Resin for use in a coating composition

Patent metadata

Field	Value
Publication number	US-9328191-B2
Application number	US-201113577128-A
Country	US
Kind code	B2
Filing date	Feb 4, 2011
Priority date	Feb 5, 2010
Publication date	May 3, 2016
Grant date	May 3, 2016

Abstract

A coating system comprises a substrate and a cured film disposed on the substrate and formed from a coating composition. The coating composition comprises a solvent component and a resin. The resin comprises a reaction product of a polyolefin and an oligomer or polymer. The polyolefin, different from the oligomer or polymer, has a functional group that is reactive with the oligomer or polymer and the functional group is selected from acrylate, methacrylate, carboxyl, hydroxyl, epoxide, anhydride and isocyanate functional groups. The oligomer or polymer and the polyolefin are at least partially immiscible in solution at ambient temperature. The oligomer or polymer is grafted with the polyolefin to form the resin.

First claim

What is claimed is:

1. A resin comprising a reaction product of:
an oligomer or polymer comprising an acrylic having a number average molecular weight of from 2,500 to 4,000 g/mol, said oligomer or polymer having reactive functionality thereon selected from hydroxyl, carboxyl, anhydride, isocyanate, and epoxide functional groups; and
a polyolefin that is different from said oligomer or polymer and having a functional group selected from acrylate, methacrylate, carboxyl, hydroxyl, epoxide, anhydride and isocyanate functional groups, the polyolefin having a number average molecular weight of from 350 to 700 g/mol;
wherein said functional group of said polyolefin is reactive with said reactive functionality of said oligomer or polymer;
wherein said oligomer or polymer and said polyolefin are at least partially immiscible in solution at ambient temperature; and
wherein said polyolefin is reacted in an amount of from 15 to 50 parts by weight and said oligomer or polymer is reacted in an amount of from 50 and 85 parts by weight, based on 100 parts by weight of the components utilized to form said resin.

2. A resin as set forth in claim 1 wherein said oligomer or polymer has a first polarity and said polyolefin has a second polarity that is opposite said first polarity.

3. A resin as set forth in claim 1 wherein said polyolefin is selected from polyethylene, polypropylene, polybutylene, and combinations thereof.

4. A resin as set forth in claim 1 wherein said polyolefin is a crystalline polyalkylene.

5. A resin as set forth in claim 1 wherein said oligomer or polymer is produced from monomers selected from methyl methacrylate, butyl methacrylate, hydroxyethyl methacrylate, hydroxypropyl methacrylate, glycidyl methacrylate, and combinations thereof, and
wherein said oligomer or polymer has reactive functionality thereon selected from hydroxyl, carboxyl, epoxide, anhydride and isocyanate functional groups.

6. A resin as set forth in claim 1 further defined as a graft polymer.

7. A resin as set forth in claim 1 having a glass transition temperature of from −20° C. to 100 C.

8. A resin as set forth in claim 1 , consisting of said reaction product of said oligomer or polymer comprising said acrylic and said polyolefin.

9. A resin comprising a reaction product of:
an oligomer or polymer comprising an acrylic having a number average molecular weight of from 2,500 to 4,000 g/mol, said oligomer or polymer having reactive functionality thereon selected from hydroxyl, carboxyl, epoxide, anhydride, and isocyanate functional groups; and
a crystalline polyalkylene having a functional group selected from carboxyl and hydroxyl functional groups which is reactive with said reactive functionality of said oligomer or polymer, the crystalline polyalkylene having a number average molecular weight of from 350 to 700 g/mol;
wherein said oligomer or polymer and said crystalline polyalkylene are at least partially immiscible in solution at ambient temperature; and
wherein said crystalline polyalkylene is reacted in an amount of from 15 to 50 parts by weight and said oligomer or polymer is reacted in an amount of from 50 and 85 parts by weight, based on 100 parts by weight of the components utilized to form said resin.

10. A resin as set forth in claim 9 wherein said oligomer or polymer has a first polarity and said polyolefin has a second polarity that is opposite said first polarity.

11. A resin as set forth in claim 9 further defined as a graft polymer.

12. A resin as set forth in claim 9 , consisting of said reaction product of said oligomer or polymer comprising said acrylic and said crystalline polyalkylene.

13. A method of forming a resin, said method comprising the steps of:
providing an oligomer or polymer comprising an acrylic having a number average molecular weight of from 2,500 to 4,000 g/mol, the oligomer or polymer having a reactive functionality thereon selected from hydroxyl, carboxyl, anhydride, epoxide and isocyanate functional groups;
providing a polyolefin that is different from the oligomer or polymer which has a functional group that is selected from acrylate, methacrylate, anhydride, carboxyl, hydroxyl, epoxide, and isocyanate functional groups, the polyolefin having a number average molecular weight of from 350 to 700 g/mol; and
grafting the oligomer or polymer with the polyolefin to form the resin;
wherein the functional group of the polyolefin is reactive with the reactive functionality of the oligomer or polymer;
wherein the oligomer or polymer and the polyolefin are at least partially immiscible in solution at ambient temperature; and
wherein the polyolefin is reacted in an amount of from 15 to 50 parts by weight and the oligomer or polymer is reacted in an amount of from 50 and 85 parts by weight, based on 100 parts by weight of the components utilized to form the resin.

14. A method as set forth in claim 13 wherein the oligomer or polymer has a first polarity and the polyolefin has a second polarity that is opposite the first polarity.

15. A method as set forth in claim 13 wherein the polyolefin is reacted in an amount of from 15 to 45 parts by weight based on 100 parts by weight of the components utilized to form the resin.

16. A method as set forth in claim 13 with the method consisting of the steps as recited in claim 13 .

17. A coating system comprising:
a substrate; and
a cured film disposed on said substrate and formed from a coating composition comprising:
a solvent component;
a resin comprising a reaction product of:
an oligomer or polymer comprising an acrylic having a number average molecular weight of from 2,500 to 4,000 g/mol, said oligomer or polymer having reactive functionality thereon selected from hydroxyl, carboxyl, epoxide, anhydride and isocyanate functional groups, wherein said oligomer or polymer optionally comprises functionality for crosslinking; and
a polyolefin that is different from the oligomer or polymer which has a functional group selected from carboxyl, hydroxyl, epoxide, isocyanate, anhydride, acrylate and methacrylate functional groups, the polyolefin having a number average molecular weight of from 350 to 700 g/mol, wherein the functional group of the polyolefin is reactive with the oligomer or polymer;
wherein said oligomer or polymer and said polyolefin are at least partially immiscible in solution at ambient temperature; and
wherein said polyolefin is reacted in an amount of from 15 to 50 parts by weight and said oligomer or polymer is reacted in an amount of from 50 and 85 parts by weight, based on 100 parts by weight of the components utilized to form said resin; and

optionally a crosslinking agent;
wherein said cured film has a gloss of less than 35 gloss units as measured by a glossmeter at 20.

Assignees

• Tye Anthony J
• Rihan Ali A
• Pierce Jeff
• Basf Coatings Gmbh

Inventors

• Tye Anthony J
• Rihan Ali A
• Pierce Jeff

Classifications

• C08L23/0892

  with monomers containing atoms other than carbon, hydrogen or oxygen · CPC title

• C08F299/00

  Macromolecular compounds obtained by interreacting polymers involving only carbon-to-carbon unsaturated bond reactions, in the absence of non-macromolecular monomers · CPC title

• C08L2205/05

  containing polymer components which can react with one another · CPC title

• C08L67/00

  Compositions of polyesters obtained by reactions forming a carboxylic ester link in the main chain (of polyester-amides C08L77/12; of polyester-imides C08L79/08); Compositions of derivatives of such polymers · CPC title

• C08L23/0884

  Epoxide-containing esters · CPC title