Method of molding composite plastic sheet material to form a compression molded, deep-drawn article

Patent metadata

Field	Value
Publication number	US-9364975-B2
Application number	US-201213606430-A
Country	US
Kind code	B2
Filing date	Sep 7, 2012
Priority date	Sep 7, 2012
Publication date	Jun 14, 2016
Grant date	Jun 14, 2016

Abstract

A method of molding composite plastic sheet material to form a compression molded, deep-drawn article is provided. The method includes placing a heated blank of moldable, composite plastic sheet material over a female die having an article-defining cavity defined by inner surfaces of the die so that the heated blank has a predetermined position and orientation over the cavity. Then an inner portion of the heated blank is forced into the cavity along a substantially vertical axis and against the inner surfaces of the die to obtain deep-drawn material. Outer peripheral portions of the heated blank adjacent the cavity are controllably held with corresponding predetermined holding forces based on the size and shape of the article to resist movement of the outer peripheral portions towards the cavity during the step of forcing wherein the deep-drawn material controllably stretches during the step of forcing without wrinkling, tearing or ripping.

First claim

What is claimed is:

1. A method of molding composite plastic sheet material to form a compression molded, deep-drawn article, the method comprising:
placing a heated blank of moldable, composite plastic sheet material over a female die having an article-defining cavity defined by inner surfaces of the female die so that the heated blank has a predetermined position and orientation over the article-defining cavity;
forcing an inner portion of the heated blank into the article-defining cavity of the female die along a substantially vertical axis and against the inner surfaces of the female die to obtain deep-drawn material;
controllably holding outer peripheral portions of the blank adjacent the article-defining cavity with corresponding predetermined holding forces obtained by selective placement of holding devices on the outer peripheral portions of the blank based on the size and shape of the article to resist movement of the outer peripheral portions towards the article-defining cavity during the step of forcing, wherein the deep-drawn material and the outer peripheral portions are controllably stretched during the step of forcing without wrinkling, tearing or ripping;
removing the deep-drawn material from the female die; and
removing any excess material from the periphery of the deep-drawn material to form the deep-drawn article.

2. The method as claimed in claim 1 , wherein the step of holding is performed with variable holding forces which increase during the step of forcing.

3. The method as claimed in claim 2 , wherein the holding forces are applied on the blank outside of the cavity so that a first holding force is initially applied to a first outer peripheral portion to allow the inner portion of the blank to travel into the cavity and a second holding force larger than the first holding force is later applied on the first outer peripheral portion of the blank outside of the cavity as the inner portion of the blank travels into the cavity.

4. The method as claimed in claim 1 , wherein the step of holding is performed at a plurality of spaced, outer peripheral portions of the blank adjacent the article-defining cavity.

5. The method as claimed in claim 1 , wherein the step of forcing is performed in a single stamping stage.

6. The method as claimed in claim 1 , wherein the composite plastic sheet material comprises a plurality of discontinuous fibers dispersed within a thermoplastic resin.

7. The method as claimed in claim 6 , wherein the thermoplastic resin is selected from polyolefins, thermoplastic polyolefin blends, polyvinyl polymers, diene polymers, polyamides, polyesters, polycarbonates, polyestercarbonates, styrene-containing polymers, acrylic polymers, polyimides, polylphenylene ether, polyphenylene oxide, polyphenylenesulphide, polyethers, polyetherketones, polyacetals, polyurethanes, polybenzimidazole, and copolymers or mixtures thereof.

8. The method as claimed in claim 6 , wherein the fibers are selected from glass fibers, carbon fibers, synthetic organic fibers, natural fibers, mineral fibers, metal and/or metalized or coated fibers, or mixtures thereof.

9. The method as claimed in claim 6 , wherein the fibers are selected from glass fibers, carbon fibers, polyaramid fibers, polyester fibers, nylon fibers, hemp fibers, sisal fibers, basalt fibers, steel fibers, aluminum fibers, copper fibers, zinc fibers, or mixtures thereof.

10. The method as claimed in claim 1 , wherein the composite sheet material has a porosity between about 5% to about 95% by volume and an areal density of from about 400 g/m 2 to about 4000 g/m 2 .

11. The method as claimed in claim 6 , wherein the fiber content is from about 20% to about 80% by weight of the thermoplastic resin.

12. The method as claimed in claim 1 , wherein bottom and side walls of the article have a thickness in a range of 1 mm to 5 mm.

13. A method of molding porous, reinforced, composite thermoplastic sheet material to form a compression molded, deep-drawn automotive article, the method comprising:
placing a heated blank of moldable, reinforced, composite thermoplastic sheet material over a female die having an article-defining cavity defined by inner surfaces of the female die so that the heated blank has a predetermined position and orientation over the article-defining cavity;
forcing an inner portion of the heated blank into the article-defining cavity of the female die along a substantially vertical axis and against the inner surfaces of the female die to obtain deep-drawn material;
controllably holding outer peripheral portions of the blank adjacent the article-defining cavity with corresponding predetermined holding forces obtained by selective placement of holding devices on the outer peripheral portions of the blank based on size and shape of the article to resist movement of the outer peripheral portions towards the article-defining cavity during the step of forcing wherein the deep-drawn material and the outer peripheral portions are controllably stretched during the step of forcing without wrinkling, tearing or ripping;
removing the deep-drawn material from the female die; and
removing any excess material from the periphery of the drawn material to form the drawn automotive article.

14. The method as claimed in claim 13 , wherein the step of holding is performed with variable holding forces which increase during the step of forcing.

15. The method as claimed in claim 14 , wherein the variable holding forces are applied on the blank outside of the cavity so that a first holding force is initially applied to a first outer peripheral portion of the blank to allow the inner portion of the blank to travel into the cavity and a second holding force larger than the first holding force is later applied on the first outer peripheral portion of the blank outside of the cavity as the inner portion of the blank travels into the cavity.

16. The method as claimed in claim 13 , wherein the step of holding is performed at a plurality of spaced, outer peripheral portions of the blank adjacent the article-defining cavity.

17. The method as claimed in claim 13 , wherein the step of forcing is performed in a single stamping stage.

18. The method as claimed in claim 13 , wherein the thermoplastic composite sheet material comprises a plurality of discontinuous fibers dispersed within a thermoplastic resin.

19. The method as claimed in claim 18 , wherein the thermoplastic resin is selected from polyolefins, thermoplastic polyolefin blends, polyvinyl polymers, diene polymers, polyamides, polyesters, polycarbonates, polyestercarbonates, styrene-containing polymers, acrylic polymers, polyimides, polylphenylene ether, polyphenylene oxide, polyphenylenesulphide, polyethers, polyetherketones, polyacetals, polyurethanes, polybenzimidazole, and copolymers or mixtures thereof.

20. The method as claimed in claim 18 , wherein the fibers are selected from glass fibers, carbon fibers, synthetic organic fibers, natural fibers, mineral fibers, metal and/or metalized or coated fibers, or mixtures thereof.

21. The method as claimed in claim 18 , wherein the fibers are selected from glass fibers, carbon fibers, polyaramid fibers, polyester fibers, nylon fibers, hemp fibers, sisal fibers, basalt fibers, steel fibers, aluminum fibers, copper fibers, zinc fibers, or mixtures thereof.

22. The method as claimed in claim 13 , wherein the composite sheet material has a porosity between about 5% to about 95% by volume and an areal density of from about

Assignees

• Preisler Darius J
• Heikkila Christopher A
• Global Ip Holdings Llc

Inventors

• Preisler Darius J
• Heikkila Christopher A

Classifications

• B29C51/082

  by shaping between complementary mould parts · CPC title

• B29C43/36 Primary

  Moulds for making articles of definite length, i.e. discrete articles · CPC title

• B29K2105/12

  of short lengths, e.g. chopped filaments, staple fibres or bristles · CPC title

• B29C2793/009

  after shaping · CPC title

• B29L2031/3008

  Instrument panels · CPC title