Composition of polyamides with low concentration of carboxamide groups and electrically conductive carbon

Patent metadata

Field	Value
Publication number	US-9418773-B2
Application number	US-201113882689-A
Country	US
Kind code	B2
Filing date	Oct 31, 2011
Priority date	Nov 5, 2010
Publication date	Aug 16, 2016
Grant date	Aug 16, 2016

Abstract

A polyamide composition comprising the following components: a) at least 40 parts by weight of a polyamide whose monomer units contain an arithmetic average of at least 7.5 carbon atoms, b) 0.1 to 15 parts by weight of at least one salt with a non-metallic cation, c) 0.1 to 25 parts by weight of at least one dispersant based on esters or amides and d) an electrically conductive carbon selected from the group of carbon black, graphite powder, carbon fibers, carbon nanotubes and/or graphene, in an amount which results in a specific surface resistance of the polymer composition to IEC 60167 of 10 −1 to 10 10 Ω, e) 0 to 5 parts by weight of at least one metal salt, and optionally f) customary assistants and additives, where the polyamide of component a) is not a PA12 if carbon nanotubes are present as component d), and where the sum of the parts by weight of components a) to f) is 100, can be used for production of mouldings with improved electrical conductivity and improved surface quality.

First claim

The invention claimed is:

1. A polyamide composition, comprising:
a) at least 40 parts by weight of a polyamide whose monomer units have an arithmetic average of 7.5 carbon atoms or more;
b) from 0.1 to 15 parts by weight of at least one salt having a nonmetallic cation;
c) from 0.1 to 25 parts by weight of at least one dispersant based on an ester or an amide;
d) an electrically conductive carbon selected from the group consisting of carbon black, a graphite powder, a carbon fiber, a carbon nanotube and graphene, in an amount such that the polyamide composition has a specific surface resistance in accordance with IEC 60167 of from 10 −1 to 10 10 Ω;
e) from 0 to 5 parts by weight of at least one metal salt; and
f) optionally one or more auxiliaries or additives,
based on a total of 100 parts by weight of a) to f),
wherein the polyamide of a) is not PA12 when the electrically conductive carbon of d) comprises a carbon nanotube, and
the nonmetallic cation of b) consists of a quaternary nitrogen compound.

2. The polyamide composition of claim 1 , comprising
from 0.1 to 10 parts by weight of b),
from 1 to 10 parts by weight of c),
from 1 to 10 parts by weight of a carbon nanotube as d), and
from 0 to 5 parts by weight of e).

3. The polyamide composition of claim 2 , having a specific volume resistance in accordance with ICE 60093 of not more than 10 9 Ωm.

4. The polyamide composition of claim 2 , wherein the nonmetallic cation of b) is acyclic quaternary ammonium.

5. The polyamide composition of claim 1 , having a specific volume resistance in accordance with ICE 60093 of not more than 10 9 Ωm.

6. The polyamide composition of claim 1 , wherein the dispersant of c) is c1) or c2):
c1) a polyacrylic ester, obtained by esterification of an alkyl polyacrylate which is optionally obtained by polymerization and whose alkyl radicals have from 1 to 3 carbon atoms, with at least one alcohol selected from the group consisting of a) and b):
a) a saturated aliphatic alcohol having from 4 to 50 carbon atoms, and
b) an unsaturated aliphatic alcohol having from 4 to 50 carbon atoms,
where a) and b) are included in an amount such that from 30 to 100% of ester groups are transesterified,
and
c2) a polyester-polyamine condensation product obtained by partial or complete reaction of
A) one or more amino-functional polymers comprising at least four amino groups, with
B) one or more polyesters of formula (I) or (Ia)
T-C(O)—[O-A-C(O)] x —OH  (I)

T-O—[C(O)-A-O-] y Z  (Ia)

and
C) one or more polyethers of formula (II) or (IIa)
T-C(O)—B—Z  (II)

T-O—B—Z  (IIa)

where
T is independently at each occurrence a hydrogen radical or an optionally substituted, linear or branched aryl, arylalkyl, alkyl or alkenyl radical having from 1 to 24 carbon atoms,
A is independently at each occurrence at least one divalent radical selected from the group consisting of a linear, branched, cyclic and aromatic hydrocarbon,
Z is independently at each occurrence at least one radical selected from the group consisting of a sulphonic acid, a sulphuric acid, a phosphonic acid, a phosphoric acid, a carboxylic acid, an isocyanate, and an epoxide,
B is independently at each occurrence a radical of formula (III)
—(C l H 2l O) a —(C m H 2m O) b —(C n H 2n O) c —(SO) d —  (III),

where
SO is —CH 2 —CH(Ph)-O— where Ph is a phenyl radical,
a, b, and c are each, independently of one another, from 0 to 100, with the proviso that a+b+c≧0, and a+b+c+d>0,
d≧0,
l, m, and n are each, independently of one another, 2 or greater, and
x and y are each, independently of one another, 2 or greater.

7. The polyamide composition of claim 6 , wherein the dispersant of c) is c1).

8. The polyamide composition of claim 6 , wherein the dispersant of c) is c2).

9. The polyamide composition of claim 6 , wherein a, b and c are each independently from 5 to 35.

10. The polyamide composition of claim 6 , wherein a, b and c are each independently from 10 to 20.

11. The polyamide composition of claim 6 , wherein d is from 1 to 5.

12. The polyamide composition of claim 6 , wherein l, m and n are each independently from 2 to 4.

13. The polyamide composition of claim 6 , having a specific volume resistance in accordance with ICE 60093 of not more than 10 9 Ωm.

14. The polyamide composition of claim 1 , wherein the metal salt of e) is an alkali metal salt, an alkaline earth metal salt or a zinc salt.

15. The polyamide composition of claim 14 , having a specific volume resistance in accordance with ICE 60093 of not more than 10 9 Ωm.

16. A moulding, comprising:
the polyamide composition of claim 1 .

17. The polyamide composition of claim 1 , wherein the nonmetallic cation of b) is acyclic quaternary ammonium.

18. The polyamide composition of claim 1 , wherein the nonmetallic cation of b) has formula (1) or (2):
R 1 R 2 R 3 R 4 N +   (1)

R 1 R 2 N + ═CR 3 R 4   (2)

where
R 1 , R 2 , R 3 , and R 4 are independently selected from the group consisting of hydrogen, a linear or branched or double bond-containing aliphatic hydrocarbon radical having from 1 to 30 carbon atoms or a saturated or unsaturated cycloaliphatic hydrocarbon radical having from 5 to 40 carbon atoms, an aromatic hydrocarbon radical having from 6 to 40 carbon atoms, an alkylaryl radical having from 7 to 40 carbon atoms, a linear or branched and optionally unsaturated aliphatic hydrocarbon radical which has from 2 to 30 carbon atoms and is interrupted by a radical containing one or more heteroatoms, a linear or branched or double bond-containing aliphatic hydrocarbon radical which has from 2 to 30 carbon atoms and is interrupted by one or more functions selected from the group consisting of —O—C(O)—, —(O)C—O—, —NH—C(O)—, —(O)C—NH, —(CH 3 )N—C(O)—, —(O)C—N(CH 3 )—, —S(O 2 )—O—, —O—S(O 2 )—, —S(O 2 )—NH—, —NH—S(O 2 )—, —S(O 2 )—N(CH 3 )—, —N(CH 3 )—S(O 2 )—, and a linear or branched or double bond-containing aliphatic or cycloaliphatic hydrocarbon radical which has from 1 to 30 carbon atoms and is terminally functionalized by —OH, —OR′, —NH 2 , —N(H)R′, —N(R′) 2 or a polyether —(R 5 —O) n —R 6 having or random structure,
where
R′ is a saturated or unsaturated C 1 -C 30 -alkyl radical,
R 5 is a linear or branched hydrocarbon radical comprising from 2 to 4 carbon atoms,
n is from 1 to 100, and
R 6 is hydrogen, a linear or branched or double bond-containing aliphatic hydrocarbon radical having from 1 to 30 carbon atoms, or a saturated or double bond-containing cycloaliphatic hydrocarbon radical having from 5 to 40 carbon atoms, an aromatic hydrocarbon radical having from 6 to 40 carbon atoms or an alkylaryl radical having from 7 to 40 carbon atoms or a radical —C(O)—R 7 ,
where
R 7 is a linear or branched or double bond-containing aliphatic hydrocarbon radical having from 1 to 30 carbon atoms, a double bond-containing cycloaliphatic hydrocarbon radical having from 5 to 40 carbon atoms, an aromatic hydrocarbon radical having from 6 to 40 carbon atoms, or an alkylaryl radical having from 7 to 40 carbon atoms.

19. The polyamide composition of claim 8 , having a specific volume resistance in accordance with ICE 60093 of not more than 10 9 Ωm.

Assignees

• Hermasch Sylvia Anita
• Wursche Roland
• Häger Harald
• Lehmann Kathrin
• Evonik Degussa Gmbh

Inventors

• Hermasch Sylvia Anita
• Wursche Roland
• Häger Harald
• Lehmann Kathrin

Classifications

• C08K5/10

  Esters; Ether-esters · CPC title

• C08L71/02

  Polyalkylene oxides · CPC title

• C09D5/24

  Electrically-conducting paints {(conductive materials H01B1/00)} · CPC title

• H01B1/24 Primary

  the conductive material comprising carbon-silicon compounds, carbon or silicon · CPC title

• C08L33/08

  Homopolymers or copolymers of acrylic acid esters · CPC title