Bulk annealing of glass sheets

Patent metadata

Field	Value
Publication number	US-9340443-B2
Application number	US-201314047251-A
Country	US
Kind code	B2
Filing date	Oct 7, 2013
Priority date	Dec 13, 2012
Publication date	May 17, 2016
Grant date	May 17, 2016

Abstract

Surface modification layers and associated heat treatments, that may be provided on a sheet, a carrier, or both, to control both room-temperature van der Waals (and/or hydrogen) bonding and high temperature covalent bonding between the thin sheet and carrier. The room-temperature bonding is controlled so as to be sufficient to hold the thin sheet and carrier together during vacuum processing, wet processing, and/or ultrasonic cleaning processing, for example. And at the same time, the high temperature covalent bonding is controlled so as to prevent a permanent bond between the thin sheet and carrier during high temperature processing, as well as maintain a sufficient bond to prevent delamination during high temperature processing.

First claim

What is claimed is:

1. A method of annealing glass sheets, comprising:
stacking a plurality of glass sheets, each of the glass sheets having two major surfaces, so that interfaces are defined between adjacent ones of the glass sheets in the plurality of glass sheets, wherein there is disposed on at least one of the major surfaces that faces one of the interfaces, a surface modification layer, wherein the surface modification layer is one of HMDS, a plasma polymerized fluoropolymer, and an aromatic silane; and
exposing the stack of glass sheets to a time-temperature cycle sufficient to compact each of the glass sheets, wherein the time-temperature cycle includes a temperature ≧400° C., but less than the strain point of the glass sheets,
wherein the surface modification layer is sufficient to control, throughout the time-temperature cycle, bonding between the adjacent ones of the glass sheets in the stack defining the one of the interfaces, wherein bonding is controlled to be of such a force so that one sheet does not separate from another if one is held and the other subjected to the force of gravity, but so that the sheets may be separated without breaking one of the adjacent ones of the glass sheets into two or more pieces.

2. The method of claim 1 , wherein the time-temperature cycle includes a temperature ≧600° C., but less than the strain point of the glass sheets.

3. The method of claim 1 , wherein the surface modification layer comprises a plasma polymerized fluoropolymer, and is one of: plasma polymerized polytetrafluroethylene; and a plasma polymerized fluoropolymer surface modification layer deposited from a CF4-C4F8 mixture having ≦40% C4F8.

4. The method of claim 1 , wherein the surface modification layer comprises an aromatic silane, and is a phenyl silane.

5. The method of claim 1 , wherein the surface modification layer comprises an aromatic silane, and is one of: phenyltriethoxysilane; diphenyldiethoxysilane; and 4-pentafluorophenyltriethoxysilane.

6. The method of claim 1 , wherein the time-temperature cycle is carried out in an oxygen-free environment.

7. The method of claim 1 , wherein the at least one of the major surfaces having the surface modification layer thereon has a surface energy of ≧40 mJ/m 2 .

8. The method of claim 1 , adhesion energy between the major surfaces of the sheets facing the one of the interfaces is greater than about 24 mJ/m 2 .

9. The method of claim 1 , adhesion energy between the major surfaces of the sheets facing the one of the interfaces is from 50 to 1000 mJ/m 2 .

10. A method of annealing glass sheets, comprising:
stacking a plurality of glass sheets, each of the glass sheets having two major surfaces, so that interfaces are defined between adjacent ones of the glass sheets in the plurality of glass sheets, wherein there is disposed on at least one of the major surfaces that faces one of the interfaces, a surface modification layer, wherein the surface modification layer is comprises an aromatic silane, and is a phenyl silane; and
exposing the stack of glass sheets to a time-temperature cycle sufficient to compact each of the glass sheets,
wherein the surface modification layer is sufficient to control, throughout the time-temperature cycle, bonding between the adjacent ones of the glass sheets in the stack defining the one of the interfaces, wherein bonding is controlled to be of such a force so that one sheet does not separate from another if one is held and the other subjected to the force of gravity, but so that the sheets may be separated without breaking one of the adjacent ones of the glass sheets into two or more pieces.

11. The method of claim 10 , wherein the time-temperature cycle includes a temperature ≧400° C., but less than the strain point of the glass sheets.

12. The method of claim 1 , adhesion energy between the major surfaces of the sheets facing the one of the interfaces is greater than about 24 mJ/m 2 .

13. The method of claim 1 , adhesion energy between the major surfaces of the sheets facing the one of the interfaces is from 50 to 1000 mJ/m 2 .

14. A method of annealing glass sheets, comprising:
stacking a plurality of glass sheets, each of the glass sheets having two major surfaces, so that interfaces are defined between adjacent ones of the glass sheets in the plurality of glass sheets, wherein there is disposed on at least one of the major surfaces that faces one of the interfaces, a surface modification layer, wherein the surface modification layer comprises an aromatic silane, and is one of: phenyltriethoxysilane; diphenyldiethoxysilane; and 4-pentafluorophenyltriethoxysilane; and
exposing the stack of glass sheets to a time-temperature cycle sufficient to compact each of the glass sheets,
wherein the surface modification layer is sufficient to control, throughout the time-temperature cycle, bonding between the adjacent ones of the glass sheets in the stack defining the one of the interfaces, wherein bonding is controlled to be of such a force so that one sheet does not separate from another if one is held and the other subjected to the force of gravity, but so that the sheets may be separated without breaking one of the adjacent ones of the glass sheets into two or more pieces.

15. The method of claim 14 , wherein the time-temperature cycle includes a temperature ≧400° C., but less than the strain point of the glass sheets.

16. The method of claim 14 , adhesion energy between the major surfaces of the sheets facing the one of the interfaces is greater than about 24 mJ/m 2 .

17. The method of claim 14 , adhesion energy between the major surfaces of the sheets facing the one of the interfaces is from 50 to 1000 mJ/m2.

Assignees

• Corning Inc

Inventors

• Bellman Robert Alan
• Bookbinder Dana Craig
• Manley Robert George
• Mazumder Prantik
• Chang Theresa
• Domey Jeffrey John
• Stephens Ii Alan Thomas

Classifications

• B32B17/06

  comprising glass as the main or only constituent of a layer, next to another layer of a specific {material} · CPC title

• C03C17/328

  Polyolefins · CPC title

• C03C1/00

  Ingredients generally applicable to manufacture of glasses, glazes, or vitreous enamels · CPC title

• C03B40/005 Primary

  Fabrics, felts or loose covers · CPC title

• C03B25/025 Primary

  Glass sheets · CPC title