Plate glass production device, and plate glass production method

Patent metadata

Field	Value
Publication number	US-9352995-B2
Application number	US-201414453476-A
Country	US
Kind code	B2
Filing date	Aug 6, 2014
Priority date	Feb 8, 2012
Publication date	May 31, 2016
Grant date	May 31, 2016

Abstract

Provided is an apparatus for producing a sheet glass, including: a forming device that forms a glass ribbon by allowing molten glass continuously supplied onto molten metal in a bath to flow on the molten metal; a rotary roll disposed in an outer vicinity of the bath and configured to draw the glass ribbon obliquely upward from the molten metal; and a supporting device supporting the rotary roll from below.

First claim

The invention claimed is:

1. A method for producing a sheet glass, the method comprising:
a step of forming a glass ribbon by allowing molten glass continuously supplied onto molten metal in a bath to flow on the molten metal;
a step of drawing the glass ribbon obliquely upward from the molten metal by using a rotary roll disposed in an outer vicinity of the bath; and
a step of placing a leading edge portion of the glass ribbon onto the rotary roll,
wherein the rotary roll is supported from below,
wherein the rotary roll is floated on a liquid in an auxiliary bath provided adjacent to the bath and is supported with the liquid and
wherein the rotary roll is vertically movable in accordance with a change of a liquid level due to an increase or a decrease of an amount of the liquid in the auxiliary bath.

2. The method for producing a sheet glass according to claim 1 , further comprising a step of reducing an amount of the liquid in the auxiliary bath to lower the rotary roll with respect to the bath before a leading edge portion of the glass ribbon is placed onto the rotary roll.

3. The method for producing a sheet glass according to claim 1 , further comprising a step of increasing the amount of the liquid in the auxiliary bath to elevate the rotary roll with respect to the bath after the leading edge portion of the glass ribbon is placed onto the rotary roll.

4. The method for producing a sheet glass according to claim 1 , wherein the liquid is molten metal.

5. The method for producing a sheet glass according to claim 4 , wherein an atmosphere above the molten metal in the auxiliary bath is a reducing atmosphere.

6. The method for producing a sheet glass according to claim 1 , wherein the rotary roll is formed from carbon, silicon carbide, or silica.

7. The method for producing a sheet glass according to claim 1 , wherein the sheet glass is composed of an alkali-free glass containing, as represented by mass percentage on the basis of oxides, SiO 2 : 50 to 66%; Al 2 O 3 : 10.5 to 24%; B 2 O 3 : 0 to 12%; MgO: 0 to 8%; CaO: 0 to 14.5%; SrO: 0 to 24%; BaO: 0 to 13.5%; and ZrO 2 : 0 to 5%, wherein MgO+CaO+SrO+BaO is 9 to 29.5%.

8. The method for producing a sheet glass according to claim 7 , wherein the sheet glass is composed of an alkali-free glass containing, as represented by % by mass based on oxides, SiO 2 : 58 to 66%; Al 2 O 3 : 15 to 22%; B 2 O 3 : 5 to 12%; MgO: 0 to 8%; CaO: 0 to 9%; SrO: 3 to 12.5%; and BaO: 0 to 2%, wherein MgO+CaO+SrO+BaO is 9 to 18%.

Assignees

• Asahi Glass Co Ltd

Inventors

• Iga Motoichi

Classifications

• C03B18/06

  using mechanical means, e.g. restrictor bars, edge rollers · CPC title

• C03C3/093

  containing zinc or zirconium · CPC title

• C03B18/20

  Composition of the atmosphere above the float bath; Treating or purifying the atmosphere above the float bath · CPC title

• C03B18/02

  Forming sheets · CPC title

• C03B2225/02

  Means for positioning, aligning or orientating the sheets during their travel, e.g. stops · CPC title