Polytetrafluoroethylene aqueous emulsion and process for its production, polytetrafluoroethylene aqueous dispersion obtainable by using such an aqueous emulsion, polytetrafluoroethylene fine powder, and stretched porous material

Patent metadata

Field	Value
Publication number	US-9376520-B2
Application number	US-201213447803-A
Country	US
Kind code	B2
Filing date	Apr 16, 2012
Priority date	Nov 9, 2009
Publication date	Jun 28, 2016
Grant date	Jun 28, 2016

Abstract

To produce a PTFE aqueous emulsion, whereby the environmental load is little, the stability of the aqueous emulsion is high, and a molded product having high heat resistance can be obtained. A process for producing a PTFE aqueous emulsion, which comprises emulsion-polymerizing tetrafluoroethylene (TFE) by means of at least one fluorinated emulsifier selected from the group consisting of a C 4-8 fluorinated carboxylic acid having from 1 to 4 etheric oxygen atoms in its main chain, and its salts, to obtain an aqueous emulsion containing polytetrafluoroethylene (PTFE) microparticles having an average primary particle size of from 0.1 to 0.3 μm, wherein at the beginning of the emulsion polymerization of TFE, a (polyfluoroalkyl)ethylene (a) represented by “CH 2 ═CH—Rf 1 ”, and/or a comonomer (b) having a monomer reactivity ratio r TFE of from 0.1 to 8 in copolymerization with tetrafluoroethylene, is incorporated to the emulsion polymerization system, so as to be from 0.001 to 0.01 mass % relative to the final amount of polytetrafluoroethylene produced.

First claim

What is claimed is:

1. A process for producing a polytetrafluoroethylene aqueous emulsion, the process comprising:
charging to a polymerization reactor a full amount of at least one comonomer selected from the group consisting of CH 2 ═CH—(CF 2 ) 4 F, CH 2 ═CH—(CF 2 ) 6 F and perfluoro(2-methylene-4-methyl-1,3-dioxolane);
adding to the reactor at least one fluorinated emulsifier selected from the group consisting of a C 4-8 fluorinated carboxylic acid having from 1 to 4 etheric oxygen atoms in a main chain and salts thereof;
initiating an emulsion polymerization reaction of tetrafluorethylene in the presence of the at least one fluorinated emulsifier and the full amount of the at least one comonomer; and
continuing the emulsion polymerization of tetrafluoroethylene to obtain an aqueous emulsion containing polytetrafluoroethylene microparticles having an average primary particle size of from 0.21 to 0.27 μm;
wherein
a stability time of an aqueous 20% solid content emulsion of the polytetrafluoroethylene microparticles at 23° C. is greater than 200 seconds,
a content of the at least one comonomer in the polytetrafluoroethylene produced is from 0.0015 to 0.01 mass % relative to the final amount of polytetrafluoroethylene produced, and
a stress relaxation time of the polytetrafluoroethylene produced is at least 500 seconds.

2. The process for producing a polytetrafluoroethylene aqueous emulsion according to claim 1 , wherein the average primary particle size of the polytetrafluoroethylene microparticles is from 0.22 to 0.27 μm.

3. The process for producing a polytetrafluoroethylene aqueous emulsion according to claim 1 , wherein the at least one comonomer is at least one of, CH 2 ═CH—(CF 2 ) 4 F and CH 2 ═CH—(CF 2 ) 6 F.

4. The process for producing a polytetrafluoroethylene aqueous emulsion according to claim 1 , wherein the at least one comonomer is perfluoro(2-methylene-4-methyl-1,3-dioxolane).

5. A polytetrafluoroethylene aqueous emulsion obtained by the process as defined in claim 1 .

6. A polytetrafluoroethylene aqueous dispersion obtained by a process comprising:
stabilizing the emulsion of claim 5 by adding a nonionic surfactant; and concentrating the content of polytetrafluoroethylene microparticles to from 50 to 70 mass %.

7. A polytetrafluoroethylene fine powder obtained by a process comprising:
coagulating the polytetrafluoroethylene aqueous emulsion as defined in claim 5 ,
wherein a stress relaxation time of the polytetrafluoroethylene fine powder is at least 500 seconds.

8. The polytetrafluoroethylene fine powder according to claim 7 , wherein a standard specific gravity of the polytetrafluoroethylene fine powder is from 2.135 to 2.155.

9. A stretched porous material obtained by a process comprising:
paste extrusion of the polytetrafluoroethylene fine powder as defined in claim 7 , followed by stretching the extrudate.

Assignees

• Higuchi Shinya
• Matsuoka Yasuhiko
• Kobayashi Shigeki
• Asahi Glass Co Ltd

Inventors

• Higuchi Shinya
• Matsuoka Yasuhiko
• Kobayashi Shigeki

Classifications

• C08F214/26 Primary

  Tetrafluoroethene · CPC title

• C08F2/24

  with the aid of emulsifying agents · CPC title

• C08J3/03

  in aqueous media · CPC title

• C08J2327/18

  Homopolymers or copolymers of tetrafluoroethylene · CPC title

• C08F14/26

  Tetrafluoroethene · CPC title