 60 wt % Zirconium-Hafnium Oxide, 5 wt % Lanthanum Oxide, and 5 wt % Praseodymium Oxide; and said CZNY OSM includes 31 wt % Cerium, 58.3 wt % Zirconium-Hafnium, 5.5 wt % Neodymium, and 5.2 wt % Yttrium Oxide.

11. The catalyst system of claim 3 , wherein the at least one impregnation layer is further loaded with about 150 g/ft 3 to about 630 g/ft 3 of iron; about 499 g/ft 3 to about 1497 g/ft 3 Cerium; and 0 g/ft 3 to about 317 g/ft 3 yttrium.

12. The catalyst system of claim 3 , wherein the at least one impregnation layer is further loaded with about 150 g/ft 3 to about 630 g/ft 3 of iron; 0 g/ft 3 to about 1497 g/ft 3 Cerium; and about 31.7 g/ft 3 to about 317 g/ft 3 yttrium.

13. The catalyst system of claim 3 , wherein the washcoat comprises about 7.36 wt % iron.

14. The catalyst system of claim 1 , wherein the at least one impregnation layer is loaded with about 60 g/ft 3 to about 630 g/ft 3 of iron.

15. The catalyst system of claim 1 , wherein the at least one impregnation layer is loaded with about 499 g/ft 3 to about 1497 g/ft 3 of cerium.

16. The catalyst system of claim 1 , wherein the washcoat comprises iron, rhodium, and CZNY OSM.

17. The catalyst system of claim 16 , wherein the washcoat comprises 7.36 wt % iron, rhodium, and CZNY OSM, and wherein the CZNY OSM comprises 31 wt % Cerium, 58.3 wt % Zirconium-Hafnium, 5.5 wt % Neodymium, and 5.2 wt % Yttrium Oxide.

18. The catalyst system of claim 1 , wherein the washcoat comprises about 4 wt % to about 20 wt % iron.

19. The catalyst system of claim 1 , wherein rhodium is loaded in the washcoat at about 0.1 g/ft 3 to about 20 g/ft 3 .

20. The catalyst system of claim 19 , wherein rhodium is loaded in the washcoat at about 4.8 g/ft 3 .

Assignees

• Clean Diesel Tech Inc

Inventors

• Hatfield Randal L
• Golden Stephen J
• Ngo Johnny T

Classifications

• B01J23/10 Primary

  of rare earths · CPC title

• B01J35/56

  Foraminous structures having flow-through passages or channels, e.g. grids or three-dimensional [3D] monoliths · CPC title

• B01D2255/2061

  Yttrium · CPC title

• B01J21/04

  Alumina · CPC title

• Y02T10/22

  Cross-Sectional Technologies · mapped topic