Method for manufacturing glass blank for magnetic disk, method for manufacturing glass substrate for magnetic disk, glass blank for magnetic disk

Patent metadata

Field	Value
Publication number	US-9409809-B2
Application number	US-201213982838-A
Country	US
Kind code	B2
Filing date	Apr 27, 2012
Priority date	Apr 27, 2011
Publication date	Aug 9, 2016
Grant date	Aug 9, 2016

Abstract

A method for manufacturing a glass blank for magnetic disk and a method for manufacturing a glass substrate for magnetic disk are provided which are capable of producing a glass blank for magnetic disk having a good surface waviness by press forming. The method includes a forming process of press-forming a lump of molten glass using a pair of dies, wherein in the forming process, press forming is performed using thermally equalizing means for reducing a difference in temperature in the press forming surface of the die during pressing of the molten glass.

First claim

What is claimed is:

1. A method for manufacturing a glass blank for magnetic disk, the method including a forming process of press-forming a lump of molten glass using a pair of dies, the method comprising:
press-forming a lump of molten glass while falling from a direction orthogonal to the falling direction using a pair of dies;
obtaining a correlation between a difference in temperature of a pair of dies in the press-forming the molten glass and flatness of the glass blank obtained after press forming, the difference being measured at positions of the pair of dies facing each other;
determining a difference in temperature of the pair of dies based on the correlation, the difference corresponding to a target flatness of the glass blank; and
performing the forming process so that a difference in temperature of the pair of dies is within the determined difference in temperature.

2. The method for manufacturing a glass blank for magnetic disk according to claim 1 , wherein the target flatness is equal to flatness of a magnetic disk, the flatness of the magnetic disk being determined to prevent a head from touching the magnetic disk when the magnetic disk is mounted in a hard disk device.

3. The method for manufacturing a glass blank for magnetic disk according to claim 1 , wherein in the forming process, press forming is performed so that the temperature of portions of the pair of dies, which contact the molten glass, is substantially the same.

4. The method for manufacturing a glass blank for magnetic disk according to claim 1 , wherein the temperature of the pair of dies is kept lower than a glass transition point (Tg) of the molten glass during a period of time until the glass blank is separated from the die after beginning to contact the die.

5. The method for manufacturing a glass blank for magnetic disk according to claim 1 , wherein in the forming process, press forming is performed without attaching a mold release material to the die.

6. The method for manufacturing a glass blank for magnetic disk according to claim 1 , wherein a thermal expansion coefficient at 100° C. to 300° C. of the glass blank obtained after press forming is in a range of 30×10 −7 to 100×10 −7 (K −1 ).

7. The method for manufacturing a glass blank for magnetic disk according to claim 1 , wherein in the forming process, the lump of molten glass is press-formed so that flatness of the glass blank is 8 μm or less.

8. A method for manufacturing a glass substrate for magnetic disk, including a polishing process for polishing a glass blank with a machining allowance of 50 μm or less to manufacture a glass substrate for magnetic disk, the glass blank being manufactured with the method for manufacturing a glass blank for magnetic disk according to claim 1 .

9. A method for manufacturing a glass substrate for magnetic disk, wherein a glass substrate for magnetic disk is manufactured using a glass blank for magnetic disk, the glass blank being obtained with the method for manufacturing a glass blank for magnetic disk according to claim 1 .

10. A method for manufacturing a glass blank for magnetic disk, the method including a forming process of forming a plate-shaped glass blank by press-forming a falling molten glass in a direction orthogonal to the falling direction using a pair of dies while the molten glass is falling, wherein the forming process comprises a thermally equalizing process for reducing a difference in temperature of the pair of dies during a period of time until a new molten glass is press-formed after the dies are opened.

11. The method for manufacturing a glass blank for magnetic disk according to claim 10 , wherein the thermally equalizing process is a process of bringing a thermally equalizing material into contact with at least one of the pair of dies.

12. The method for manufacturing a glass blank for magnetic disk according to claim 10 , wherein in the forming process, press forming is performed so that the temperature of portions of the pair of dies, which contact the molten glass, is substantially the same.

13. The method for manufacturing a glass blank for magnetic disk according to claim 10 , wherein the temperature of the pair of dies is kept lower than a glass transition point (Tg) of the molten glass during a period of time until the glass blank is separated from the die after beginning to contact the die.

14. The method for manufacturing a glass blank for magnetic disk according to claim 10 , wherein in the forming process, press forming is performed without attaching a mold release material to the die.

15. A method for manufacturing a glass substrate for magnetic disk, including a polishing process for polishing a glass blank with a machining allowance of 50 μm or less to manufacture a glass substrate for magnetic disk, the glass blank being manufactured with the method for manufacturing a glass blank for magnetic disk according to claim 10 .

16. A method for manufacturing a glass substrate for magnetic disk, wherein a glass substrate for magnetic disk is manufactured using a glass blank for magnetic disk, the glass blank being obtained by the method for manufacturing a glass blank for magnetic disk according to claim 10 .

17. A method for manufacturing a glass blank for magnetic disk, the method comprising:
performing a forming process of forming a plate-shaped glass blank by press-forming a falling molten glass in a direction orthogonal to the falling direction using a pair of dies while the molten glass is falling;
performing, after the forming process, a detachment process of detaching from the die the glass blank attached to the die is performed without causing a difference in temperature of the pair of dies; and
performing, after the detaching process, the forming process by press-forming the next molten glass.

18. The method for manufacturing a glass blank for magnetic disk according to claim 17 , wherein in the detachment process, at least a part of the outer circumferential portion of the glass blank is cooled while both the dies and the glass blank are in contact with each other.

19. The method for manufacturing a glass blank for magnetic disk according to claim 18 , wherein in the detachment process, at least a part of the outer circumferential edge portion of the glass blank is cooled by supplying a gas to the glass blank.

20. The method for manufacturing a glass blank for magnetic disk according to claim 19 , wherein the gas is supplied immediately before or concurrent with time at which the pair of dies having been closed starts to open.

21. The method for manufacturing a glass blank for magnetic disk according to claim 17 , wherein in the forming process, press forming is performed so that the temperature of portions of the pair of dies, which contact the molten glass, is substantially the same.

22. The method for manufacturing a glass blank for magnetic disk according to claim 17 , wherein the temperature of the pair of dies is kept lower than a glass transition point (Tg) of the molten glass during a period of time until the glass blank is separated from the die after beginning to contact the die.

23. The method for manufacturing a glass blank for magnetic disk according to claim 17 , wherein in the forming process, press forming is performed without attaching a mold release material to the die.

24. The method for manufacturing a glass blank for magnetic disk according to claim 17 , wherein surface roughness (Ra) of each of th

Assignees

• Isono Hideki
• Tanino Hidekazu
• Murakami Akira
• Sato Takashi
• Sato Masamune
• Hoya Corp

Inventors

• Isono Hideki
• Tanino Hidekazu
• Murakami Akira
• Sato Takashi
• Sato Masamune

Classifications

• G11B5/8404 Primary

  manufacturing base layers · CPC title

• C03B2215/70

  Horizontal or inclined press axis · CPC title

• C03B2215/07

  Ceramic or cermets · CPC title

• C03B11/122

  Heating · CPC title

• C03B11/088

  Flat discs · CPC title