Hot forging use non-heat-treated steel and hot forged non-heat-treated steel part

Patent metadata

Field	Value
Publication number	US-9376738-B2
Application number	US-31182108-A
Country	US
Kind code	B2
Filing date	Oct 27, 2008
Priority date	Oct 29, 2007
Publication date	Jun 28, 2016
Grant date	Jun 28, 2016

Abstract

The present invention provides hot forging use non heat-treated steel where controlled cooling after shaping by hot forging is used to make the main structure of the steel martensite even without subsequent reheating and heat treatment by quenching and tempering and thereby give a steel part with a high strength and high toughness and superior machineability and a hot forged non heat-treated steel part made of that steel, in particular provides a martensite type hot forging use non heat-treated steel characterized by containing, by mass %, C: 0.10 to 0.20%, Si: 0.10 to 0.50%, Mn: 1.0 to 3.0%, P: 0.001 to 0.1%, S: 0.005 to 0.8%, Cr: 0.10 to 1.50%, Al: over 0.1 to 0.20%, and N: 0.0020 to 0.0080% and having a balance of substantially Fe and unavoidable impurities and a hot forged non heat-treated steel part made of such steel and characterized in that the steel structure of the entire cross-section at part or all of that part is substantially a martensite structure with an effective crystal grain size of 15 μm or less.

First claim

The invention claimed is:

1. A non-heat-treated steel for hot forging consisting of, by mass %,
C: 0.14 to 0.20%,
Si: 0.13 to 0.50%,
Mn: 1.0 to 3.0%,
P: 0.001 to 0.1%,
S: 0.051 to 0.8%,
Cr: 0.56 to 1.50%,
Al: 0.119 to 0.20%,
N: 0.0020 to 0.006%,
optionally, B: 0.0005 to 0.0050% and Ti: 0.005 to 0.030%,
optionally, one or more of V: 0.05 to 0.30% or Mo: 0.05 to 1.0%, and
a balance of Fe and unavoidable impurities.

2. The non-heat-treated steel for hot forging as set forth in claim 1 , wherein
B: 0.0005 to 0.0050% and
Ti: 0.005 to 0.030% are present in the steel.

3. The non-heat-treated steel for hot forging as set forth in claim 1 or 2 , wherein one or more of
V: 0.05 to 0.30% or
Mo: 0.05 to 1.0% is present in the steel.

Assignees

• Teramoto Shinya
• Miyanishi Kei
• Hashimura Masayuki
• Nippon Steel & Sumitomo Metal Corp

Inventors

• Teramoto Shinya
• Miyanishi Kei
• Hashimura Masayuki

Classifications

• C21D7/13

  by hot working · CPC title

• C22C38/38 Primary

  with more than 1.5% by weight of manganese · CPC title

• C22C38/02 Primary

  containing silicon · CPC title

• C22C38/32

  with boron · CPC title

• C22C38/24

  with vanadium · CPC title