Method for synthesizing polymers from acrylic acid, one of the salts of same or the mixture thereof

Patent metadata

Field	Value
Publication number	US-9458273-B2
Application number	US-201314390076-A
Country	US
Kind code	B2
Filing date	Apr 3, 2013
Priority date	Apr 4, 2012
Publication date	Oct 4, 2016
Grant date	Oct 4, 2016

Abstract

The present invention concerns a method for preparing a polymer comprising a step of radical polymerization of monomers comprising at least monomers (M1) chosen from acrylic acid, one of the salts of same, or the mixture thereof, in which said radical polymerization step is carried out:
continuously; at a pH which remains between 3 and 5 during the polymerization step; in the presence of a metabisulfite/persulfate redox pair, for example the sodium metabisulfite/sodium persulfate pair, as a radical initiator, with a metabisulfite/persulfate molar ratio of between 1 and 3.5 and an initiator/monomer molar percentage of between 5% and 18%.

First claim

The invention claimed is:

1. A process for preparing a polymer comprising a step of radical polymerization of monomers comprising at least monomers (M1) selected from a group consisting of acrylic acid, a salt thereof, and a mixture thereof, wherein said radical polymerization step is carried out:
continuously;
at a pH which remains included from 3 to 5 during the polymerization step;
in the presence of a metabisulfite/persulfate redox couple, as a radical initiator, with a metabisulfite/persulfate molar ratio included from 1 to 3.5 and an initiator/monomer molar percentage included from 5% to 18%.

2. The process as claimed in claim 1 , wherein the pH is included from 3.5 to 5.

3. The process as claimed in claim 1 , wherein the sodium metabisulfite/sodium persulfate molar ratio is included from 1 to 2.5.

4. The process as claimed in claim 1 , wherein the molar percentage is included from 3% to 10%.

5. The process as claimed in claim 1 , wherein the polymerization step is carried out at a temperature which remains included from 30° C. to 100° C. throughout the polymerization.

6. The process as claimed in claim 1 , wherein the polymerization is carried out in a tubular reactor, a plate reactor or a microreactor which is appropriate.

7. The process as claimed in claim 6 , wherein the tubular reactor comprises at least one static mixer.

8. The process as claimed in claim 1 , wherein the polymerization step is carried out with a residence time of less than 5 minutes.

9. The process as claimed in claim 1 , wherein the polymer obtained has a weight-average molar mass included from 1000 g/mol to 10 000 g/mol.

10. The process as claimed in claim 1 , wherein the polymer obtained is subjected to an additional post-treatment step in the presence of additives, of biocides or of bases.

11. The process as claimed in claim 1 , wherein the radical polymerization reaction is carried out in the presence of at least one monomer (M2), said monomer (M2) being different than the monomer (M1).

12. The process as claimed in claim 11 , wherein the monomer (M2) is a monomer which has one or more functions or groups selected from the group consisting of: carboxylic acid; sulfonate; sulfate; phosphonate; phosphate; hydroxyl; primary, secondary, tertiary or quaternary amine; lactam; amide; ethylene glycol or polyalkylene oxide; carboxybetaine, sulfobetaine and phosphobetaines.

13. The process as claimed in claim 1 , wherein said metabisulfite/persulfate redox couple is the sodium metabisulfite/sodium persulfate couple.

14. The process as claimed in claim 1 , wherein the pH is included from 4.0 to 5.

15. The process as claimed in claim 1 , wherein the pH is included from 4.4 to 4.9.

16. The process as claimed in claim 1 , wherein the sodium metabisulfite/sodium persulfate molar ratio is less than or equal to 2.

17. The process as claimed in claim 1 , wherein the molar percentage is included from 6% to 8.5%.

18. The process as claimed in claim 1 , wherein the polymerization step is carried out with a residence time of less than 2 minutes.

19. The process as claimed in claim 1 , wherein the polymer obtained has a weight-average molar mass included from 1500 g/mol to 7500 g/mol.

20. The process as claimed in claim 1 , wherein the polymer obtained has a weight-average molar mass included from 2000 g/mol to 6000 g/mol.

Assignees

• Rhodia Operations

Inventors

• Ferlin Patrick
• Wilson James
• Benachich Fadila

Classifications

• C08F120/06 Primary

  Acrylic acid; Methacrylic acid; Metal salts or ammonium salts thereof · CPC title

• C08F220/06 Primary

  Acrylic acid; Methacrylic acid; Metal salts or ammonium salts thereof · CPC title

• C08F4/40

  Redox systems · CPC title