Precipitation hardening martensitic stainless steel, and steam turbine long blade, steam turbine, and power plant using the same

Patent metadata

Field	Value
Publication number	US-9388702-B2
Application number	US-201313741946-A
Country	US
Kind code	B2
Filing date	Jan 15, 2013
Priority date	Jan 19, 2012
Publication date	Jul 12, 2016
Grant date	Jul 12, 2016

Abstract

The problem to be solved of the present invention is to provide a precipitation hardening martensitic stainless steel having excellent tissue stability, strength, toughness, and corrosion-resistance, requiring no sub-zero treatment, and having excellent productivity; and also a steam turbine long blade using the same. The problem is solved by providing a precipitation hardening martensitic stainless steel containing, by mass, 0.1% or less of C; 0.1% or less of N; 9.0% or more and 14.0% or less of Cr; 9.0% or more and 14.0% or less of Ni; 0.5% or more and 2.5% or less of Mo; 0.5% or less of Si; 1.0% or less of Mn; 0.25% or more and 1.75% or less of Ti; 0.25% or more and 1.75% or less of Al, and the rest is Fe and inevitable impurities; and a steam turbine long blade using the precipitation hardening martensitic stainless steel.

First claim

What is claimed is:

1. A precipitation hardening martensitic stainless steel comprising, by mass, 0.1% or less of C; 0.1% or less of N; 9.0% or more and 14.0% or less of Cr; 9.0% or more and 14.0% or less of Ni; 0.5% or more and 1.47% or less total of Mo with optional W; 0.5% or less of Si; 1.0% or less of Mn; 0.25% or more and 1.75% or less of Ti; 0.25% or more and 1.75% or less of Al; 1.0% or less of Co and the rest is Fe and inevitable impurities, and
a parameter A related to martensite transformation finish-temperature and a parameter B related to martensitic tissue stability satisfying the following specific range:
(Cr+2.2Si+1.1Mo+0.6W+4.3Al+2.1Ti)−(Ni+31.2C+0.5Mn+27N+1.1Co)  A:

(125−4.0Cr−6.0Ni−3.0Mo+2.5Al−1.5W−3.5Mn−3.5Si−5.5Co−2.0Ti−221.5C−321.4N), and,  B:

Specific range: 4.0≦A≦10.0 and 2.0≦B≦7.0.

2. The precipitation hardening martensitic stainless steel according to claim 1 , wherein the total amount of Al and Ti is 0.75% or more and 2.25% or less by mass.

3. The precipitation hardening martensitic stainless steel according to claim 1 , further comprising at least one member selected from Nb, V, and Ta wherein the total amount thereof is 0.5% or less by mass.

4. The precipitation hardening martensitic stainless steel according to claim 1 , further comprising, by mass, Re: 1.0% or less.

5. The precipitation hardening martensitic stainless steel according to claim 1 , wherein the inevitable impurities are at least one member selected from S, P, Sb, Sn, and As, the amounts thereof being, by mass, S: 0.5% or less, P: 0.5% or less, Sb: 0.1% or less, Sn: 0.1% or less, and As: 0.1% or less.

6. The precipitation hardening martensitic stainless steel according to claim 1 , wherein a temperature range of a solution treatment is 900 to 1000° C. and a temperature range of an aging treatment is 500 to 600° C.

7. A steam turbine long blade using the precipitation hardening martensitic stainless steel of claim 1 .

8. The steam turbine long blade according to claim 7 , wherein a Stellite plate made of a Co-based alloy is joined to a front end portion of the blade.

9. A turbine rotor comprising the steam turbine long blade of claim 7 .

10. A steam turbine comprising the turbine rotor of claim 9 .

11. A power plant comprising the steam turbine of claim 10 .

Assignees

• Hitachi Ltd
• Mitsubishi Hitachi Power Sys

Inventors

• Oikawa Shinji
• Yoda Hideo
• Arai Masahiko
• Doi Hiroyuki

Classifications

• F05D2300/171

  Steel alloys · CPC title

• C22C38/44

  with molybdenum or tungsten · CPC title

• C22C38/001

  containing N · CPC title

• C22C38/50

  with titanium or zirconium · CPC title

• C21D9/0068

  for particular articles not mentioned below · CPC title