Method of depollution and regeneration of a fuel cell electrode poisoned by sulfur compounds

Patent metadata

Field	Value
Publication number	US-9406954-B2
Application number	US-201214131970-A
Country	US
Kind code	B2
Filing date	Jun 12, 2012
Priority date	Jul 13, 2011
Publication date	Aug 2, 2016
Grant date	Aug 2, 2016

Abstract

A method for depolluting and regenerating a catalytic fuel-cell electrode, the reaction of the fuel of the cell and capture of at least one polluting species occurring on the catalytic electrode, comprises: a decrease, at a constant first reference current density, in fuel flow, relative to a nominal fuel flow, for a first length of time, leading to a value for the stoichiometric coefficient of fuel lower than 1, to increase oxidation potential on the catalytic electrode and reach oxidation potential of the polluting species, to eliminate it; a cut-off of current for a cut-off time; an increase in flow above nominal flow, leading to a value of stoichiometric coefficient higher than or equal to 1; and an increase in current density until a second current density chosen by operator and possibly identical to or different from the initial reference current density, is reached.

First claim

The invention claimed is:

1. A method for depolluting and regenerating a catalytic fuel-cell electrode in a fuel cell having a fuel and operating with a fuel flow and at a current density, the reaction of the fuel of the fuel cell and capture of at least one polluting species occurring on said catalytic electrode, comprising the following steps:
a decrease, at a constant current density being a first reference current density, in the fuel flow, relative to a nominal fuel flow, for a first length of time, leading to a value for a stoichiometric coefficient (StH 2 ) of said fuel lower than 1, so as to increase the oxidation potential on said catalytic electrode and reach the oxidation potential of said polluting species, in order to eliminate said polluting species;
a cut-off of the current for a length of time called the cut-off time;
an increase in the fuel flow above the nominal flow, leading, once more, to a value of the stoichiometric coefficient higher than or equal to 1; and
an increase in the current density until a second current density chosen by the operator is reached.

2. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 1 , comprising passage to zero current triggered by observation of a drop in current density.

3. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 1 , comprising passage to zero current triggered by control of a potential of the electrode, and therefore a voltage of the fuel cell, varying over time.

4. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 1 , in which the cut-off time is between 30 seconds and 5 minutes.

5. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 1 , in which the increase in current density until about said second current density is reached is carried out gradually.

6. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 1 , in which the increase in the current density until about said second current density is reached is carried out in successive steps.

7. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 1 , in which the fuel is hydrogen-based, the catalytic electrode being noble-metal based.

8. The method for depolluting and regenerating a catalytic electrode as claimed in claim 7 , in which the noble metal is platinum, palladium or ruthenium.

9. The method for depolluting and regenerating a catalytic electrode as claimed in claim 7 , in which the fuel is based on pure hydrogen.

10. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 7 , in which the fuel is based on reformed hydrogen.

11. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 7 , in which the catalytic electrode comprises platinum nanoparticles supported by carbon aggregates.

12. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 7 , in which the polluting species is a sulfur-containing species.

13. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 12 , in which the duration of the decrease in hydrogen flow is adjusted to achieve a threshold anodic potential on the catalytic electrode at least higher than 0.9 V.

14. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 13 , in which the decrease in hydrogen flow is maintained for at least about one minute and less than about ten minutes.

15. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 12 , in which the polluting species is hydrogen sulfide.

16. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 7 , in which the polluting species is a carbon-containing species.

17. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 16 , in which the polluting species is carbon monoxide.

18. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 1 , comprising the following steps in succession:
a decrease in fuel flow from a nominal value corresponding to a first stoichiometric value, for a first length of time, causing the potential on said catalytic electrode to pass from an initial value to a first value higher than or equal to the oxidation potential of the polluting species;
an increase in fuel flow corresponding to a second stoichiometric value, for a second length of time, in order to accelerate the flow of fuel toward the catalytic sites of the anode; and
return of the flow to said nominal operating value for the reaction of the fuel at the catalytic electrode.

19. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 18 , in which the first length of time and the second length of time are about 3 minutes.

20. The method for depolluting and regenerating a catalytic fuel-cell electrode as claimed in claim 18 , in which the first stoichiometric value is about equal to 0.5, the second stoichiometric value being about equal to 2.

Assignees

• Passot Sylvain
• Faure Christel
• Franco Alejandro
• Lemaire Olivier
• Commissariat Energie Atomique
• L'Air Liquide

Inventors

• Passot Sylvain
• Faure Christel
• Franco Alejandro
• Lemaire Olivier

Classifications

• H01M8/04223 Primary

  during start-up or shut-down; Depolarisation or activation, e.g. purging; Means for short-circuiting defective fuel cells · CPC title

• H01M8/04753 Primary

  of fuel cell reactants · CPC title

• H01M2008/1095

  Fuel cells with polymeric electrolytes · CPC title

• Y02E60/50

  Fuel cells · CPC title

• H01M8/04238

  Depolarisation · CPC title