Modified conjugated diene rubber, method for producing same, and rubber composition

Patent metadata

Field	Value
Publication number	US-9434792-B2
Application number	US-201214114123-A
Country	US
Kind code	B2
Filing date	Apr 17, 2012
Priority date	Apr 26, 2011
Publication date	Sep 6, 2016
Grant date	Sep 6, 2016

Abstract

A method containing a step of reacting a conjugated diene polymer having an alkali metal or alkaline earth metal active end with a hydrocarbyloxysilane compound having one or more of each of the following functional groups I and II in its molecule to obtain a modified conjugated diene polymer containing a functional group II, and a step of mixing the modified conjugated diene polymer and a compound such as organic acid. A modified conjugated diene rubber which can be used as a raw material of a cross-linked rubber which can be used in tire treads and the like and can enhance low fuel consumption performance is provided. The functional group I is a hydrocarbyloxysilyl group. The functional group II is a nitrogen-containing group in which both of two hydrogen atoms of a primary amino group are substituted with protective groups.

First claim

The invention claimed is:

1. A method comprising:
reacting a conjugated diene polymer with a hydrocarbyloxysilane compound having one or more functional groups (I) and one or more a functional groups (II) in a molecule thereof to obtain a modified conjugated diene polymer containing the functional group (II), wherein the conjugate diene polymer comprises a structural unit derived from a conjugated diene compound and optionally a structural unit derived from an aromatic vinyl compound, and further comprises an alkali metal or alkaline-earth metal active end, the functional group (I) is a hydrocarbyloxysilyl group, and the functional group (II) is a nitrogen-containing group in which both of two hydrogen atoms of a primary amino group are substituted with a protective group; and
mixing the modified conjugated diene polymer and at least one compound selected from the group consisting of an organic acid, an organic acid halide, and a carboxylic anhydride to obtain a modified conjugated diene rubber.

2. The method according to claim 1 , wherein the at least one compound is selected from the group consisting of a carboxylic acid, a carboxylic anhydride, a carboxylic halide, an organic phosphoric acid, an organic phosphoric acid halide, an organic phosphorous acid, an organic phosphorous acid halide, an organic sulfonic acid, an organic sulfonic acid halide, an organic sulfinic acid, an organic sulfonic acid halide, and an organic thio acid.

3. The method according to claim 1 , further comprising:
bringing the modified conjugated diene rubber into contact with water.

4. The method according to claim 1 ,
wherein the modified conjugated diene rubber has an onium structure formed by the modified conjugated diene polymer.

5. A modified conjugated diene rubber obtained by the method according to claim 1 .

6. A rubber composition, comprising:
the modified conjugated diene rubber according to claim 5 ,
silica and/or carbon black, and
a cross-linking agent.

7. A cross-linked rubber obtained by a process comprising cross-linking the rubber composition according to claim 6 .

8. A tire, comprising the cross-linked rubber according to claim 7 .

9. The method according to claim 1 , further comprising:
performing an anionic polymerization of the conjugated diene compound and optionally the aromatic vinyl compound in a presence of an alkali metal- or alkaline-earth metal-based polymerization initiator to obtain the conjugate diene polymer.

10. The method according to claim 1 , wherein the alkali metal or alkaline-earth metal active end comprises lithium.

11. The method according to claim 1 , wherein the conjugated diene compound is 1,3-butadiene.

12. The method according to claim 1 , wherein the aromatic vinyl compound is styrene.

13. The method according to claim 1 , wherein an amount of the at least one compound mixed with the modified conjugated diene polymer is 1.0 molar equivalent or more based on alkali components present in a reaction system.

14. The method according to claim 1 , wherein an amount of the at least one compound mixed with the modified conjugated diene polymer is 1.5 molar equivalent or more based on alkali components present in a reaction system.

15. The method according to claim 1 , wherein a temperature of mixing the modified conjugated diene polymer and the at least one compound is from 0 to 120° C.

16. The method according to claim 1 , wherein a temperature of mixing the modified conjugated diene polymer and the at least one compound is from 20 to 100° C.

Assignees

• Morita Hiroyuki
• Shibata Masahiro
• Tanaka Ryoji
• Jsr Corp

Inventors

• Morita Hiroyuki
• Shibata Masahiro
• Tanaka Ryoji

Classifications

• C08C19/25 Primary

  Incorporating silicon atoms into the molecule · CPC title

• C08K3/36

  Silica · CPC title

• B60C1/0016

  Compositions of the tread · CPC title

• C08K3/04

  Carbon · CPC title

• C08C19/44

  of polymers containing metal atoms exclusively at one or both ends of the skeleton · CPC title