Torsional extreme-plastic processing method of conic metal pipe

Patent metadata

Field	Value
Publication number	US-9447487-B2
Application number	US-201214365837-A
Country	US
Kind code	B2
Filing date	Nov 30, 2012
Priority date	Dec 16, 2011
Publication date	Sep 20, 2016
Grant date	Sep 20, 2016

Abstract

The present invention relates to a torsional extreme-plastic processing method. In other words, a processing method in which severe plastic deformation based on torsion and compressive force is applied to a material by using a mold to produce miniaturize and nano-size crystal particles in a conic pipe. According to the severe plastic deformation method of the present invention, a punch that matches an inner shape of the conic metal pipe is mounted inside the conic metal pipe, and then a mold that matches an outer shape of the conic metal pipe is mounted outside the conic metal pipe. Thus, microstructures of the conic metal pipe may be ultra-finely crystallized or nano-crystallized through shearing by applying compression and torsion to the conic metal pipe.

First claim

The invention claimed is:

1. A method of performing a torsional plastic forming process to a conic metal pipe, comprising:
mounting a punch having a configuration corresponding to an interior configuration of the conic metal pipe in the conic metal pipe;
mounting a metal die having a configuration corresponding to an exterior configuration of the conic metal pipe on the conic metal pipe; and
concurrently applying compressive and twisting forces to the conic metal pipe through the punch and the metal die to cause shear deformation of the conic metal pipe, thus enabling a fine microstructure of the conic metal pipe to have ultrafine crystal grains or nanocrystalline grains,
wherein a radius of curvature of a tip of the punch is larger than a tip of the conic metal pipe.

2. The method according to claim 1 , wherein the shear deformation is obtained by pressing the punch against the metal die and rotating the punch.

3. The method according to claim 2 , wherein an amount of the shear deformation is controlled by adjustment of a compressive force and a number of revolutions of the punch.

4. The method according to claim 3 , wherein a higher compressive force is applied to a central area of the conic metal pipe so as to cause the fine microstructure of the central area to have ultrafine crystal grains or nanocrystalline grains.

5. The method according to claim 3 , wherein a shape of the conic metal pipe before the torsional plastic forming process is equal to a shape of a conic metal pipe after the torsional plastic forming process, other than the of thickness.

6. The method according to claim 3 , wherein the metal die includes a heating element to control a process temperature.

7. The method according to claim 3 , wherein the punch includes a heating element to control a process temperature.

8. The method according to claim 2 , wherein a higher compressive force is applied to a central area of the conic metal pipe so as to cause the fine microstructure of the central area to have ultrafine crystal grains or nanocrystalline grains.

9. The method according to claim 2 , wherein a shape of the conic metal pipe before the torsional plastic forming process is equal to a shape of a conic metal pipe after the torsional plastic forming process, other than the of thickness.

10. The method according to claim 2 , wherein the metal die includes a heating element to control a process temperature.

11. The method according to claim 2 , wherein the punch includes a heating element to control a process temperature.

12. The method according to claim 1 , wherein a higher compressive force is applied to a central area of the conic metal pipe so as to cause the fine microstructure of the central area to have ultrafine crystal grains or nanocrystalline grains.

13. The method according to claim 1 , wherein a shape of the conic meal pipe before the torsional plastic forming process is equal to a shape of a conic metal pipe after the torsional plastic forming process, other than the of thickness.

14. The method according to claim 1 , wherein the metal die includes a heating element to control a process temperature.

15. The method according to claim 1 , wherein the punch includes a heating element to control a process temperature.

16. The method according to claim 1 , wherein the metal die is rotatable alone or together with the punch.

17. The method according to claim 1 , wherein,
a curvature of the tip of the metal die is equal to a curvature of the tip of the punch, and
a vertex portion of the conic metal pipe is closed.

Assignees

• Postech Academy-Industry Found

Inventors

• Kim Hyoung-Seop
• Um Ho-Yong
• Yoon Eun-Yoo
• Lee Dong-Jun
• Lee Seong

Classifications

• B21K21/02

  Producing blanks in the shape of discs or cups as semifinished articles for making hollow articles, e.g. to be deep-drawn or extruded · CPC title

• B21C23/01

  starting from material of particular form or shape, e.g. mechanically pre-treated (B21C23/22 takes precedence) · CPC title

• B21D35/002

  Processes combined with methods covered by groups B21D1/00 - B21D31/00 · CPC title

• B21J5/063

  Friction heat forging (friction heat riveting B21J15/027) · CPC title

• C21D9/10

  shotgun barrels · CPC title