Latex binders, aqueous coatings and paints having freeze-thaw ability and methods for using same

Patent metadata

Field	Value
Publication number	US-9388323-B2
Application number	US-32125609-A
Country	US
Kind code	B2
Filing date	Jan 16, 2009
Priority date	Jan 18, 2008
Publication date	Jul 12, 2016
Grant date	Jul 12, 2016

Abstract

Disclosed are latex polymers and an aqueous coating compositions having excellent freeze-thaw stability, open time, stain resistance, low temperature film formation, foam resistance, block resistance, adhesion, water sensitivity and a low-VOC content. The latex polymers and aqueous coating compositions include at least one latex polymer derived from at least one monomer copolymerized or blended with an alkoxylated compound, for example an alkoxylated tristyrylphenol or an alkoxylated tributylphenol. Also provided is an aqueous coating composition including at least one latex polymer, at least one pigment, water and at least one freeze-thaw additive. Typically, the freeze-thaw additive in an amount greater than about 1.3% by weight of the polymer, typically in an amount greater than about 2% by weight of the polymer, in an amount greater than about 4% by weight of the polymer, in an amount greater than about 7.5% by weight of the polymer, in an amount greater than about 10% by weight of the polymer or in an amount greater than about 20% by weight of the polymer.

First claim

What is claimed is:

1. A latex polymer binder derivable from:
at least one first monomer, and
at least one second monomer of formula:

wherein:
R 1 , R 2 , and R 3 are independently selected from the group consisting of:

X comprises a divalent hydrocarbon radical comprising a linear or branched alkylene radical having from about 2 to 8 carbon atoms;
n is an integer ranging from 1 to 100; and
R comprises at least one acrylate, C 1 -C 6 alkyl acrylate, allyl, vinyl, maleate, itaconate, fumarate, acrylo, methacrylo, acrylamido, methacrylamido, diallylamino, allyl ether, vinyl ether, α-alkenyl, maleimido, styrenyl, or α-alkyl styrenyl group; and
further wherein said latex polymer binder is a binder having a glass transition temperature (Tg) ranging from about −5° C. to about 5° C.

2. The binder of claim 1 , wherein R comprises at least one acrylate, C 1 -C 6 alkyl acrylate, allyl, vinyl, maleate, itaconate or fumarate.

3. The binder of claim 1 , wherein R comprises at least one acrylo, methacrylo, acrylamido, methacrylamido, diallylamino, allyl ether, vinyl ether, α-alkenyl, maleimido, styrenyl, or α-alkyl styrenyl group.

4. The binder of claim 1 , wherein R comprises:
R a CH═C(R b )COO—,
wherein R a is H, and R b comprises H or a C 1 -C 4 alkyl.

5. The binder of claim 1 , wherein R comprises
—HC═CYZ or —OCH═CYZ,
wherein:
Y is H, CH 3 , or Cl;
Z is CN, Cl, —COOR c , —C 6 H 4 R c , —COOR d , or —HC═CH 2 ;
R d is C 1 -C 8 alkyl or C 2 -C 8 hydroxy alkyl; and
R c is H, Cl, Br, or C 1 -C 4 alkyl.

6. The binder of claim 1 , wherein n is an integer ranging from about 10 to about 50.

7. The binder of claim 6 , wherein n is an integer ranging from about 20 to about 50.

8. The binder of claim 1 , wherein the first monomer comprises at least one acrylic monomer comprising acrylic acid, acrylic acid ester, methacrylic acid, methacrylic acid ester, or a mixture thereof.

9. The binder of claim 8 , wherein the binder is further derivable from at least one third monomer comprising styrene, alpha-methyl styrene, vinyl chloride, acrylonitrile, methacrylonitrile, ureido methacrylate, vinyl acetate, a vinyl ester of a branched tertiary monocarboxylic acid, itaconic acid, crotonic acid, maleic acid, fumaric acid, ethylene, or a C 4 -C 8 conjugated diene.

10. The binder of claim 1 , wherein the binder has a glass transition temperature (Tg) ranging from about −5° C. to about 0° C.

11. The binder of claim 1 , wherein the binder has a mean particle size of less than about 200 nm.

12. The binder of claim 1 , wherein the binder has a mean particle size of less than about 190 nm.

13. The binder of claim 1 , wherein the binder has a mean particle size of less than about 175 nm.

14. A method for imparting freeze-thaw stability to a low VOC coating composition, comprising:
forming the composition with a latex polymer binder prepared by copolymerizing:
(1) at least one first monomer with
(2) at least one second monomer of formula:

wherein:
R 1 ,R 2 , and R 3 are independently selected from the group consisting of:

X comprises a divalent hydrocarbon radical comprising a linear or branched alkylene radical having from about 2 to 8 carbon atoms;
n is an integer ranging from 1 to 100; and
R comprises at least one acrylate, C 1 -C 6 , alkyl acrylate, allyl, vinyl, maleate, itaconate, fumarate, acrylo, methacrylo, acrylamido, methacrylamido, diallylamino, allyl ether, vinyl ether, α-alkenyl, maleimido, styrenyl, or α-alkyl styrenyl group; and
further wherein the binder has a glass transition temperature (Tg) ranging from about −5° C. to about 5° C., and freeze-thaw stability is imparted to the low VOC coating composition.

15. The method of claim 14 , wherein the binder has a glass transition temperature (Tg) ranging from about −5° C. to about 0° C.

16. The method of claim 15 , wherein the binder has a mean particle size of less than about 200 nm.

17. The method of claim 14 , wherein the binder has a mean particle size of less than about 190 nm.

18. The method of claim 14 , wherein the binder has a mean particle size of less than about 175 nm.

Assignees

• Zong Zhengang
• Li Yi-Zhong
• Ruiz Jose
• Rhodia Operations

Inventors

• Zong Zhengang
• Li Yi-Zhong
• Ruiz Jose

Classifications

• C07C43/23

  containing hydroxy or O-metal groups · CPC title

• C08K5/0008

  Organic ingredients according to more than one of the "one dot" groups of C08K5/01 - C08K5/59 · CPC title

• C09D133/02 Primary

  Homopolymers or copolymers of acids; Metal or ammonium salts thereof · CPC title

• C09D133/08

  Homopolymers or copolymers of acrylic acid esters · CPC title

• C08F2/24

  with the aid of emulsifying agents · CPC title