Negative electrode for nonaqueous electrolyte secondary cell, method of manufacturing the same, and nonaqueous electrolyte secondary cell

Patent metadata

Field	Value
Publication number	US-9350023-B2
Application number	US-86221010-A
Country	US
Kind code	B2
Filing date	Aug 24, 2010
Priority date	Sep 3, 2009
Publication date	May 24, 2016
Grant date	May 24, 2016

Abstract

A negative electrode for a nonaqueous electrolyte secondary cell, includes: a negative electrode active material layer containing a negative electrode active material, a polyvinylidene fluoride component including polyvinylidene fluoride and/or a derivative having polyvinylidene fluoride as a main chain, a styrene-butadiene component including a styrene-butadiene polymer and/or a derivative having a styrene-butadiene polymer as a main chain, a nonionic surfactant having an HLB of 10 to 15, and N-methylpyrrolidone; and a foil-shaped negative electrode current collector provided with the negative electrode active material layer on at least one principal surface of the collector.

First claim

The invention is claimed as follows:

1. A negative electrode for a nonaqueous electrolyte secondary cell, comprising:
a negative electrode active material layer containing a negative electrode active material, (A) a polyvinylidene fluoride component including polyvinylidene fluoride and/or a derivative having polyvinylidene fluoride as a main chain, (B) a styrene-butadiene component including a styrene-butadiene polymer and/or a derivative having a styrene-butadiene polymer as a main chain, and (C) a nonionic surfactant having a hydrophile-lipophile balance of 10 to 15; and
a foil-shaped negative electrode current collector provided with the negative electrode active material layer on at least one principal surface of the collector,
wherein the negative electrode active material layer is formed using a dispersion based mainly on N-methylpyrrolidone.

2. The negative electrode according to claim 1 , wherein the negative electrode active material layer further contains (E) a hydrophobic cellulose component including methyl cellulose and/or hydroxycellulose.

3. The negative electrode according to claim 1 , wherein the nonionic surfactant (C) is at least one selected from the group including polyoxyalkylene alkyl ethers, polyoxyalkylene alkylphenyl ethers, and polyoxyalkylene branched decyl ethers.

4. A nonaqueous electrolyte secondary cell comprising:
a positive electrode having a foil-shaped positive electrode current collector provided with a positive electrode active material layer on at least one principal surface of the positive electrode current collector;
a negative electrode having a foil-shaped negative electrode current collector provided with a negative electrode active material layer on at least one principal surface of the negative electrode current collector;
a separator for avoiding contact between the positive electrode and the negative electrode; and
a nonaqueous electrolyte solution operable to take part in electrode reactions on the positive electrode and the negative electrode,
wherein the negative electrode active material layer contains a negative electrode active material, (A) a polyvinylidene fluoride component including polyvinylidene fluoride and/or a derivative having polyvinylidene fluoride as a main chain, (B) a styrene-butadiene component including a styrene-butadiene polymer and/or a derivative having a styrene-butadiene polymer as a main chain, and (C) a nonionic surfactant having a hydrophile-lipophile balance of 10 to 15,
wherein the negative electrode active material layer is formed using a dispersion based mainly on N-methylpyrrolidone.

5. The negative electrode according to claim 1 , wherein the negative electrode active material is a carbonaceous material.

6. The negative electrode according to claim 1 , wherein a total amount of the polyvinylidene fluoride component and the styrene-butadiene component ranges from 1.5 parts by weight to 5 parts by weight based on 100 parts by weight of the negative electrode active material.

7. The negative electrode according to claim 1 , wherein a mixing ratio of a weight of the polyvinylidene fluoride component to a weight of the styrene-butadiene component ranges from 9.5/0.5 to 2/8.

8. The negative electrode according to claim 1 , wherein an amount of the nonionic surfactant having a hydrophile-lipophile balance of 10 to 15 ranges from 0.2 parts by weight to 1.5 parts by weight based on 100 parts by weight of the negative electrode active material.

9. The negative electrode according to claim 1 , wherein a volume density of the negative electrode is about 1.9 g/cc to about 1.95 g/cc.

10. The nonaqueous electrolyte secondary cell according to claim 4 , wherein a volume density of the negative electrode is about 1.9 g/cc to about 1.95 g/cc.

11. The nonaqueous electrolyte secondary cell according to claim 4 , wherein a thickness of the separator is approximately 25 μm.

12. The negative electrode according to claim 1 , wherein the negative electrode active material layer is formed using the styrene-butadiene component in a state of a water-soluble dispersion.

13. The negative electrode according to claim 1 , wherein the nonionic surfactant having a hydrophile-lipophile balance of 10 to 15 comprises at least one selected from the group consisting of: polyoxyethylene isodecyl ether, polyoxyalkylene isotridecyl ether, polyoxyethylene isotridecyl ether, and polyoxyethylene alkylphenyl ether, and polyoxyalkylene alkyl ether.

Assignees

• Nakamura Toshikazu
• Tsujimoto Hisashi
• Obana Yoshiaki
• Sony Corp

Inventors

• Nakamura Toshikazu
• Tsujimoto Hisashi
• Obana Yoshiaki

Classifications

• H01M4/1391

  of electrodes based on mixed oxides or hydroxides, or on mixtures of oxides or hydroxides, e.g. LiCoOx · CPC title

• Y02P70/54

  Cross-Sectional Technologies · mapped topic

• H01M4/621 Primary

  Binders · CPC title

• H01M4/0404

  by coating on electrode collectors · CPC title

• H01M4/623

  fluorinated polymers · CPC title