Abstract

The invention discloses a blue quantum dot composite particle, a photoelectric element and a photoelectric device. The blue quantum dot composite particle comprises a core and a shell that covers the core, wherein the core is a blue quantum dot, the shell is formed of a polymer, and the surface of the shell is chemically modified with gold nano-granules. The fluorescence efficiency of the blue quantum dot composite particle according to the invention is very high.

First claim

What is claimed is:

1. A blue quantum dot composite particle having a core and a shell that covers the core, wherein the core is a blue quantum dot, the shell is formed of a polymer, and the surface of the shell is chemically modified with gold nano-granules, and wherein the thickness of the shell is in the range of from 5 nm to 30 nm.

2. The blue quantum dot composite particle according to claim 1 , wherein the grain size of the gold nano-granules is in the range from 3 nm to 10 nm.

3. The blue quantum dot composite particle according to claim 1 , wherein the modification degree of the gold nano-granules in the blue quantum dot composite particle is that the surface of one blue quantum dot is modified with 2-3 gold nano-granules on average.

4. The blue quantum dot composite particle according to claim 1 , wherein the modification degree of the gold nano-granules in the blue quantum dot composite particle is that the surface of one blue quantum dot is modified with 2-3 gold nano-granules on average.

5. The blue quantum dot composite particle according to claim 2 , wherein the modification degree of the gold nano-granules in the blue quantum dot composite particle is that the surface of one blue quantum dot is modified with 2-3 gold nano-granules on average.

6. The blue quantum dot composite particle according to claim 1 , wherein the monomer of the polymer is at least one selected from methyl methacrylate, methyl acrylate, ethyl acrylate and butyl acrylate.

7. The blue quantum dot composite particle according to claim 1 , wherein the monomer of the polymer is at least one selected from methyl methacrylate, methyl acrylate, ethyl acrylate and butyl acrylate.

8. The blue quantum dot composite particle according to claim 2 , wherein the monomer of the polymer is at least one selected from methyl methacrylate, methyl acrylate, ethyl acrylate and butyl acrylate.

9. The blue quantum dot composite particle according to claim 1 , wherein the blue quantum dot consists of a compound selected from the II-VI group elements and a compound selected from the III-V group elements.

10. The blue quantum dot composite particle according to claim 1 , wherein the blue quantum dot consists of a compound selected from the II-VI group elements and a compound selected from the III-V group elements.

11. The blue quantum dot composite particle according to claim 2 , wherein the blue quantum dot consists of a compound selected from the II-VI group elements and a compound selected from the III-V group elements.

12. A photoelectric element, comprising the blue quantum dot composite particle according to claim 1 .

13. A method for preparing a blue quantum dot composite particle having a core and a shell that covers the core, wherein the core is a blue quantum dot, the shell is formed of a polymer, and the surface of the shell is chemically modified with gold nano-granules, and wherein the thickness of the shell is in the range from 5 nm to 30 nm, the method comprising:
coating a polymer on the surface of a blue quantum dot via seed emulsion polymerization;
modifying the polymer via hydrolysis so as to make the surface thereof have a carboxyl functional group; and
combining gold nano-granules having an amino functional group on its surface with a blue quantum dot having a carboxyl functional group on its surface via chemical coupling, and obtaining the blue quantum dot composite particle.

14. The method according to claim 13 , wherein the thickness of the polymer coated on the surface of the blue quantum dot is in the range from 5 nm to 30 nm.

15. The method according to claim 13 , wherein the grain size of the gold nano-granule is in the range from 3 nm to 10 nm.

16. The method according to claim 13 , wherein the monomer of the polymer is at least one selected from methyl methacrylate, methyl acrylate, ethyl acrylate and butyl acrylate.

17. The method according to claim 14 , wherein the monomer of the polymer is at least one selected from methyl methacrylate, methyl acrylate, ethyl acrylate and butyl acrylate.

18. The method according to claim 15 , wherein the monomer of the polymer is at least one selected from methyl methacrylate, methyl acrylate, ethyl acrylate and butyl acrylate.

Assignees

• Boe Technology Group Co Ltd

Inventors

• Tang Chen
• Gu Jingxia

Classifications

• H10P14/6546

  to change the surface groups of the insulating materials · CPC title

• H10P14/6534

  by exposure to a liquid · CPC title

• H10P14/6342

  Liquid deposition, e.g. spin-coating, sol-gel techniques or spray coating · CPC title

• H10P14/683

  carbon-based polymeric organic materials, e.g. polyimides, poly cyclobutene or PVC · CPC title

• B82Y20/00

  Nanooptics, e.g. quantum optics or photonic crystals · CPC title