Bonded part with laminated rubber member and method of making

Patent metadata

Field	Value
Publication number	US-9327482-B2
Application number	US-201514749181-A
Country	US
Kind code	B2
Filing date	Jun 24, 2015
Priority date	Jun 30, 2009
Publication date	May 3, 2016
Grant date	May 3, 2016

Abstract

A method of forming a bonded part with a press-fit, vulcanized rubber member residing in compression between two rigid members and bonded thereto. The rubber member is a laminate with a core layer between two self-bonding rubber layers. The bonded part may be, for example, a vibration damper, isolator or absorber. The core layer and the self-bonding layers may have the same primary elastomer and cure system type, and the self-bonding layers have an adhesion promoter not present in the core layer. The adhesive layers may be from 0.05 to 1 mm thick or from 5% to 10% of the laminate thickness.
The method includes forming a rubber core layer, curing it, applying a rubber adhesive layer on each side to form a laminate, inserting the laminate between two rigid members under compression, and post-curing to form a bonded part. The adhesive layers may be partially cured before inserting.

First claim

What is claimed is:

1. A method comprising:
(a) forming a rubber core layer from an elastomer composition comprising a primary elastomer and a cure system;
(b) curing said core layer at least 80% of full cure according to ASTM D-5289 or equivalent test method;
(c) applying a self-bonding rubber adhesive layer on each side of said cured core layer to form a rubber laminate;
(d) inserting said rubber laminate between two rigid members where it resides under compression to form a composite article; and
(e) post-curing said composite article to cure the self-bonding rubber layer and to effect a bond between the self-bonding rubber layers and the rigid members and to effect a bond between the self-bonding rubber layers and the core layer, thus forming a bonded part;
wherein each self-bonding rubber adhesive layer is cured to no more than 70% of full cure according to ASTM D-5289 or equivalent method before said inserting.

2. The method of claim 1 wherein the extent of said curing of said core layer in step (b) is 100% of full cure according to ASTM D-5289 or equivalent test method.

3. The method of claim 1 wherein the extent of said curing of said core layer in step (b) is substantially fully cured.

4. The method of claim 1 wherein each adhesive layer is 0.05 mm to 1.0 mm in thickness.

5. The method of claim 1 wherein each adhesive layer is from about 5% to about 10% of the total laminate thickness.

6. The method of claim 1 wherein each adhesive layer is applied under pressure and then partially cured to from 30% to 80% of full cure before said inserting step.

7. The method of claim 1 wherein said applying is by extrusion coating with a self-bonding rubber composition.

8. The method of claim 1 wherein said forming and said applying is by co-extrusion.

9. The method of claim 1 wherein said applying is by an insert molding process selected from the group consisting of injection molding, compression molding, and transfer molding and includes partially curing the adhesive layers to no more than 70% of full cure.

10. The method of claim 1 wherein said applying is by solution coating with a drying step which also partially cures each adhesive layer to no more than 70% of full cure.

11. The method of claim 1 wherein the primary elastomers of the core layer and each adhesive layer are the same type and selected from the group consisting of ethylene-alpha-olefin elastomer, ethylene propylene copolymers (EPM), ethylene propylene diene terpolymers (EPDM), styrene-butadiene rubber (SBR), acrylonitrile butadiene rubber (NBR), natural rubber (NR), ethylene vinyl acetate elastomer (EVM, EAM), epichlorohydrin (ECO), and blends thereof; and wherein cure systems of the core layer and each adhesive layer are compatible and co-cure for adhesion there between; and wherein each adhesive layer comprises an adhesion promoter not present in the core layer.

12. The method of claim 11 wherein the core layer comprises EPDM as the primary elastomer and a peroxide cure system;
and each adhesive layer comprises EPDM as primary elastomer, a peroxide cure system, and a metal salt of an unsaturated organic acid as the adhesion promoter.

13. The method of claim 12 wherein the rigid members are metal members.

14. The method of claim 13 wherein each adhesive layer includes two peroxides with different cure activation temperatures at least 5° C. apart.

Assignees

• Gates Corp

Inventors

• Feng Yuding
• Zhu Lin
• Hodjat Yahya
• Dunlap Paul N

Classifications

• F16F15/1442

  with a single mass · CPC title

• B32B2605/08

  Cars · CPC title

• B32B37/153

  at least one layer is extruded and immediately laminated while in semi-molten state · CPC title

• B32B27/20

  using fillers, pigments, thixotroping agents · CPC title

• B32B15/18

  comprising iron or steel {(B32B15/011, B32B15/012 and B32B15/013 take precedence)} · CPC title