Method for repairing a damage point in a cast part and method for producing a suitable repair material

Patent metadata

Field	Value
Publication number	US-9358644-B2
Application number	US-201214342651-A
Country	US
Kind code	B2
Filing date	Aug 23, 2012
Priority date	Sep 1, 2011
Publication date	Jun 7, 2016
Grant date	Jun 7, 2016

Abstract

A method prepares a repair material for and repairs a damage point in the surface of cast parts. Spray particles having the same cast structure as the cast part are used as materials. The particles are applied to the damage point by cold gas spraying. The cold gas spraying is performed such that the spray particles are not melted and, advantageously, the cast structure is retained after the spray particles contact the repair point. The repair point can thus be advantageously furnished with the same properties as the rest of the component to be repaired. The repair material can be produced in that a cast part having the required cast structure is reduced to small pieces.

First claim

The invention claimed is:

1. A method for repairing a damaged site in a surface of a cast part, comprising:
providing a cast body made of a material of which the cast part is formed;
comminuting the cast body to produce a repair material comprised of spray particles having a same cast microstructure as the cast part; and
applying the repair material to the damaged site by cold gas spraying.

2. The method as claimed in claim 1 ,
wherein a distribution of the diameters of the spray particles has a mean diameter of at least 100 μm and at most 200 μm.

3. The method as claimed in claim 2 , wherein a width of the distribution is at least half the range indicated in claim 2 .

4. The method as claimed in claim 3 , further comprising heating the damaged site while applying the repair material.

5. The method as claimed in claim 4 , further comprising heat treating the cast part after applying the repair material.

6. The method as claimed in claim 5 ,
wherein the cast part is formed of globular gray cast iron or aluminum-silicon.

7. The method as claimed in claim 1 , further comprising heating the damaged site while applying the repair material.

8. The method as claimed in claim 7 , further comprising irradiating the damaged site with a laser beam.

9. The method as claimed in claim 1 , further comprising heat treating the cast part after applying the repair material.

10. The method as claimed in claim 1 , wherein the cast part is formed of globular gray cast iron.

11. The method as claimed in claim 1 ,
wherein the comminuting is selected from the group consisting of shredding and grinding.

12. A method comprising:
casting a cast part;
casting a body made of a material of which the cast part is formed; and
comminuting the body to produce a repair material comprised of spray particles having a same cast microstructure as the cast part; and
using cold gas spraying to apply the repair material to a damaged site in a surface of the cast part.

13. The method as claimed in claim 12 ,
wherein the comminuting is selected from the group consisting of shredding and grinding.

14. The method as claimed in claim 12 , further comprising irradiating the damaged site with a laser beam.

15. The method as claimed in claim 12 , further comprising heating the damaged site while applying the repair material.

16. The method as claimed in claim 12 , further comprising heat treating the cast part after applying the repair material.

17. The method as claimed in claim 12 ,
wherein the cast part is formed of globular gray cast iron or aluminum-silicon.

18. A method for repairing a damaged site in a surface of a cast part, comprising:
casting a body and the cast part in a same production run;
comminuting the body to produce spray particles; and
repairing the damaged site with the spray particles by cold gas spraying.

19. The method as claimed in claim 18 , further comprising removing an edge zone from the body before the comminuting.

20. The method as claimed in claim 18 , wherein a material of the cast part is selected from the group consisting of globular gray iron, laminar-carbon gray iron, and aluminum-silicon.

21. The method as claimed in claim 18 , wherein a kinetic energy of the spray particles causes the spray particles to adhere to the damaged site.

Assignees

• Heinrichsdorff Frank
• Krüger Ursus
• Reiche Ralph
• Stier Oliver
• Siemens Ag

Inventors

• Heinrichsdorff Frank
• Krüger Ursus
• Reiche Ralph
• Stier Oliver

Classifications

• B23K2103/06

  Cast-iron alloys · CPC title

• B23K26/352

  for surface treatment · CPC title

• C23C24/04

  Impact or kinetic deposition of particles · CPC title

• B23K26/127

  in an enclosure · CPC title

• B23P6/04 Primary

  Repairing fractures or cracked metal parts or products, e.g. castings · CPC title