Flexible visor having anti-fogging properties and anti-fogging coating compositions

Patent metadata

Field	Value
Publication number	US-9346974-B2
Application number	US-201414314241-A
Country	US
Kind code	B2
Filing date	Jun 25, 2014
Priority date	Jun 25, 2013
Publication date	May 24, 2016
Grant date	May 24, 2016

Abstract

The present disclosure is directed to transparent composites having anti-fogging properties and anti-fog coating compositions for providing anti-fogging properties. The anti-fogging layers can contain an adhesive polymer, a hard polymer, and a hydrophilic polymer, wherein the adhesive polymer, hard polymer, and hydrophilic polymers are different. In further embodiments, composites are described including a substrate layer; a first adhesive layer; a first transparent layer; a second adhesive layer; a second transparent layer; and an anti-fog layer.

First claim

What is claimed is:

1. An anti-fog coating composition comprising an adhesive polymer, a hard polymer, and a hydrophilic polymer, wherein the adhesive polymer, hard polymer, and hydrophilic polymer are different, and the hard polymer has an elongation at break of at least 100% as measured according to ASTM D412, and a pencil hardness of at least 2H as measured according to ASTM D3363.

2. The anti-fog coating composition according to claim 1 , wherein the adhesive polymer comprises a polymer having a Tg of less than about 45 degrees Celsius; and wherein the hydrophilic polymer comprises a polymer having a backbone and hydrophilic segments covalently bonded to the backbone.

3. The anti-fog coating composition according to claim 1 , wherein the hydrophilic polymer comprises a polymer having a polyurethane backbone and hydrophilic segments covalently bonded to the polyurethane backbone wherein the hydrophilic segments comprise alkylene oxides, lactones, lactams, or combinations thereof.

4. The anti-fog coating composition according to claim 1 , wherein:
the hydrophilic polymer is present in the anti-fog coating composition in an amount within a range of about 10 wt % to about 90 wt % based on the total dry weight of the anti-fog coating composition;
the hard polymer is present in the anti-fog coating composition in an amount within a range of about 10 wt % to about 80 wt % based on the total dry weight of the anti-fog coating composition; and
the adhesive polymer is present in the anti-fog coating composition in an amount within a range of about 10 wt % to about 80 wt % based on the total dry weight of the anti-fog coating composition.

5. The anti-fog coating composition according to claim 1 , wherein the hard polymer comprises a polymer or interpolymer prepared from ethylenically unsaturated monomers comprising styrene, styrene derivatives, acrylic acid or its derivate, methacrylic acid or its derivate, olefins, (meth)acrylonitriles, itaconic acid and its derivatives, maleic acid and its derivatives, vinyl halides, vinylidene halides, fluoropolymers, or combinations thereof.

6. The anti-fog coating composition according to claim 1 , wherein the adhesive polymer comprises a polyester or a polyurethane.

7. The anti-fog coating composition according to claim 1 , wherein the anti-fog coating composition further comprises a crosslinker.

8. A transparent composite comprising:
a substrate layer; and
an anti-fog layer, wherein the anti-fog layer comprises an adhesive polymer, a hard polymer, and a hydrophilic polymer, wherein the adhesive polymer, hard polymer, and hydrophilic polymers are different, and the hard polymer has an elongation at break of at least 100% as measured according to ASTM D412, and a pencil hardness of at least 2H as measured according to ASTM D3363.

9. The transparent composite according to claim 8 , wherein the transparent composite further comprises:
a first adhesive layer;
a first transparent layer;
a second adhesive layer; and
a second transparent layer.

10. The transparent composite according to claim 8 , wherein the transparent composite is in the form of personal protective equipment.

11. The transparent composite according to claim 9 , wherein a peel strength between the first transparent layer and substrate layer is at least about 2 pounds per linear inch (PLI) as measured according to ASTM D1876.

12. The transparent composite according to claim 8 , wherein the anti-fog layer is non-tacky as determined by folding the layer over itself, separating the layer, and observing if the layer stuck to itself.

13. The transparent composite according to claim 8 , wherein
the anti-fog layer comprises an anti-blocking agent comprising a colloidal silica present in the anti-fog layer in a range of from about 3 wt. % to about 40 wt. % based on the total weight of the anti-fog layer; and/or
wherein the anti-fog layer comprises an anti-blocking agent comprising a fluorinated anionic surfactant present in the anti-fog layer in an amount in a range of from about 0.01 wt. % to about 10 wt. % based on the total weight of the anti-fog layer.

14. The transparent composite according to claim 8 , wherein the adhesive polymer comprises a polymer having a Tg of less than about 45 degrees Celsius; and wherein the hydrophilic polymer comprises a polymer having a backbone and hydrophilic segments covalently bonded to the backbone.

15. The transparent composite according to claim 8 , wherein:
the hydrophilic polymer is present in the anti-fog layer in an amount within a range of about 10 wt % to about 90 wt % based on the total dry weight of the anti-fog layer;
the hard polymer is present in the anti-fog layer in an amount within a range of about 10 wt % to about 80 wt % based on the total dry weight of the anti-fog layer; and
the adhesive polymer is present in the anti-fog layer in an amount within a range of about 10 wt % to about 80 wt % based on the total dry weight of the anti-fog layer.

16. The transparent composite according to claim 8 , wherein the hydrophilic polymer comprises a polymer having a polyurethane backbone and hydrophilic segments covalently bonded to the polyurethane backbone wherein the hydrophilic segments comprise alkylene oxides, lactones, lactams, or combinations thereof.

17. The transparent composite according to claim 8 , wherein the hard polymer comprises a polymer or interpolymer prepared from ethylenically unsaturated monomers comprising styrene, styrene derivatives, acrylic acid or its derivate, methacrylic acid or its derivate, olefins, (meth)acrylonitriles, itaconic acid and its derivatives, maleic acid and its derivatives, vinyl halides, vinylidene halides, fluoropolymers, or combinations thereof.

18. The transparent composite according to claim 8 , wherein the adhesive polymer comprises a polyester or a polyurethane.

19. The transparent composite according to claim 8 , wherein the anti-fog layer further comprises a crosslinker.

Assignees

• Saint Gobain Performance Plast

Inventors

• Majumdar Debasis
• Hirschey Ryan C
• Russo John P
• Buss Gerard T

Classifications

• B32B2250/24

  All layers being polymeric · CPC title

• B32B2250/246

  All polymers belonging to those covered by groups B32B27/32 and B32B27/30 · CPC title

• C09D175/04 Primary

  Polyurethanes · CPC title

• B32B7/12

  using interposed adhesives or interposed materials with bonding properties · CPC title

• B32B2551/00

  Optical elements · CPC title