Urea-formaldehyde (UF) resin composition for enhanced stability, tensile and tear strength before and after cure

Patent metadata

Field	Value
Publication number	US-9404220-B2
Application number	US-201414501650-A
Country	US
Kind code	B2
Filing date	Sep 30, 2014
Priority date	Sep 30, 2013
Publication date	Aug 2, 2016
Grant date	Aug 2, 2016

Abstract

The present invention provides aqueous urea formaldehyde resin (UF resin) compositions having a pH or 7.0 or more, preferably, 8.5 or more, and comprising the UF resin modified with from 2.5 to 15 wt. %, of at least one ammonia or volatile amine neutralized carboxylic acid group containing solution polymer or alkali soluble emulsion polymer modifier, based on total UF resin and polymer solids, wherein the polymer modifier is the reaction product of 30 to 100 wt. % of methacrylic acid, acrylic acid, maleic anhydride, a salt thereof, or mixtures thereof, wherein the solution polymer has a weight average molecular weight of from 2,000 to 16,000 and the alkali soluble emulsion copolymer has a weight average molecular weight of from 1,500 to 20,000. The compositions enable the provision of untreated glass mats having improved wet web strength to prevent mat breakage in process.

First claim

We claim:

1. An aqueous urea formaldehyde resin (UF resin) composition having a pH or 7.0 or more and comprising the UF resin modified in a total polymer modifier amount of from 2.5 to 15 wt. %, based on total UF resin and polymer solids, of at least one ammonia or volatile amine neutralized carboxylic acid group containing polymer which is the reaction product of 30 wt. % or more of methacrylic acid, acrylic acid, maleic anhydride, a salt thereof, or mixtures thereof as a carboxylic acid group containing monomer, wherein the at least one ammonia or volatile amine neutralized carboxylic acid group containing polymer is chosen from a solution polymer having a weight average molecular weight of from 2,000 to 16,000 and alkali soluble emulsion copolymers (resins) having a weight average molecular weight of from 1,500 to 20,000.

2. The aqueous urea formaldehyde resin composition as claimed in claim 1 , wherein the total polymer modifier amount ranges from 5 to 10 wt. %, based on total UF resin and polymer solids.

3. The aqueous urea formaldehyde resin composition as claimed in claim 1 , wherein the at least one ammonia or volatile amine neutralized carboxylic acid group containing polymer is the reaction product of 35 wt. % or more of a carboxylic acid group containing monomer.

4. The aqueous urea formaldehyde resin composition as claimed in claim 1 , wherein the carboxylic acid group containing monomer is methacrylic acid or its salt.

5. The aqueous urea formaldehyde resin composition as claimed in claim 1 , wherein the ammonia or volatile amine neutralized carboxylic acid group containing polymer is chosen from a solution polymer from 2,000 to 12,000, and an alkali soluble emulsion copolymer having a weight average molecular weight of from 1,500 to 15,000.

6. The aqueous urea formaldehyde resin composition as claimed in claim 1 which has a pH of 8 or more.

7. The aqueous urea formaldehyde resin composition as claimed in claim 1 , wherein the ammonia or volatile amine neutralized alkali soluble emulsion polymer is a copolymer comprising the copolymerization product of the methacrylic acid, acrylic acid, maleic anhydride, a salt thereof, or mixtures thereof as the carboxylic acid group containing monomer with from 30 to 70 wt. % of a nonionic comonomer, based on the total weight of monomers used to make the ammonia or volatile amine neutralized carboxylic acid group containing polymer.

8. The aqueous urea formaldehyde resin composition as claimed in claim 7 , wherein the ammonia or volatile amine neutralized solution polymer comprises the polymerization product of a monomer mix comprising 50 wt. % or more of methacrylic acid, based on the total weight of monomers used to make the polymer, and the remainder of a water soluble nonionic comonomer.

9. The aqueous urea formaldehyde resin composition as claimed in claim 1 , wherein the composition passes a 24 hour room temperature binder composition stability test at a 2:1 (vol:vol) dilution in which 1.0 ml of the undiluted aqueous urea formaldehyde resin composition at 50% solids is mixed with 2.0 ml of whitewater comprising 0.06 wt. %, as solids, of a mixture of a polyacrylamide thickener and a alkylamine dispersant.

10. A method of using the aqueous urea formaldehyde resin composition as claimed in claim 1 , comprising forming the composition, applying the composition to a wet laid continuous glass fiber mat and heating to cure the composition.

Assignees

• Rohm & Haas

Inventors

• Brady Jean M
• Finley Maureen J
• Williams Drew E

Classifications

• C08L33/10

  Homopolymers or copolymers of methacrylic acid esters · CPC title

• C08G12/40

  Chemically modified polycondensates · CPC title

• C08L33/14

  of esters containing halogen, nitrogen, sulfur, or oxygen atoms in addition to the carboxy oxygen · CPC title

• C08L61/32

  Modified amine-aldehyde condensates · CPC title

• C08G12/12

  Ureas; Thioureas · CPC title