Method for producing a molded part from a carbon material using recycled carbon fibers and molded part

Patent metadata

Field	Value
Publication number	US-9352967-B2
Application number	US-201213571635-A
Country	US
Kind code	B2
Filing date	Aug 10, 2012
Priority date	Feb 10, 2010
Publication date	May 31, 2016
Grant date	May 31, 2016

Abstract

A method produces a molded part from carbon containing carbon fibers in an amount of less than 20% by weight. The method includes comminuting waste parts or scrap parts formed from a carbon fiber-reinforced synthetic material, a carbon fiber reinforced carbon or a carbon fiber reinforced concrete. A mixture is produced from the comminuted product, a binder such as pitch, a carbon material such as coke and optionally one or more additives, wherein the mixture contains less than 20% by weight of fibers. The mixture is molded into a molded part and the molded part is carbonized. Optionally, the molded carbonized part is impregnated with an impregnating agent. Finally and optionally, the molded carbonized part or the molded part impregnated part is graphitized.

First claim

The invention claimed is:

1. A method for manufacturing a molded part formed from carbon containing a quantity of less than 20% by weight of carbon fibers, which comprises the following steps:
a) comminuting parts selected from the group consisting of waste parts formed from a carbon fiber-reinforced composite material or scrap parts formed from a carbon fiber-reinforced composite material resulting in a comminuted product, releasing a matrix and the carbon fibers of the carbon fiber-reinforced composite material from each other during or after the comminuting step, wherein a release of the matrix from the carbon fibers being accomplished by contacting the parts with an acid, a caustic substance or a solvent;
b) producing a mixture from the comminuted product, a binder, and a carbon material, wherein the mixture contains less than 20% by weight of the carbon fibers;
c) molding the mixture into the molded part; and
d) carbonizing the molded part.

2. The method according to claim 1 , which further comprises selecting the parts from the group consisting of a carbon fiber reinforced synthetic material, a carbon fiber reinforced carbon, a carbon fiber reinforced concrete and a mixture of at least two of the above-identified materials.

3. The method according to claim 2 , which further comprises carrying out the step of comminuting the parts in one of a shredder, a cutting mill, an impact mill or a hammer mill.

4. The method according to claim 1 , which further comprises:
comminuting the parts of the carbon fiber reinforced composite material in step a) to particles with a length in a range 1 to 100 mm; and
screening dust out of the comminuted product so that the comminuted product of step a) has less than 5% by weight of dust particles with a mean particle size of less than 100 μm during or after the comminuting step.

5. The method according to claim 1 , which further comprises separating the matrix from the carbon fibers of the carbon fiber-reinforced composite material before or after the comminuting step, wherein separation of the matrix from the carbon fibers is carried out by screening or sifting.

6. The method according to claim 5 , which further comprises carrying out the sifting with a shifter selected from the group consisting of a rotary sifter, a pneumatic sifter and a zigzag sifter.

7. The method according to claim 1 , which further comprises:
selecting the binder from a compound selected from the group consisting of phenolic resins, pitches, furan resins, phenyl esters and any mixture of at least two of the above identified compounds; and
selecting the carbon material from the group consisting of coke, pitch coke, metallurgical coke, petcoke, and needle coke, and a ratio in the mixture between the carbon material and the binder is in a range 5:1 to 2:1.

8. The method according to claim 7 , which further comprises setting the ratio in the mixture between the carbon material and the binder to be 4:1.

9. The method according to claim 1 , which further comprises adjusting a fiber content of the mixture to be less than 15% by weight.

10. The method according to claim 1 , which further comprises:
impregnating the molded part with an impregnating agent; and
graphitizing the molded part, wherein the graphitizing is carried out at a temperature in a range 1800° C. to 3000° C.

11. The method according to claim 10 , which further comprises:
impregnating the molded part with impregnating pitch as the impregnating agent; and
carrying out the graphitizing in a range of 2300° C. to 2700° C.

12. The method according to claim 1 , which further comprises carbonizing the parts formed from carbon fiber-reinforced composite material before carrying out step a).

13. The method according to claim 1 , which further comprises providing the mixture with at least one additive.

14. The method according to claim 1 , which further comprises adjusting a fiber content of the mixture to be less than 10% by weight.

15. The method according to claim 1 , which further comprises adjusting a fiber content of the mixture to less be than 5% by weight.

16. The method according to claim 1 , which further comprises adjusting a fiber content of the mixture to be less than 3% by weight.

17. The method according to claim 1 , which further comprises carbonizing the parts formed from carbon fiber-reinforced composite material after the comminuting step a) but before step b).

18. A method for manufacturing a molded part formed from carbon containing a quantity of less than 20% by weight of carbon fibers, which comprises the following steps:
a) comminuting parts selected from the group consisting of waste parts formed from a carbon fiber-reinforced composite material or scrap parts formed from a carbon fiber-reinforced composite material resulting in a comminuted product;
b) performing an oxidative treatment on the comminuted product, wherein the oxidative treatment is performed in an aqueous bath containing an oxidizing agent, an anodic oxidation is carried out in an aqueous bath containing an electrolyte or the oxidation is carried out in a gas stream containing an oxidizing agent;
c) producing a mixture from the comminuted product, a binder, and a carbon material, wherein the mixture contains less than 20% by weight of the carbon fibers;
d) molding the mixture into the molded part; and
e) carbonizing the molded part.

19. A method for manufacturing a molded part formed from carbon containing a quantity of less than 20% by weight of carbon fibers, which comprises the following steps:
a) comminuting parts selected from the group consisting of waste parts formed from a carbon fiber-reinforced carbon and scrap parts formed from a carbon fiber-reinforced carbon resulting in comminuted product and oxidizing the comminuted product, releasing a matrix and the carbon fibers of the carbon fiber-reinforced composite material from each other during or after the comminuting step, wherein a release of the matrix from the carbon fibers being accomplished by contacting the parts with an acid, a caustic substance or a solvent;
b) producing a mixture from the comminuted product obtained in step a), pitch, coke and at least one additive, wherein the mixture contains less than 20% by weight of the carbon fibers;
c) molding the mixture obtained in step b) into the molded part;
d) carbonizing the molded part obtained in step c);
e) impregnating the molded part carbonized in step d) with an impregnating agent; and
f) graphitizing the molded part impregnated in step e).

20. A method for manufacturing a molded part formed from carbon containing a quantity of less than 20% by weight of carbon fibers, which comprises the following steps:
a) comminuting parts selected from the group consisting of waste parts formed from a carbon fiber-reinforced carbon and scrap parts formed from a carbon fiber-reinforced carbon resulting in a comminuted product, oxidizing the comminuted product, and releasing a matrix and the carbon fibers of the carbon fiber-reinforced composite material from each other during or after the comminuting step, wherein a release of the matrix from the carbon fibers being accomplished by contacting the parts with an acid, a caustic substance or a solvent;
b) producing a mixture from the comminuted product, pitch, coke and at least one additive, wherein the mixture contains less than 20% by weight of the carbon fibers;
c) molding the mixture into the molded part;
d) carbonizing the molded part;
e) impregnating the molded part carbonized wi

Assignees

• Christ Martin
• Öttinger Oswin
• Bode Reiner
• Prefontaine Alain
• Schwaiger Georg
• Sgl Carbon Se

Inventors

• Christ Martin
• Öttinger Oswin
• Bode Reiner
• Prefontaine Alain
• Schwaiger Georg

Classifications

• C04B2235/616

  Liquid infiltration of green bodies or pre-forms · CPC title

• C04B35/83

  Carbon fibres in a carbon matrix · CPC title

• C04B2235/6021

  Extrusion moulding · CPC title

• C04B35/532

  containing a carbonisable binder · CPC title

• C04B2235/9607

  Thermal properties, e.g. thermal expansion coefficient · CPC title