Coated paper having a coating structure with controlled distribution of latex and method for preparing the same

Patent metadata

Field	Value
Publication number	US-9433972-B2
Application number	US-201414581557-A
Country	US
Kind code	B2
Filing date	Dec 23, 2014
Priority date	Jan 7, 2011
Publication date	Sep 6, 2016
Grant date	Sep 6, 2016

Abstract

Disclosed is coated paper having a coating structure in which styrene-butadiene latex distribution of a paper coating layer is controlled in order to reduce fold cracking of the coated paper and a method for manufacturing the same. The coated paper in which different types of latexes are separately applied to two coating layers exhibits considerably improved stiffness and reduced fold crack, as compared to the existing coated paper.

First claim

The invention claimed is:

1. A method for preparing coated paper comprising:
preparing a first coating solution comprising a latex having a particle size of 70 to 120 nm and a glass transition temperature of 10 to 30° C. and a second coating solution comprising a latex having a particle size of 120 to 200 nm and a glass transition temperature of −30 to 0° C.;
coating a base paper with the first coating solution, followed by drying, to form a first coating layer as a pre-coating layer; and
coating the first coating layer with the second coating solution, followed by drying, to form a second coating layer as a top coating layer,
wherein a total thickness of the coating layers of the first coating layer and the second coating layer is within the range of 20 to 60 μm.

2. The method according to claim 1 , wherein the first coating solution or the second coating solution is prepared by mixing 5 to 20 parts by weight of a styrene-butadiene latex and 0.1 to 9 parts by weight of a thickener, with respect to 100 parts by weight of the pigment and the auxiliary pigment, to have a solid content of 60 to 75% and pH of 8 to 11.

3. The method according to claim 1 , wherein the base paper is a base paper for art paper, a base paper for art board paper, or a base paper for cardboard, each having a basis weight of 70 to 350 g/M 2 .

4. The method according to claim 1 , wherein the coating layer is formed using a super calendar or a soft-nip calendar.

Assignees

• Lg Chemical Ltd

Inventors

• Yeu Seung-Uk
• Han Chang-Sun
• Lee Young-Min
• Kim Byoung-Yun

Classifications

• Y10T428/2495

  Thickness [relative or absolute] · CPC title

• B05D2203/00

  Other substrates · CPC title

• H04N21/2665

  Gathering content from different sources, e.g. Internet and satellite · CPC title

• D21H23/56

  Rolls (D21H23/38 takes precedence) · CPC title

• H04N21/4622

  Retrieving content or additional data from different sources, e.g. from a broadcast channel and the Internet (web site content organization and management for information retrieval from the Internet G06F16/958; transmission by internet of broadcast information H04H60/82; stock exchange data over packet-switching network H04L12/1804; push services including data channel over packet-switching network H04L12/1859) · CPC title