Broadband multi-mode optical fibers with flat-zone in dopant concentration profile

Patent metadata

Field	Value
Publication number	US-9329335-B2
Application number	US-201514725315-A
Country	US
Kind code	B2
Filing date	May 29, 2015
Priority date	Jan 31, 2014
Publication date	May 3, 2016
Grant date	May 3, 2016

Abstract

Described is a design approach to fabricating broadband graded-index multimode fibers where the concentration profile of at least one dopant in the core region includes at least one flat-zone. Designs for use in CWDM applications are also disclosed.

First claim

What is claimed is:

1. A broadband multimode optical fiber comprising:
a core region having a transverse cross-section and a longitudinal axis, said core region being configured for broadband operation at wavelengths λ within a predetermined wavelength range, Λ, and
a cladding region surrounding said core region,
said core and cladding regions being configured to support the propagation of optical radiation in said core region and along said axis simultaneously in a plurality of transverse modes,
said core region having a refractive index profile n(r, λ) and being co-doped with a plurality of dopants each having a concentration profile, the concentrations and distributions of said dopants being radially varied within said transverse cross-section of said core region so that the refractive index of said core region is radially graded and so that variations in z(r, λ) with respect to wavelength are reduced, where
z ( r ,λ) n 2 ( r ,λ) k 0 2 ,

r is radius, λ is the wavelength of said optical radiation, n is the refractive index of said core region, k 0 =2π/λ is the wave number, and
wherein the concentration profile of at least one of said dopants has at least one flat-zone where the concentration of said at least one dopant is essentially constant with radius within said at least one zone.

2. The fiber of claim 1 , wherein said core region has a radius r=a, and said at least one flat-zone extends from said axis over a radial distance from r=0 to r=r 1 <<a.

3. The fiber of claim 1 , wherein said core region has a radius r=a, and said at least one flat-zone extends from r a over a radial distance to r=r 2 , where r 2 <a.

4. The fiber of claim 1 , wherein the concentration of said at least one dopant is essentially constant with radius within said at least one zone in that the magnitude of said concentration does not vary by more than approximately ±0.1 mole % within said at least one zone when the concentration level of said at least one dopant is less than approximately 1.0 mole %.

5. The fiber of claim 1 , wherein said fiber is manufactured by a silica glass deposition system in which mass flow controllers control the flow rate of dopant precursors, at least one of said controllers having difficulty controlling said flow rates accurately for a prescribed dopant precursor at low flow rates near or below a particular value, and wherein the concentration profile of the dopant deposited from said prescribed precursor includes said at least one flat zone.

6. The fiber of claim 5 wherein said deposited dopant is selected from the group consisting of fluorine and phosphorus.

7. The fiber of claim 1 , wherein
said fiber comprises silica and is designed for operation in a CWDM system has an NA˜0.2,
said core region is co-doped with Ge, P and F, has a parabolic index profile with α=2.08±0.1, and has a radius r=a=25 μm approximately.

8. The fiber of claim 7 , wherein said P and F dopants are characterized by concentration profiles as follows:
(a) said F concentration profile generally decreases from about 3.0 mole % at r=a=25 μm to about 0.6 mole % at r=0; and said F profile has a flat-zone that extends from r=0 to approximately r=10 μm; and within said F flat-zone said F concentration either remains essentially flat or decreases from r=0 to ˜3<r 1 <˜10 μm and then increases to ˜2.5-3.5 mole % from r 1 to r=a; and
(b) said P concentration profile decreases monotonically from ˜2.5-3.5 mole % to ˜0 mole % from r=0 to r=a.

9. The fiber of claim 7 , wherein said P and F dopants are characterized by concentration profiles as follows:
(a) said F concentration profile generally increases from about 0 mole % at r=a=25 μm to a peak of about 2.8 mole % at r=20 μm and then decreases to about 0.4 mole % at r=0; and said F profile has a flat-zone that extends from r=0 to approximately r=10 μm; and within said F flat-zone said F concentration either remains essentially flat or decreases from r=0 to ˜3<r 1 <˜10 μm, then increases to ˜2.5-4.0 mole % from r 1 to r˜18-22 μm, and then decreases to zero or decreases to a second flat zone from r˜23 μm to r=a=25 μm; and
(b) said P concentration profile decreases monotonically from ˜1.0-3.5 mole % at r=0 to ˜0.1 mole % at r˜18-22 μm, then increases monotonically to ˜0.4-1.0 mole % at r=22-24 μm, and finally decreases monotonically to an approximate value between 0-1.0 mole % at r=a=25 μm.

10. A method of making a broadband multimode optical fiber comprising the steps of:
forming a core region having a transverse cross-section and a longitudinal axis, said core region being configured for broadband operation at wavelengths λ, within a predetermined wavelength range, Λ,
forming a cladding region surrounding said core region,
forming said core and cladding regions so that they are configured to support the propagation of optical radiation in said core region and along said axis simultaneously in a plurality of transverse modes,
said core region having a refractive index profile n(r, λ),
doping said core region with a plurality of dopants each having a concentration profile, the concentrations and distributions of said dopants being radially varied within said transverse cross-section of said core region so that the refractive index of said core region is radially graded and so that variations in z(r, λ) with respect to wavelength are reduced, where
z ( r ,λ) n 2 ( r ,λ) k 0 2 ,

r is radius, λ is the wavelength of said optical radiation, n is the refractive index of said core region, k 0 =2π/λ is the wave number, and
forming the concentration profile of at least one of said dopants so that it has at least one flat-zone where the concentration of said at least one dopant is essentially constant with radius within said at least one zone; and
inputting the dopant concentration profiles to a deposition system that produces an optical fiber preform in which the concentration of each dopant in its core region corresponds to the inputted profiles.

11. The method of claim 10 , wherein said core region is formed to have a radius r=a, and said at least one flat-zone is formed to extend from said axis over a radial distance from r=0 to r=r 1 <<a.

12. The method of claim 10 , wherein said core region is formed to have a radius r=a, and said at least one flat-zone extends from r=a over a radial distance to r=r 2 , where r 2 <a.

13. The method of claim 10 , wherein said doping step is performed so that the concentration of said at least one dopant is essentially constant with radius within said at least one zone in that the magnitude of said concentration does not vary by more than approximately ±0.1 mole % within said at least one zone when the concentration level of said at least one dopant is less than approximately 1.0 mole).

14. The method of claim 10 , further including the step of manufacturing said fiber by by a silica glass deposition system in which mass flow controllers control the flow rate of dopant precursors, at least one of said controllers having difficulty controlling said flow rates accurately for a prescribed dopant precursor at low flow rates near or below a particular value, and wherein the said doping step is performed so that the concentration profile of the dopant deposited from said prescribed precursor includes said at least one flat zone.

15. The method of claim 10 wherein said deposited dopant is selected from the group consisting of fluorine and phosphorus.

16. The method of claim 10 , further including the step of drawing an optical fiber from the preform.

Assignees

• Ofs Fitel Llc

Inventors

• Balemarthy Kasyapa
• Shubochkin Roman
• Vaidya Durgesh S
• Yan Man F

Classifications

• C03B2201/28

  doped with phosphorus · CPC title

• G02B6/0281

  Graded index region forming part of the central core segment, e.g. alpha profile, triangular, trapezoidal core (G02B6/0288, G02B6/0286 take precedence) · CPC title

• C03B2203/26

  Parabolic or graded index [GRIN] core profile · CPC title

• C03B37/027

  Fibres composed of different sorts of glass, {e.g. glass optical fibres}(C03B37/0253, C03B37/028 take precedence) · CPC title

• C03B2201/12

  doped with fluorine (C03B2201/14 takes precedence) · CPC title