Composite oxide, preparation method for same, and application thereof

Patent metadata

Field	Value
Publication number	US-9314776-B2
Application number	US-201314440096-A
Country	US
Kind code	B2
Filing date	Oct 10, 2013
Priority date	Nov 1, 2012
Publication date	Apr 19, 2016
Grant date	Apr 19, 2016

Abstract

This invention relates to a composite oxide, production and use thereof as a methane selective oxidizing catalyst. The composite oxide has a composition as illustrated by the formula RhR x Mo y V z O δ-α , wherein the symbols are as defined in the specification. When used as a methane selective oxidizing catalyst, the present composite oxide provides a high methane conversion and a high selectivity to the aimed products.

First claim

We claim:

1. A composite oxide, comprising a composition represented by a formula RhR x Mo y V z O δ-α ,
wherein R is Ni, Co or a combination of Ni and Co, x=0-3.0, y=0.1-0.9, z=0.1-0.9, δ is a positive number at which a valency of oxygen in the composite oxide reaches a balance, α is 0 to δ/2,
wherein when R represents the combination of Ni and Co, a molar ratio of Ni:Co is 0.01-20:1.

2. The composite oxide according to claim 1 , further comprising a carrier, wherein a weight ratio of the composite oxide to the carrier is 0.01-1:1, wherein the carrier is one or more inorganic refractory oxide.

3. The composite oxide according to claim 1 , wherein a powder X ray diffraction pattern of the composite oxide in a crystalline form has a peak at a diffraction angle 2 theta of 28.5±0.5°.

4. A process for producing a composite oxide, comprising:
reacting a Rh source, a Mo source, a V source, an optional Ni source, and an optional Co source under reaction conditions to obtain the composite oxide,
wherein an amount of the Rh source, an amount of the Mo source, an amount of the V source, an amount of the Ni source and an amount of the Co source are predetermined such that the composite oxide has a composition as represented by the formula RhR x Mo y V z O δ-α , wherein R is Ni, Co or a combination of Ni and Co, x=0-3.0, y=0.1-0.9, δ is a positive number at which a valency of oxygen in the composite oxide reaches a balance, α is 0, when R represents the combination of Ni and Co, a molar ratio of Ni:Co is 0.01-20:1,
optionally a step of partially reducing the composite oxide so that α ranges from more than 0 to δ/2, and
optionally a step of supporting the composite oxide on a carrier.

5. The process according to claim 4 , wherein the Rh source is one or more selected from the group consisting of water soluble inorganic acid salts and water soluble organic acid salts of Rh, and nitrates and acetates of Rh, the Ni source is one or more selected from the group consisting of water soluble inorganic acid salts and water soluble organic acid salts of Ni, and nitrates and acetates of Ni, the Co source is one or more selected from the group consisting of water soluble inorganic acid salts and water soluble organic acid salts of Co, and nitrates and acetates of Co, the Mo source is one or more selected from the group consisting of water soluble inorganic acid salts, water soluble organic acid salts and ammonium oxometallates of Mo, the V source is one or more selected from the group consisting of water soluble inorganic acid salts, water soluble organic acid salts and ammonium oxometallates of V, the optional carrier is one or more selected from the group consisting of SiO 2 , Al 2 O 3 , MgO—SiO 2 , MgO—Al 2 O 3 , Al 2 O 3 —SiO 2 , CaO—SiO 2 , CaO—MgO—SiO 2 and precursors thereof, and an amount of the carrier is predetermined so that a weight ratio of the composite oxide to the carrier (calculated as the inorganic refractory oxide) is 1-3:1.

6. The process according to claim 4 , wherein the Rh source, the Mo source, the V source, the Ni source and the Co source are each in a form of an aqueous solution, further comprising mixing the Rh source, the Mo source, the V source, optionally the Ni source, and optionally the Co source to form a reaction mixture, subjecting the reaction mixture to coprecipitation to form an aqueous slurry, dehydrating, drying and calcinating the aqueous slurry to obtain the composite oxide.

7. The process according to claim 6 , wherein the reaction mixture is adjusted to a pH value of 3-10 and maintained a reaction temperature of 60-90 degrees Celsius, for a reaction duration of 1-12 h, wherein the drying step is carried out at a drying temperature of 60-150 degrees Celsius for a drying duration of 4-48 h, wherein the calcination step is carried out at a calcination temperature of 400-900 degrees Celsius for a calcination duration of 3-10 h.

8. The process according to claim 6 , wherein the aqueous solution of the Mo source further contains ammonia at a concentration of 1-3 mol/L, and/or the aqueous solution of the V source further contains a C 2-6 polycarboxylic acid at a concentration of 0.1-0.5 mol/L.

9. A process for coproducing ethanol and acetaldehyde by a methane selective oxidation reaction, comprising obtaining a catalyst of claim 1 , contacting methane with the catalyst under a methane selective oxidation reaction condition.

10. The process according to claim 9 , wherein the methane selective oxidation reaction condition comprises a reaction temperature of 300-800 degrees Celsius, a reaction pressure of 0.1-5.0 MPa (gage), a feeding gas composition (by molar) of CH 4 :O 2 :H 2 O=1:0.1-1:0.2-10, and a methane space velocity of 1200-3500 h −1 .

11. A process for coproducing ethanol and acetaldehyde by a methane selective oxidation reaction, comprising:
producing a composite oxide according to the process of claim 4 ,
contacting a feeding gas with the composite oxide at 300-800 degrees Celsius and a pressure of 0.1-5.0 MPa (gage), and
wherein the feeding gas comprises methane, oxygen, and steam at a molar ratio of 1:0.1-1:0.2-10.

12. The composite oxide according to claim 1 , wherein x=0.01-3.0, y=0.2-0.7, z=0.2-0.9, α is 0 to δ/4, when R represents the combination of Ni and Co, the molar ratio of Ni:Co is 0.1-10:1.

13. The composite oxide according to claim 1 , wherein x=0.5-2.5, y=0.4-0.6, z=0.5-0.8, when R represents the combination of Ni and Co, the molar ratio of Ni:Co is 1-3:1.

14. The composite oxide according to claim 1 , wherein x=1.0-2.0.

15. The composite oxide according to claim 2 , wherein the weight ratio of the composite oxide to the carrier is 0.1-0.3:1, the carrier is one or more selected from the group consisting of SiO 2 , Al 2 O 3 , MgO—SiO 2 , MgO—Al 2 O 3 , Al 2 O 3 —SiO 2 , CaO—SiO 2 , and CaO—MgO—SiO 2 .

16. The composite oxide according to claim 3 , wherein the powder X ray diffraction pattern has peaks at diffraction angles 2 theta of 18.5±0.5°, 28.5±0.5°, 31.5±0.5°, and 34.5±0.5°.

17. The process according to claim 9 , wherein the suitable methane selective oxidation reaction condition comprises a reaction temperature of 500-600 degrees Celsius, a reaction pressure of 0.5-1.0 MPa (gage), a feeding gas composition (by molar) of CH 4 :O 2 :H 2 O=1:0.25-0.5:2-4, and a methane space velocity of 2000-2800 h −1 .

Assignees

• China Petroleum & Chemical
• Fushun Res Inst Petroleum & Petrochemicals Sinopec

Inventors

• Zhang Shudong
• Jin Yingjie
• Ni Xiangqian
• Li Jie
• Zhang Xiwen
• Zhang Xinwei

Classifications

• B01J2523/00

  Constitutive chemical elements of heterogeneous catalysts · CPC title

• B01J23/887

  containing in addition other metals, oxides or hydroxides provided for in groups B01J23/02 - B01J23/36 · CPC title

• B01J23/002

  Mixed oxides other than spinels, e.g. perovskite · CPC title

• C07C47/06

  Acetaldehyde · CPC title

• B01J2523/822

  Rhodium · CPC title